阅读说明：本技术 一种耐磨、抗菌防臭的牛仔面料的制备工艺 (Preparation process of wear-resistant, antibacterial and deodorant jean fabric ) 是由 王小洁 徐昇 于 2020-12-21 设计创作，主要内容包括：本发明涉及牛仔面料技术领域,尤其涉及一种耐磨、抗菌防臭的牛仔面料的制备工艺,牛仔面料由竹炭纤维、竹纤维、天丝、混合纤维、黏胶纤维组成,竹炭纤维的重量含量占总体面料的55％-65％,混合纤维的重量含量占总体面料的15％-25％,竹炭纤维、竹纤维、天丝和黏胶纤维混纺作经纱,混合纤维和黏胶纤维混纺后作纬纱,本发明制作的牛仔布料,可通过竹炭纤维和竹纤维进行抑菌防臭,同时锦纶纤维、氨纶纤维和涤纶纤维均匀较高的强度,使得牛仔布料更加的耐磨,且能够抑菌防臭,使得用户可以舒服的穿戴牛仔布料的衣物。(The invention relates to the technical field of denim fabric, in particular to a preparation process of wear-resistant, antibacterial and deodorant denim fabric, which comprises bamboo charcoal fibers, bamboo fibers, tencel, mixed fibers and viscose fibers, wherein the weight content of the bamboo charcoal fibers accounts for 55-65% of the total fabric, the weight content of the mixed fibers accounts for 15-25% of the total fabric, the bamboo charcoal fibers, the bamboo fibers, the tencel and the viscose fibers are blended to form warp yarns, and the mixed fibers and the viscose fibers are blended to form weft yarns.)

1. The wear-resistant, antibacterial and deodorant denim fabric is characterized by comprising 55-65 wt% of bamboo charcoal fibers, 15-25 wt% of mixed fibers and weft yarns, wherein the bamboo charcoal fibers, the bamboo fibers, the tencel fibers and the viscose fibers are blended to form warp yarns, and the mixed fibers and the viscose fibers are blended to form weft yarns.

2. The wear-resistant, antibacterial and deodorant denim fabric according to claim 1, wherein the mixed fiber is composed of polyamide fiber, spandex fiber and polyester fiber.

3. The wear-resistant, antibacterial and deodorant denim fabric according to claim 2, characterized in that the weight content of the polyamide fibers, the spandex fibers and the polyester fibers in the mixed fibers is 3: 2: 1.

4. a preparation process of wear-resistant, antibacterial and deodorant jean fabric is characterized by comprising the following steps:

s1, selecting materials, namely selecting 180 parts of bamboo charcoal fiber, 20-40 parts of bamboo fiber, 20-40 parts of tencel, 40-60 parts of mixed fiber and 10-30 parts of viscose fiber as raw materials in parts by weight;

s2, preparing strips: preparing bamboo charcoal fibers and viscose fibers into composite bamboo charcoal fiber strips, preparing bamboo fibers and viscose fibers into composite bamboo fiber strips, preparing tencel and viscose fibers into composite tencel strips, and preparing composite mixed fiber strips from mixed fibers and viscose fibers to form B fiber strips;

s3, drawing: drawing the composite bamboo charcoal fiber strips, the composite bamboo fiber strips and the composite top thread strips to form A fiber strips;

s4, roving: respectively carrying out rough spinning on the fiber strips A and the fiber strips B;

s5, yarn forming and ball making: obtaining yarn A and yarn B;

s6, dyeing: respectively carrying out bundle indigo reduction dyeing on the yarn A and the yarn B through a bundle dyeing machine;

s7, knitting: knitting the yarn A as warp yarn and the yarn B as weft yarn by a jean knitting machine to obtain jean fabric;

s8, subsequent processing: and rolling, shaping, drying and cooling to obtain the denim fabric.

5. The preparation process of the wear-resistant, antibacterial and deodorant denim fabric according to claim 4, wherein in the S2, the humidity of the B fiber strips is 30% -40%.

6. The preparation process of the wear-resistant, antibacterial and deodorant denim fabric according to claim 4, wherein in the S3, the humidity of the A fiber strips is 35% -50%.

7. The preparation process of the wear-resistant, antibacterial and deodorant denim fabric according to claim 4, characterized in that in S8, microwave drying is adopted for drying, and natural cooling at room temperature is adopted for cooling.

Technical Field

The invention relates to the technical field of jean fabric, in particular to a preparation process of wear-resistant, antibacterial and deodorant jean fabric.

Background

The traditional jean fabric has the advantages of firmness, good wear resistance, long service life and the like, so that a plurality of workers in the same line can wear jean clothes for a long time, but the jean clothes are polluted by a large amount of sweat due to high labor intensity, and the jean clothes have odor, so that the jean clothes are uncomfortable to wear.

