阅读说明：本技术 应用于smc/bmc复合材料的纳米多功能性复合材料 (Nano multifunctional composite material applied to SMC/BMC composite material ) 是由 徐兴通 于 2020-12-18 设计创作，主要内容包括：本发明公开了应用于SMC/BMC复合材料的纳米多功能性复合材料,涉及复合材料技术领域；它的配方如下：纳米碳酸钙10-30％、碳酸钙镁10-30％、硬脂酸锌20-40％、硬脂酸5-10％、纳米二氧化硅5-10％、氧化镁5-10％、过氧化苯甲酰叔丁酯5-10％、过氧化苯甲酰5-10％、偶联剂3-6％、抗氧剂3-6％、紫外线吸收剂3-5％、分散剂1-3％、对苯二酚1-3％；本发明环保安全,完美替代传统工艺配方中甲类危化品的进入,在环境保护以及消除厂区隐患方面起到了非常大的作用,简易多功,提升产品质量的同时,也简化了工艺流程。(The invention discloses a nano multifunctional composite material applied to SMC/BMC composite material, relating to the technical field of composite materials; the formula of the medicine is as follows: 10-30% of nano calcium carbonate, 10-30% of calcium magnesium carbonate, 20-40% of zinc stearate, 5-10% of stearic acid, 5-10% of nano silicon dioxide, 5-10% of magnesium oxide, 5-10% of benzoyl peroxide tert-butyl ester, 5-10% of benzoyl peroxide, 3-6% of coupling agent, 3-6% of antioxidant, 3-5% of ultraviolet absorbent, 1-3% of dispersing agent and 1-3% of hydroquinone; the invention is environment-friendly and safe, perfectly replaces the entrance of the first-class hazardous chemical in the traditional process formula, plays a very large role in environmental protection and eliminating hidden troubles of factories, is simple and multifunctional, improves the product quality and simplifies the process flow.)

1. The nano multifunctional composite material applied to the SMC/BMC composite material is characterized in that: the formula of the medicine is as follows: 10-30% of nano calcium carbonate, 10-30% of calcium magnesium carbonate, 20-40% of zinc stearate, 5-10% of stearic acid, 5-10% of nano silicon dioxide, 5-10% of magnesium oxide, 5-10% of benzoyl peroxide tert-butyl ester, 5-10% of benzoyl peroxide, 3-6% of coupling agent, 3-6% of antioxidant, 3-5% of ultraviolet absorbent, 1-3% of dispersing agent and 1-3% of hydroquinone.

2. The production process of the multifunctional nano composite material applied to the SMC/BMC composite material is characterized by comprising the following steps of: the production process comprises the following steps: 10-30% of nano calcium carbonate, 10-30% of calcium magnesium carbonate, 20-40% of zinc stearate, 5-10% of stearic acid, 5-10% of nano silicon dioxide, 5-10% of magnesium oxide, 5-10% of benzoyl peroxide tert-butyl ester, 5-10% of benzoyl peroxide, 3-6% of coupling agent, 3-6% of antioxidant, 3-5% of ultraviolet absorbent, 1-3% of dispersing agent and 1-3% of hydroquinone are physically and dry-mixed at normal temperature and normal pressure, and are screened and packaged after the dry mixing is finished.

3. A process for the production of a nano-multifunctional composite for the application to SMC/BMC composites as claimed in claim 1 wherein: the mesh number of the screened screening is 20-100 meshes.

4. A process for the production of a nano-multifunctional composite for the application to SMC/BMC composites as claimed in claim 1 wherein: the packaging is 25 kg/bag.

Technical Field

The invention belongs to the technical field of composite materials, and particularly relates to a nano multifunctional composite material applied to SMC/BMC composite materials.

Background

The composite material is a material with new performance formed by two or more materials with different properties through a physical or chemical method on a macroscopic (microscopic) scale. The materials mutually make up for the deficiencies in performance to generate a synergistic effect, so that the comprehensive performance of the composite material is superior to that of the original composition material to meet various different requirements.

The existing composite material has the following disadvantages:

firstly, a plurality of basic raw materials and a class A hazardous chemical substance are added in the traditional SMC/BMC composite material mould pressing process formula. Therefore, the problems of dust splashing, non-standard waste discharge, nonstandard stacking of dangerous chemicals of class A and the like often occur on the site, a series of problems in the aspects of environmental protection, site safety and the like can be caused, and accidents are easy to occur.

Secondly, because of the particularities of the SMC/BMC composite moulding industry, each moulded article has its particular role and purpose. In order to achieve acceptable quality standards, different auxiliary materials must be added during the molding process to solve this problem. The production procedures of the product can be increased while the types of the auxiliary materials are increased, and the production efficiency of the product is greatly influenced.

Disclosure of Invention

Aiming at solving the problem of the defects of the existing composite material; the invention aims to provide a nano multifunctional composite material applied to SMC/BMC composite material.

The invention relates to an SMC/BMC nano multifunctional preparation applied to an SMC/BMC composite material, which comprises the following formula: 10-30% of nano calcium carbonate, 10-30% of calcium magnesium carbonate, 20-40% of zinc stearate, 5-10% of stearic acid, 5-10% of nano silicon dioxide, 5-10% of magnesium oxide, 5-10% of benzoyl peroxide tert-butyl ester, 5-10% of benzoyl peroxide, 3-6% of coupling agent, 3-6% of antioxidant, 3-5% of ultraviolet absorbent, 1-3% of dispersing agent and 1-3% of hydroquinone.

