热塑性模塑组合物
阅读说明:本技术 热塑性模塑组合物 (Thermoplastic molding composition ) 是由 J·克勒梅 S·瓦格纳 于 2020-02-19 设计创作,主要内容包括:本发明涉及玻璃纤维用于增加由包含热塑性聚酰胺的模塑组合物制成的模塑体的熔接线强度的用途,所述玻璃纤维根据DIN ISO 527-5的拉伸强度为86.0至92.0GPa,根据DIN ISO 527-5的弹性E模量为2600至3200MPa且根据DIN ISO 7884-1的软化点为900℃至950℃。(The invention relates to the use of glass fibers having a tensile strength of 86.0 to 92.0GPa according to DIN ISO527-5, an E-modulus of elasticity of 2600 to 3200MPa according to DIN ISO527-5 and a softening point of 900 to 950 ℃ according to DIN ISO7884-1 for increasing the weld line strength of molded bodies made of molding compositions comprising thermoplastic polyamides.)