阅读说明：本技术 一种新型防霉剂 (Novel mildew preventive ) 是由 陈长钦 于 2018-09-12 设计创作，主要内容包括：本发明提供了一种新型防霉剂,按各组份重量比包括：二氧化硅50-60份、苯酚15-20份、乳化硅油15-20份、五氯酚钠50-60份、滑石粉55-65份、无水乙醇4-10份、乙烯基硅氧烷10-20份、氢氧化物5-10份、次录酸钠10-15份、聚氧乙烯烷基磷酸酯5-10份、椰油酸二乙醇酰胺3-5份、增稠剂2-4份、二甲苯溶液90-105份,该防霉剂具有杀菌、吸湿的功效,可以改善物料的仓储环境,提高防霉效果。(The invention provides a novel mildew preventive, which comprises the following components in percentage by weight: 50-60 parts of silicon dioxide, 15-20 parts of phenol, 15-20 parts of emulsified silicone oil, 50-60 parts of sodium pentachlorophenate, 55-65 parts of talcum powder, 4-10 parts of absolute ethyl alcohol, 10-20 parts of vinyl siloxane, 5-10 parts of hydroxide, 10-15 parts of sodium hypochlorite, 5-10 parts of polyoxyethylene alkyl phosphate, 3-5 parts of coconut diethanolamide, 2-4 parts of thickening agent and 90-105 parts of xylene solution.)

1. The novel mildew preventive is characterized by comprising the following components in parts by weight: 50-60 parts of silicon dioxide, 15-20 parts of phenol, 15-20 parts of emulsified silicone oil, 50-60 parts of sodium pentachlorophenate, 55-65 parts of talcum powder, 4-10 parts of absolute ethyl alcohol, 10-20 parts of vinyl siloxane, 5-10 parts of hydroxide, 10-15 parts of sodium hypochlorite, 5-10 parts of polyoxyethylene alkyl phosphate, 3-5 parts of coconut diethanolamide, 2-4 parts of thickening agent and 90-105 parts of xylene solution.

2. The novel fungicide according to claim 1, wherein said hydroxide is sodium hydroxide.

3. The novel fungicide according to claim 1, wherein said modifier is carboxymethyl cellulose.

4. The preparation method of the novel mildew preventive is characterized by comprising the following steps:

the method comprises the following steps: adding silicon dioxide, phenol, emulsified silicone oil, sodium pentachlorophenate, talcum powder, absolute ethyl alcohol, vinyl siloxane and sodium hypochlorite into a reaction kettle, heating to 60-80 ℃, and stirring for 30 minutes;

step two: cooling the reactant to 25 ℃, adding hydroxide, and stirring for 2-3 hours;

step three: adding the polyoxyethylene alkyl phosphate, the coconut diethanolamide, the thickening agent and the xylene solution into the mixture, stirring the mixture for 10 to 15 minutes, heating the mixture to 50 to 60 ℃, adding the vinyl siloxane into the mixture, stirring the mixture for 30 minutes, and cooling the mixture to room temperature to obtain a finished product.

Technical Field

The invention relates to the field of warehouse storage, in particular to a mildew inhibitor with good moisture absorption performance.

Background

The storage technology relates to various materials encountered in human life, and the selection of a storage environment incapable of being selected for different materials or the improvement of the storage environment through various different chemicals is the key point of research in the prior storage technology.

In the field of storage, the storage environment with high humidity is usually involved, and the problem that the existing mildew preventive cannot absorb moisture well and the materials are easy to mildew exists in the storage process of some cotton and linen fabric products.

Disclosure of Invention

The technical problem to be solved by the invention is as follows: the existing mildew preventive has poor moisture absorption performance and poor mildew prevention effect, and the mildew preventive with good moisture absorption performance is provided to solve the problems.

The technical scheme adopted by the invention for solving the technical problems is as follows: a novel mildew preventive comprises the following components in parts by weight: 50-60 parts of silicon dioxide, 15-20 parts of phenol, 15-20 parts of emulsified silicone oil, 50-60 parts of sodium pentachlorophenate, 55-65 parts of talcum powder, 4-10 parts of absolute ethyl alcohol, 10-20 parts of vinyl siloxane, 5-10 parts of hydroxide, 10-15 parts of sodium hypochlorite, 5-10 parts of polyoxyethylene alkyl phosphate, 3-5 parts of coconut diethanolamide, 2-4 parts of thickening agent and 90-105 parts of xylene solution.

Further: the hydroxide is sodium hydroxide.

Further: the regulator is carboxymethyl cellulose.

Further: the method comprises the following steps:

the method comprises the following steps: adding silicon dioxide, phenol, emulsified silicone oil, sodium pentachlorophenate, talcum powder, absolute ethyl alcohol, vinyl siloxane and sodium hypochlorite into a reaction kettle, heating to 60-80 ℃, and stirring for 30 minutes;

step two: cooling the reactant to 25 ℃, adding hydroxide, and stirring for 2-3 hours;

step three: adding the polyoxyethylene alkyl phosphate, the coconut diethanolamide, the thickening agent and the xylene solution into the mixture, stirring the mixture for 10 to 15 minutes, heating the mixture to 50 to 60 ℃, adding the vinyl siloxane into the mixture, stirring the mixture for 30 minutes, and cooling the mixture to room temperature to obtain a finished product.

Compared with the prior art, the mildew preventive has the beneficial effects that the mildew preventive has the effects of sterilization and moisture absorption, can improve the storage environment of materials, and improves the mildew preventive effect.

Detailed Description

The following describes in detail embodiments of the present invention