The production process of the multifunctional nano composite material applied to the SMC/BMC composite material comprises the following steps: 10-30% of nano calcium carbonate, 10-30% of calcium magnesium carbonate, 20-40% of zinc stearate, 5-10% of stearic acid, 5-10% of nano silicon dioxide, 5-10% of magnesium oxide, 5-10% of benzoyl peroxide tert-butyl ester, 5-10% of benzoyl peroxide, 3-6% of coupling agent, 3-6% of antioxidant, 3-5% of ultraviolet absorbent, 1-3% of dispersing agent and 1-3% of hydroquinone are physically and dry-mixed at normal temperature and normal pressure, and after the dry mixing is finished, the screening is carried out, and the packaging is carried out after the screening is finished.

Preferably, the screening mesh number of the screening is 20-100 meshes.

Preferably, the pack is 25 kg/bag.

Compared with the prior art, the invention has the beneficial effects that:

firstly, environmental protection and safety: the method can perfectly replace the multiple entry of the A-type hazardous chemical substances and excessive basic raw materials in the traditional process formula; plays a great role in environmental protection and eliminating hidden troubles of plant areas.

Secondly, simple and multifunctional: has the characteristics of reinforcement and toughening, flame retardance and brightness enhancement, excellent pollution resistance and weather resistance and the like; the product can be excellent in multi-dimensional performance by adding the additive once; the product quality is improved, and the process flow is simplified; the production efficiency of the product is greatly improved.

Thirdly, the product is high in quality and low in price: the SMC/BMC nano multifunctional preparation has strict cost control, eliminates various defects in the production of the traditional process, has the product price far lower than the value generated in the use process, is basically equal to the sum of the prices of the replaced raw materials of the traditional process, and completes the process upgrade on the basis of not increasing the enterprise cost for a user.

Drawings

For ease of illustration, the invention is described in detail by the following detailed description and the accompanying drawings.

FIG. 1 is a flow chart of the present invention.

Detailed Description

In order that the objects, aspects and advantages of the invention will become more apparent, the invention will be described by way of example only, and in connection with the accompanying drawings. It is to be understood that such description is merely illustrative and not intended to limit the scope of the present invention. The structure, proportion, size and the like shown in the drawings are only used for matching with the content disclosed in the specification, so that the person skilled in the art can understand and read the description, and the description is not used for limiting the limit condition of the implementation of the invention, so the method has no technical essence, and any structural modification, proportion relation change or size adjustment still falls within the range covered by the technical content disclosed by the invention without affecting the effect and the achievable purpose of the invention. Moreover, in the following description, descriptions of well-known structures and techniques are omitted so as to not unnecessarily obscure the concepts of the present invention.

It should be noted that, in order to avoid obscuring the present invention with unnecessary details, only the structures and/or processing steps closely related to the scheme according to the present invention are shown in the drawings, and other details not so relevant to the present invention are omitted.

The first embodiment is as follows: the specific implementation mode adopts the following technical scheme: the formula of the medicine is as follows: 20% of nano calcium carbonate, 20% of calcium magnesium carbonate, 24% of zinc stearate, 5% of stearic acid, 5% of nano silicon dioxide, 5% of magnesium oxide, 5% of benzoyl peroxide tert-butyl ester, 5% of benzoyl peroxide, 3% of coupling agent, 3% of antioxidant, 3% of ultraviolet absorbent, 1% of dispersing agent and 1% of hydroquinone.

As shown in FIG. 1, the production process of the multifunctional nano composite material applied to SMC/BMC composite material comprises the following steps: 20% of nano calcium carbonate, 20% of calcium magnesium carbonate, 24% of zinc stearate, 5% of stearic acid, 5% of nano silicon dioxide, 5% of magnesium oxide, 5% of benzoyl peroxide tert-butyl ester, 5% of benzoyl peroxide, 3% of coupling agent, 3% of antioxidant, 3% of ultraviolet absorbent, 1% of dispersing agent and 1% of hydroquinone are physically and dry-mixed at normal temperature and normal pressure, and are screened and packaged after being dry-mixed.

Furthermore, the mesh number of the screened screen is 20-100 meshes.

Further, the package is 25 kg/bag.

Example two: the nano multifunctional composite material applied to the SMC/BMC composite material has the following formula: 10% of nano calcium carbonate, 10% of calcium magnesium carbonate, 20% of zinc stearate, 8% of stearic acid, 8% of nano silicon dioxide, 8% of magnesium oxide, 7% of benzoyl peroxide tert-butyl ester, 8% of benzoyl peroxide, 5% of coupling agent, 5% of antioxidant, 5% of ultraviolet absorbent, 3% of dispersing agent and 3% of hydroquinone.

The production process of the multifunctional nano composite material applied to the SMC/BMC composite material comprises the following steps: 10% of nano calcium carbonate, 10% of calcium magnesium carbonate, 20% of zinc stearate, 8% of stearic acid, 8% of nano silicon dioxide, 8% of magnesium oxide, 7% of benzoyl peroxide tert-butyl ester, 8% of benzoyl peroxide, 5% of coupling agent, 5% of antioxidant, 5% of ultraviolet absorbent, 3% of dispersant and 3% of hydroquinone are physically and dry-mixed at normal temperature and normal pressure, and are screened and packaged after the dry-mixing is finished.

It will be evident to those skilled in the art that the invention is not limited to the details of the foregoing illustrative embodiments, and that the present invention may be embodied in other specific forms without departing from the spirit or essential attributes thereof. The present embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description, and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein.

Furthermore, it should be understood that although the present description refers to embodiments, not every embodiment may contain only a single embodiment, and such description is for clarity only, and those skilled in the art should integrate the description, and the embodiments may be combined as appropriate to form other embodiments understood by those skilled in the art.