Therefore, a preparation process of the wear-resistant, antibacterial and deodorant jean fabric is provided for solving the problems.

Disclosure of Invention

The invention aims to solve the defects in the prior art and provides a preparation process of a wear-resistant, antibacterial and deodorant jean fabric.

The wear-resistant, antibacterial and deodorant jean fabric comprises 55-65% of bamboo charcoal fibers, 15-25% of mixed fibers and weft yarns, wherein the bamboo charcoal fibers, the bamboo fibers, the tencel fibers and the viscose fibers are blended to form warp yarns, and the mixed fibers and the viscose fibers are blended to form weft yarns.

Preferably, the mixed fiber consists of polyamide fiber, spandex fiber and polyester fiber.

Preferably, the weight content of the polyamide fiber, the spandex fiber and the polyester fiber in the mixed fiber is 3: 2: 1.

a preparation process of wear-resistant, antibacterial and deodorant jean fabric comprises the following steps:

s1, selecting materials, namely selecting 180 parts of bamboo charcoal fiber, 20-40 parts of bamboo fiber, 20-40 parts of tencel, 40-60 parts of mixed fiber and 10-30 parts of viscose fiber as raw materials in parts by weight;

s2, preparing strips: preparing bamboo charcoal fibers and viscose fibers into composite bamboo charcoal fiber strips, preparing bamboo fibers and viscose fibers into composite bamboo fiber strips, preparing tencel and viscose fibers into composite tencel strips, and preparing composite mixed fiber strips from mixed fibers and viscose fibers to form B fiber strips;

s3, drawing: drawing the composite bamboo charcoal fiber strips, the composite bamboo fiber strips and the composite top thread strips to form A fiber strips;

s4, roving: respectively carrying out rough spinning on the fiber strips A and the fiber strips B;

s5, yarn forming and ball making: obtaining yarn A and yarn B;

s6, dyeing: respectively carrying out bundle indigo reduction dyeing on the yarn A and the yarn B through a bundle dyeing machine;

s7, knitting: knitting the yarn A as warp yarn and the yarn B as weft yarn by a jean knitting machine to obtain jean fabric;

s8, subsequent processing: and rolling, shaping, drying and cooling to obtain the denim fabric.

Preferably, in the S2, the humidity of the B fiber strips is 30-40%.

Preferably, in the S3, the humidity of the A fiber strips is 35-50%.

Preferably, in S8, the drying is performed by microwave drying, and the cooling is performed by natural cooling at room temperature.

The invention has the beneficial effects that:

the denim fabric manufactured by the invention can inhibit bacteria and prevent odor through the bamboo carbon fiber and the bamboo fiber, and meanwhile, the nylon fiber, the spandex fiber and the polyester fiber have uniform and higher strength, so that the denim fabric is more wear-resistant, and can inhibit bacteria and prevent odor, and a user can wear the denim fabric comfortably.

Detailed Description

The present invention will be further illustrated with reference to the following specific examples.

Example one

The wear-resistant, antibacterial and deodorant denim fabric is characterized by comprising bamboo charcoal fibers, bamboo fibers, tencel, mixed fibers and viscose fibers, wherein the weight content of the bamboo charcoal fibers accounts for 55% of the total fabric, the weight content of the mixed fibers accounts for 15% of the total fabric, the bamboo charcoal fibers, the tencel and the viscose fibers are blended to form warp yarns, and the mixed fibers and the viscose fibers are blended to form weft yarns;

the mixed fiber consists of nylon fiber, spandex fiber and polyester fiber, and the weight content of the nylon fiber, the spandex fiber and the polyester fiber in the mixed fiber accounts for 3: 2: 1.

a preparation process of wear-resistant, antibacterial and deodorant jean fabric is characterized by comprising the following steps:

s1, selecting materials, namely selecting 120 parts of bamboo charcoal fiber, 20 parts of bamboo fiber, 20 parts of tencel, 40 parts of mixed fiber and 10 parts of viscose fiber as raw materials in parts by weight;

s2, preparing strips: preparing bamboo charcoal fibers and viscose fibers into composite bamboo charcoal fiber strips, preparing bamboo fibers and viscose fibers into composite bamboo fiber strips, preparing tencel and viscose fibers into composite tencel strips, and preparing composite mixed fiber strips from mixed fibers and viscose fibers to form B fiber strips, wherein the humidity of the B fiber strips is 30%;

s3, drawing: drawing the composite bamboo charcoal fiber strips, the composite bamboo fiber strips and the composite tencel strips to form A fiber strips, wherein the humidity of the A fiber strips is 35%;

s4, roving: respectively carrying out rough spinning on the fiber strips A and the fiber strips B;

s5, yarn forming and ball making: obtaining yarn A and yarn B;

s6, dyeing: respectively carrying out bundle indigo reduction dyeing on the yarn A and the yarn B through a bundle dyeing machine;

s7, knitting: knitting the yarn A as warp yarn and the yarn B as weft yarn by a jean knitting machine to obtain jean fabric;

s8, subsequent processing: rolling, shaping, drying and cooling to obtain the jean fabric, wherein the drying adopts microwave drying, and the cooling adopts room temperature natural cooling.

