阅读说明：本技术 一种制丝用钢表面氧化铁皮的机械剥落方法 (Mechanical stripping method for iron scale on surface of steel for wire making ) 是由 孙金波 张志刚 宋维兆 于 2021-02-01 设计创作，主要内容包括：本发明公开了一种制丝用钢表面氧化铁皮的机械剥落方法,包括风冷工艺控制步骤,该步骤的控制参数如下：1号-13号风机挡板开度均为50%,辊道基础速度0.8m/s,辊道起步速度0.7m/s—1.1m/s、最终速度为1.2m/s,1—6号保温罩全开、7—10号保温罩全罩。本发明方法以机械剥除氧化铁皮代替传统酸洗的方法,即节约了人工成本,也减少了对环境的污染。(The invention discloses a mechanical stripping method for iron scale on the surface of steel for wire making, which comprises an air cooling process control step, wherein the control parameters of the step are as follows: the opening degrees of the baffles of the No. 1-No. 13 fans are all 50%, the basic speed of the roller way is 0.8m/s, the starting speed of the roller way is 0.7 m/s-1.1 m/s, the final speed is 1.2m/s, the No. 1-No. 6 heat preservation covers are fully opened, and the No. 7-No. 10 heat preservation covers are fully covered. The method of the invention replaces the traditional pickling method with the mechanical stripping of the iron scale, thereby saving the labor cost and reducing the pollution to the environment.)

一种制丝用钢表面氧化铁皮的机械剥落方法

技术领域

本发明涉及一种制丝用钢表面氧化铁皮的机械剥落方法。

背景技术

制丝用钢在国内多以LS,焊条为主，传统的去除氧化铁皮的方法多为酸洗，对工人身体及现场环境造成极大的危害。

发明内容

本发明的目的在于提供一种制丝用钢表面氧化铁皮的机械剥落方法，以机械剥除氧化铁皮代替传统酸洗的方法，即节约了人工成本，也减少了对环境的污染。

实现上述目的的一种制丝用钢表面氧化铁皮的机械剥落方法，包括风冷工艺控制步骤，该步骤的控制参数如下：1号-13号风机挡板开度均为50%，辊道基础速度0.8m/s，辊道起步速度0.7m/s—1.1m/s、最终速度为1.2m/s,1—6号保温罩全开、7—10号保温罩全罩。

对风冷线辊道速度进行重新计算设定，同时结合制丝用钢的冷却速率，对风机的开启度进行核算，突破了国内自然冷却的工艺惯例，使制丝用钢表面氧化铁皮得到完全剥落，利于现场拉拔使用。

具体实施方式

一种制丝用钢表面氧化铁皮的机械剥落方法，包括风冷工艺控制步骤，该步骤的控制参数如下：1号-13号风机挡板开度均为50%，辊道基础速度0.8m/s，辊道起步速度0.7m/s—1.1m/s、最终速度为1.2m/s,1—6号保温罩全开、7—10号保温罩全罩。

本发明主要采用对制丝用钢轧钢全流程的工艺设计，低温开轧，有孔型和无孔型相结合的方法，及突破国内惯例的风机使用方法，采用风机小风量，辊道提速的方法，使钢材表面形成易于剥落的氧化铁皮。