阅读说明：本技术 一种轻质高强碳化硅泡沫陶瓷及其制备方法 (Light high-strength silicon carbide foam ceramic and preparation method thereof ) 是由 史忠旗 袁媛 魏智磊 周小楠 王波 夏鸿雁 于 2020-07-14 设计创作，主要内容包括：本发明公开了一种轻质高强碳化硅泡沫陶瓷及其制备方法,属于泡沫陶瓷制备技术领域。本发明以聚氨酯泡沫为模板,将高残碳树脂与无水乙醇混合均匀,制成具有不同粘度的浆料。通过挂浆、干燥及热解碳化的步骤得到孔筋结构和强度可控的泡沫碳前驱体,然后通过原位气固碳热还原反应烧结制得轻质高强碳化硅泡沫陶瓷。与传统的模板法比较,本发明通过控制挂浆量调控碳化后泡沫碳骨架的残碳量,从而实现碳化硅泡沫陶瓷制品孔筋结构、孔隙率和强度的控制。该法制备的碳化硅泡沫陶瓷为三维开孔互联网状骨架结构,具有孔筋芯部中空、孔筋壁光滑致密等结构特点,制品具有轻质、高强的特性。(The invention discloses a light high-strength silicon carbide foam ceramic and a preparation method thereof, belonging to the technical field of foam ceramic preparation. The invention takes polyurethane foam as a template, and high carbon residue resin and absolute ethyl alcohol are uniformly mixed to prepare slurry with different viscosities. The foam carbon precursor with controllable pore rib structure and strength is obtained through the steps of slurry coating, drying and pyrolysis carbonization, and then the light high-strength silicon carbide foam ceramic is prepared through in-situ gas-solid carbon thermal reduction reaction sintering. Compared with the traditional template method, the method controls the residual carbon content of the carbonized foam carbon skeleton by controlling the slurry hanging amount, thereby realizing the control of the pore rib structure, the porosity and the strength of the silicon carbide foam ceramic product. The silicon carbide foamed ceramic prepared by the method is of a three-dimensional open-pore interconnected network framework structure, has the structural characteristics of hollow pore rib core parts, smooth and compact pore rib walls and the like, and has the characteristics of light weight and high strength.)

1. The preparation method of the light high-strength silicon carbide foam ceramic is characterized by comprising the following steps of:

1) preparing slurry: taking high carbon residue resin as a carbon source and absolute ethyl alcohol as a solvent, and mixing the high carbon residue resin and the absolute ethyl alcohol in a ratio of 1: (0.3-1) and fully and uniformly mixing to prepare slurry with the viscosity of 60-350 mPa & s;

2) slurry coating: polyurethane foam is used as a template, the polyurethane foam is soaked in the prepared slurry to be fully suspended, and then the excessive slurry is removed and dried to prepare a polyurethane foam precursor;

3) pyrolysis and carbonization: pyrolyzing and carbonizing a polyurethane foam precursor at 1000 ℃ in an inert gas atmosphere to obtain a foam carbon skeleton with a triangular rib with a compact and smooth surface and a hollow core part;

4) and (3) sintering: laying a layer of SiO powder at the bottom of a crucible in a sintering furnace, placing the foamy carbon skeleton prepared in the step 3) in the middle of the crucible, and carrying out heat preservation treatment at 1650-1850 ℃ for 2-6 h in an inert gas atmosphere to enable SiO steam and the foamy carbon skeleton to carry out in-situ gas-solid carbon thermal reduction reaction to form the light high-strength silicon carbide foamy ceramic.

2. The method for preparing the light-weight high-strength silicon carbide foamed ceramic according to claim 1, wherein the high-carbon-residue resin is one or more of epoxy resin, phenolic resin, ammonia phenolic resin, barium phenolic resin, furfural resin, phenol furfural resin and methyl phenolic resin.

3. The method for preparing the lightweight, high-strength silicon carbide foam ceramic as claimed in claim 1, wherein the polyurethane foam used has a specification of 20-65 PPI.