Example two

The wear-resistant, antibacterial and deodorant denim fabric is characterized by comprising bamboo charcoal fibers, bamboo fibers, tencel, mixed fibers and viscose fibers, wherein the weight content of the bamboo charcoal fibers accounts for 60% of the total fabric, the weight content of the mixed fibers accounts for 20% of the total fabric, the bamboo charcoal fibers, the tencel and the viscose fibers are blended to form warp yarns, and the mixed fibers and the viscose fibers are blended to form weft yarns;

the mixed fiber consists of nylon fiber, spandex fiber and polyester fiber, and the weight content of the nylon fiber, the spandex fiber and the polyester fiber in the mixed fiber accounts for 3: 2: 1.

a preparation process of wear-resistant, antibacterial and deodorant jean fabric is characterized by comprising the following steps:

s1, selecting materials, namely selecting 150 parts of bamboo charcoal fiber, 30 parts of bamboo fiber, 30 parts of tencel, 50 parts of mixed fiber and 20 parts of viscose fiber as raw materials in parts by weight;

s2, preparing strips: preparing bamboo charcoal fibers and viscose fibers into composite bamboo charcoal fiber strips, preparing bamboo fibers and viscose fibers into composite bamboo fiber strips, preparing tencel and viscose fibers into composite tencel strips, and preparing mixed fibers and viscose fibers into composite mixed fiber strips to form B fiber strips, wherein the humidity of the B fiber strips is 35%;

s3, drawing: drawing the composite bamboo charcoal fiber strips, the composite bamboo fiber strips and the composite tencel strips to form A fiber strips, wherein the humidity of the A fiber strips is 40%;

s4, roving: respectively carrying out rough spinning on the fiber strips A and the fiber strips B;

s5, yarn forming and ball making: obtaining yarn A and yarn B;

s6, dyeing: respectively carrying out bundle indigo reduction dyeing on the yarn A and the yarn B through a bundle dyeing machine;

s7, knitting: knitting the yarn A as warp yarn and the yarn B as weft yarn by a jean knitting machine to obtain jean fabric;

s8, subsequent processing: rolling, shaping, drying and cooling to obtain the jean fabric, wherein the drying adopts microwave drying, and the cooling adopts room temperature natural cooling.

EXAMPLE III

The wear-resistant, antibacterial and deodorant denim fabric is characterized by comprising bamboo charcoal fibers, bamboo fibers, tencel, mixed fibers and viscose fibers, wherein the weight content of the bamboo charcoal fibers accounts for 65% of the total fabric, the weight content of the mixed fibers accounts for 25% of the total fabric, the bamboo charcoal fibers, the tencel and the viscose fibers are blended to form warp yarns, and the mixed fibers and the viscose fibers are blended to form weft yarns;

the mixed fiber consists of nylon fiber, spandex fiber and polyester fiber, and the weight content of the nylon fiber, the spandex fiber and the polyester fiber in the mixed fiber accounts for 3: 2: 1.

a preparation process of wear-resistant, antibacterial and deodorant jean fabric is characterized by comprising the following steps:

s1, selecting materials, namely selecting 180 parts of bamboo charcoal fiber, 40 parts of bamboo fiber, 40 parts of tencel, 60 parts of mixed fiber and 30 parts of viscose fiber as raw materials in parts by weight;

s2, preparing strips: preparing bamboo charcoal fibers and viscose fibers into composite bamboo charcoal fiber strips, preparing bamboo fibers and viscose fibers into composite bamboo fiber strips, preparing tencel and viscose fibers into composite tencel strips, and preparing mixed fibers and viscose fibers into composite mixed fiber strips to form B fiber strips, wherein the humidity of the B fiber strips is 40%;

s3, drawing: drawing the composite bamboo charcoal fiber strips, the composite bamboo fiber strips and the composite tencel strips to form A fiber strips, wherein the humidity of the A fiber strips is 50%;

s4, roving: respectively carrying out rough spinning on the fiber strips A and the fiber strips B;

s5, yarn forming and ball making: obtaining yarn A and yarn B;

s6, dyeing: respectively carrying out bundle indigo reduction dyeing on the yarn A and the yarn B through a bundle dyeing machine;

s7, knitting: knitting the yarn A as warp yarn and the yarn B as weft yarn by a jean knitting machine to obtain jean fabric;

s8, subsequent processing: rolling, shaping, drying and cooling to obtain the jean fabric, wherein the drying adopts microwave drying, and the cooling adopts room temperature natural cooling.

The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.