4. The method for preparing the light-weight high-strength silicon carbide foam ceramic as claimed in claim 1, wherein in the step 2), the polyurethane foam is sufficiently kneaded to be sufficiently slurried in the dipping process, then the excess slurry is removed by a rolling method, and the mixture is naturally dried in the shade at room temperature.

5. The preparation method of the light-weight high-strength silicon carbide foamed ceramic according to claim 1, wherein in the step 3), the pyrolysis carbonization is completed by heating to 1000 ℃ at a speed of 1 ℃/min from room temperature and keeping the temperature for 2-4 h under argon atmosphere.

6. The preparation method of the light-weight high-strength silicon carbide foamed ceramic according to claim 1, wherein in the step 4), the mass ratio of the SiO powder to the foamed carbon skeleton is (6-12): 1.

7. the preparation method of the light-weight high-strength silicon carbide foamed ceramic according to claim 1, wherein in the step 4), argon is used as the inert gas, and the pressure of the argon is 0.2-0.6 MPa.

8. The method for preparing a lightweight, high-strength silicon carbide foam ceramic as claimed in claim 1, wherein in step 4), the sintering is carried out at a temperature rise rate of 5 ℃/min from room temperature to 1650 ℃ to 1850 ℃.

9. The light high-strength silicon carbide foam ceramic prepared by the preparation method of the light high-strength silicon carbide foam ceramic according to any one of claims 1 to 8 is characterized in that the light high-strength silicon carbide foam ceramic is of a three-dimensional open-cell interconnected net-shaped framework structure and is provided with triangular hollow pore ribs and smooth and compact pore rib walls; the light high-strength silicon carbide foamed ceramic has uniform pore size distribution and no pore blockage, the pore diameter is 200-350 mu m, the pore rib diameter is 50-75 mu m, and the wall thickness of the pore rib is 3-8 mu m.

10. The lightweight high-strength silicon carbide foam ceramic as claimed in claim 9, wherein the lightweight high-strength silicon carbide foam ceramic has a compressive strength of 60 to 80kPa and a density of 0.05 to 0.08g/cm³The porosity is 97.5-98.5%.

Technical Field

The invention belongs to the technical field of foamed ceramic preparation, and particularly relates to light high-strength silicon carbide foamed ceramic and a preparation method thereof.

Background

The silicon carbide (SiC) foamed ceramic has the excellent performances of high porosity (70-95%), low density, high specific surface area, high permeability, high temperature resistance, corrosion resistance, oxidation resistance and the like, can be used as a catalyst carrier, a molten metal filter, a composite material reinforcing phase, an artificial joint and other devices/components, and is widely applied to the fields of filtration catalysis, heat preservation and insulation, biological medicine, electronic devices, aerospace, energy chemical industry and the like.

The traditional organic template dipping method for preparing SiC foamed ceramic comprises the steps of mixing, slurry coating, drying, pyrolysis and carbonization and sintering, and the specific slurry composition mainly comprises two categories. The first type is that the SiC foamed ceramics is prepared by mixing water system SiC slurry with a sintering aid and sintering. For example, in the chinese patent "a method for preparing low-temperature liquid phase sintered silicon carbide foamed ceramics" (application No. 201310145115.5, application publication No. CN103253980A, application publication No. 2013.8.21), SiC foamed ceramics is prepared by liquid phase sintering using silicon carbide powder, alumina, and magnesia as main raw materials and alumina, magnesia, and the like as sintering aids. The method introduces the sintering aid into the SiC ceramic, which can reduce the sintering temperature but is not beneficial to the application of the SiC ceramic in the biomedical field, thereby greatly limiting the application field of the SiC foamed ceramic. The second method mainly adopts a reaction sintering method to prepare SiC foamed ceramics and introduces a sintering aid to improve the strength of the product. The method can adopt Polycarbosilane (PCS) as a precursor to carry out pyrolysis reaction to obtain SiC foamed ceramic, or adopt Si powder and high-carbon-residue resin as raw materials to prepare SiC foamed ceramic by high-temperature reaction sintering. However, the raw material cost for preparing the SiC foamed ceramic by using the PCS as the precursor is high, and the product is easy to shrink and crack; when Si powder and high-carbon-residue resin are used as raw materials for reaction sintering, the volume shrinkage generated by the reaction of silicon and carbon can form holes on the pore ribs of the SiC foamed ceramic, so that the strength of the SiC foamed ceramic is extremely low. For example, in chinese patent "a high-strength silicon carbide ceramic foam and a method for preparing the same by primary slurry-coating, carbonization and sintering" (application No. CN201810885523.7, application publication No. CN109133933A, application publication No. 2019.1.4), SiC ceramic foam is prepared by reacting and sintering amorphous carbon obtained by pyrolyzing and carbonizing silicon powder and high-carbon-residue resin, with silicon powder and high-carbon-residue resin as main raw materials. The method mainly improves the strength of the SiC foamed ceramic by using residual silicon left in reaction sintering as a binder and adding a sintering aid, and has the defects of complicated preparation process, high experimental cost and uneven distribution of products. In addition, the introduction of sintering aids also greatly limits the application fields of SiC foamed ceramics.

Disclosure of Invention

In order to overcome the defects of the prior art, the invention aims to provide the light high-strength silicon carbide foamed ceramic and the preparation method thereof, the method does not need to add a sintering aid, has simple operation and low experimental cost, and is easy to realize industrial production and application, and the SiC foamed ceramic prepared by the method is of a three-dimensional open-pore interconnected network framework structure, has the appearance and structural characteristics of hollow pore rib cores and smooth and compact pore rib walls, and has the characteristics of light weight, high strength and the like.

In order to achieve the purpose, the invention adopts the following technical scheme to realize the purpose:

the invention discloses a preparation method of light high-strength silicon carbide foam ceramic, which comprises the following steps:

1) preparing slurry: taking high carbon residue resin as a carbon source and absolute ethyl alcohol as a solvent, and mixing the high carbon residue resin and the absolute ethyl alcohol in a ratio of 1: (0.3-1) and fully and uniformly mixing to prepare slurry with the viscosity of 60-350 mPa & s;

2) slurry coating: polyurethane foam is used as a template, the polyurethane foam is soaked in the prepared slurry to be fully suspended, and then the excessive slurry is removed and dried to prepare a polyurethane foam precursor;

3) pyrolysis and carbonization: pyrolyzing and carbonizing a polyurethane foam precursor at 1000 ℃ in an inert gas atmosphere to obtain a foam carbon skeleton with a triangular rib with a compact and smooth surface and a hollow core part;

4) and (3) sintering: laying a layer of SiO powder at the bottom of a crucible in a sintering furnace, placing the foamy carbon skeleton prepared in the step 3) in the middle of the crucible, and carrying out heat preservation treatment at 1650-1850 ℃ for 2-6 h in an inert gas atmosphere to enable SiO steam and the foamy carbon skeleton to carry out in-situ gas-solid carbon thermal reduction reaction to form the light high-strength silicon carbide foamy ceramic.

Preferably, the high-carbon-residue resin is one or more of epoxy resin, phenolic resin, ammonia phenolic resin, barium phenolic resin, furfural resin, phenol furfural resin and methyl phenolic resin.

Preferably, the polyurethane foam used has a specification of 20-65 PPI.

Preferably, in the step 2), the polyurethane foam is sufficiently kneaded to be sufficiently slurried during the impregnation process, and then excess slurry is removed by a roll-pressing method and naturally dried in the shade at room temperature.

Preferably, in the step 3), the pyrolysis carbonization is completed by heating to 1000 ℃ at 1 ℃/min from room temperature under the argon atmosphere and preserving the heat for 2-4 h.

Preferably, in the step 4), the mass ratio of the SiO powder to the foam carbon skeleton is (6-12): 1.

preferably, in the step 4), argon is used as the inert gas, and the pressure of the argon is 0.2-0.6 MPa.

Preferably, in step 4), the sintering is performed by raising the temperature from room temperature to 1650-1850 ℃ at a rate of 5 ℃/min.

The invention also discloses the light high-strength silicon carbide foamed ceramic prepared by the preparation method of the light high-strength silicon carbide foamed ceramic, wherein the light high-strength silicon carbide foamed ceramic is of a three-dimensional open-pore interconnected network framework structure and is provided with triangular hollow pore ribs and smooth and compact pore rib walls; the light high-strength silicon carbide foamed ceramic has uniform pore size distribution and no pore blockage, the pore diameter is 200-350 mu m, the pore rib diameter is 50-75 mu m, and the wall thickness of the pore rib is 3-8 mu m.

Preferably, the compressive strength of the light high-strength silicon carbide foamed ceramic is 60-80 kPa, and the density is 0.05-0.08 g/cm³The porosity is 97.5-98.5%

Compared with the prior art, the invention has the following beneficial effects:

the invention discloses an in-situ carbothermic reduction preparation method of light high-strength SiC foamed ceramic, which takes polyurethane foam as a template, and uniformly mixes high-carbon residue resin and absolute ethyl alcohol to prepare slurry with different viscosities, and the slurry with different viscosities can control the slurry hanging amount. And soaking the polyurethane foam template in the prepared slurry, fully kneading and soaking to uniformly coat the slurry on the surface of the pore rib of the polyurethane foam template, drying the foam precursor after removing the redundant slurry, and then pyrolyzing and carbonizing the foam precursor in an argon atmosphere to obtain the foam carbon skeleton with a triangular pore rib structure with a smooth and compact surface and a hollow core part. And finally, placing the foam carbon skeleton in a crucible with SiO powder laid at the bottom, and preparing the light high-strength SiC foam ceramic through in-situ gas-solid carbon thermal reduction reaction. Compared with the traditional template method, the SiC foamed ceramic generated by the in-situ gas-solid carbon thermal reaction of the foamed carbon skeleton and SiO steam is of a three-dimensional open-pore interconnected network skeleton structure and has the structural characteristics of hollow pore rib core part, smooth and compact pore rib wall and the like, so the SiC foamed ceramic prepared by the method has the characteristics of light weight and high strength.

Further, the high carbon residue resin and the absolute ethyl alcohol are uniformly mixed in different proportions to regulate the viscosity of the slurry, so that the regulation of the slurry hanging amount is realized, the carbon residue amount of the carbonized foam carbon skeleton is further controlled, and the control of the pore rib structure and the strength of the SiC foam ceramic product is realized. In addition, the sample has uniform pore diameter, no pore blockage, high strength and no additives such as sintering aids, curing agents and the like, and is beneficial to the SiC foamed ceramics to play a great application potential in the field of biological medical treatment. The method is simple to operate, low in experimental cost and capable of realizing industrial large-scale application.

Drawings

FIG. 1 is a schematic view of a crucible structure. The method comprises the following steps: 1-furnace body; 2-crucible cover; 3-a crucible; 4-a foamy carbon skeleton; 5-hollowing out the graphite paper bracket; 6-SiO powder.

FIG. 2 is a photograph of the macro morphology of the SiC ceramic foam prepared in example 1.

FIG. 3 is an XRD of the SiC ceramic foam prepared in example 1.

FIG. 4 is a photograph of the micro-morphology of the SiC ceramic foam prepared in example 1.

Fig. 5 is an SEM photograph of a fracture of the SiC foam ceramic cell ribs prepared in example 1.

Detailed Description

In order to make the technical solutions of the present invention better understood, the technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.

It should be noted that the terms "first," "second," and the like in the description and claims of the present invention and in the drawings described above are used for distinguishing between similar elements and not necessarily for describing a particular sequential or chronological order. It is to be understood that the data so used is interchangeable under appropriate circumstances such that the embodiments of the invention described herein are capable of operation in sequences other than those illustrated or described herein. Furthermore, the terms "comprises," "comprising," and "having," and any variations thereof, are intended to cover a non-exclusive inclusion, such that a process, method, system, article, or apparatus that comprises a list of steps or elements is not necessarily limited to those steps or elements expressly listed, but may include other steps or elements not expressly listed or inherent to such process, method, article, or apparatus.

The invention is described in further detail below with reference to the accompanying drawings: