Method for preparing maleic anhydride by oxidizing n-butane

文档序号:931780 发布日期:2021-03-05 浏览:8次 中文

阅读说明:本技术 一种正丁烷氧化制顺酐的方法 (Method for preparing maleic anhydride by oxidizing n-butane ) 是由 师慧敏 张东顺 张作峰 冯晔 安欣 袁滨 刘玉芬 于 2019-08-30 设计创作,主要内容包括:本发明提供了一种正丁烷氧化制顺酐的方法,包括使包含正丁烷的原料气与第一钒磷氧催化剂接触,然后再与第二钒磷氧催化剂接触,以反应生成顺酐,其中第一钒磷氧催化剂中钒的平均价态高于第二钒磷氧催化剂中钒的平均价态。本发明提供的方法能够提高原料处理量,提高原料转化率和顺酐收率。(The invention provides a method for preparing maleic anhydride by oxidizing n-butane, which comprises the steps of contacting a feed gas containing n-butane with a first vanadium-phosphorus-oxygen catalyst, and then contacting with a second vanadium-phosphorus-oxygen catalyst to react to generate the maleic anhydride, wherein the average valence state of vanadium in the first vanadium-phosphorus-oxygen catalyst is higher than that of vanadium in the second vanadium-phosphorus-oxygen catalyst. The method provided by the invention can improve the raw material treatment capacity and the raw material conversion rate and the yield of the maleic anhydride.)

1. A method for preparing maleic anhydride by oxidizing n-butane comprises the steps of contacting a feed gas containing n-butane with a first vanadium phosphorus oxide catalyst and then with a second vanadium phosphorus oxide catalyst to react to generate the maleic anhydride, wherein the average valence state of vanadium in the first vanadium phosphorus oxide catalyst is higher than that in the second vanadium phosphorus oxide catalyst.

2. A process according to claim 1, characterised in that the average valence of the vanadium in the first and/or second vanadium phosphorus oxygen catalyst is 4.0-4.6, preferably 4.0-4.4, more preferably 4.03-4.35.

3. The process according to claim 1 or 2, wherein the average valence of the first vanadium phosphorus oxide catalyst is 4.15 to 4.40 and the average valence of the second vanadium phosphorus oxide catalyst is 4.02 to 4.25.

4. A process according to any one of claims 1 to 3, characterised in that the pore volume of the pores with a pore diameter of 2 to 50nm in the first and/or second vanadium phosphorus oxygen catalyst is 20 to 80%, preferably 30 to 60%, of the total pore volume; the pore volume of the pores with a pore diameter of more than 50nm represents 30 to 70%, preferably 40 to 70%, of the total pore volume.

5. A process according to any one of claims 1 to 4, characterised in that the volume content of pores with a pore diameter of more than 50nm in the first vanadium phosphorus oxygen catalyst is greater than the volume content of pores with a pore diameter of more than 50nm in the second vanadium phosphorus oxygen catalyst.

6. A process according to any one of claims 1 to 5, characterised in that the bulk density of the first and/or second vanadium phosphorus oxygen catalyst is from 0.60 to 0.90g/cm3Preferably 0.65 to 0.80g/cm3

7. The process according to any one of claims 1 to 6, wherein the mass content of vanadium element in the first vanadium phosphorus oxide catalyst and/or the second vanadium phosphorus oxide catalyst is 20 to 30%, preferably 21 to 26%; the mass content of the phosphorus element is 15-25%, preferably 15-19%, and preferably, the molar ratio of the vanadium element to the phosphorus element is 1: (0.8-2); preferably 1: (0.9-1.2).

8. A process according to any one of claims 1 to 7, characterised in that the process for the preparation of the first and/or second vanadium phosphorus oxygen catalyst comprises:

step S1, carrying out contact reaction on a vanadium source, a phosphorus source and a liquid medium, and then carrying out solid-liquid separation to obtain a solid;

step S2, drying and roasting the obtained solid, then molding and reaming the roasted solid, and then performing activation treatment to obtain the vanadium-phosphorus-oxygen catalyst;

the activation treatment is carried out in a mixed gas of water vapor and a supplementary gas at the temperature of 380-440 ℃, wherein the supplementary gas comprises one or more of air, nitrogen and inert gas; preference is given toThe space velocity of the mixed gas in the process of the activation treatment is 400--1Preferably 800--1More preferably 1000--1

9. The method of claim 8, wherein the vanadium source comprises one or more of vanadium pentoxide, ammonium metavanadate, and vanadyl oxalate;

the phosphorus source comprises one or more of 85% phosphoric acid, 95% phosphoric acid, 105% phosphoric acid, phosphorus pentoxide, and phosphorus pentachloride;

the liquid medium is organic alcohol, preferably isobutyl alcohol and/or benzyl alcohol;

the forming and pore-enlarging treatment comprises the steps of mixing the vanadium-phosphorus-oxygen catalyst precursor with a pore-enlarging agent, then carrying out compression forming on the vanadium-phosphorus-oxygen catalyst precursor, and removing the pore-enlarging agent, wherein the pore-enlarging agent is preferably an organic matter containing hydroxyl and/or carboxyl.

10. A process according to any one of claims 1 to 9, characterised in that the volume of the first vanadium phosphorus oxygen catalyst is 20-80% of the sum of the volumes of the first vanadium phosphorus oxygen catalyst and the second vanadium phosphorus oxygen catalyst.

Technical Field

The invention relates to a method for preparing maleic anhydride by oxidizing n-butane.

Background

Maleic anhydride (maleic anhydride) is an important organic chemical raw material and a fine chemical product, is the third largest anhydride which is only second to phthalic anhydride and acetic anhydride in the world at present, is mainly used for producing thermosetting resin and unsaturated polyester resin, and is used in the fields of pesticides, medicines, coatings, printing ink, lubricating oil additives, papermaking chemicals, textile finishing agents, food additives, surfactants and the like. In addition, a series of widely used fine chemical products such as 1, 4-butanediol (GBL), Tetrahydrofuran (THF), maleic acid, fumaric acid, tetrahydrochysene anhydride and the like can be produced by using maleic anhydride as a raw material, the development and utilization prospects are very wide, and the application range of the maleic anhydride is continuously expanded at present.

The maleic anhydride production process mainly comprises a benzene catalytic oxidation method, an n-butane catalytic oxidation method, a C4 olefin catalytic oxidation method and a phthalic anhydride byproduct method according to raw materials. In recent years, a process for producing maleic anhydride from low-cost carbon four-fraction (n-butane) has become an absolute mainstream of maleic anhydride production worldwide. Since 2011, the conversion of the benzene oxidation method to the butane oxidation method is increasingly obvious, and the yield and the operating rate of the domestic device for preparing the maleic anhydride by the n-butane oxidation method exceed those of the benzene oxidation method. These factors greatly stimulate the demand of domestic enterprises for preparing the vanadium phosphorus oxide catalyst for preparing the maleic anhydride by the butane method.

Vanadium Phosphorus Oxide (VPO) catalysts are the most widely used industrial catalysts for the oxidation of n-butane to maleic anhydride. The surface property of the catalyst, the addition of the auxiliary agent, the activation method of the catalyst and the like all have obvious influence on the performance of the catalyst. Although the current production route using n-butane as a raw material has a dominant position in the production of maleic anhydride, the catalyst needs to further improve the activity and selectivity of the catalyst and increase the yield of the maleic anhydride.

Disclosure of Invention

In order to solve the problems in the prior art, the invention provides a method for preparing maleic anhydride by oxidizing n-butane, and the conversion rate of butane and the yield of maleic anhydride in the reaction for preparing the maleic anhydride by oxidizing the n-butane can be improved by adopting the method provided by the invention.

According to a first aspect of the present invention there is provided a process for the oxidation of n-butane to maleic anhydride which comprises contacting a feed gas comprising n-butane with a first vanadium phosphorus oxygen catalyst followed by a second vanadium phosphorus oxygen catalyst to react to form maleic anhydride, wherein the average valence of vanadium in the first vanadium phosphorus oxygen catalyst is higher than the average valence of vanadium in the second vanadium phosphorus oxygen catalyst.

According to a preferred embodiment of the invention, the average valence of the vanadium in the first vanadium phosphorus oxide catalyst and/or the second vanadium phosphorus oxide catalyst is 4.0 to 4.6, and may be, for example, 4.00, 4.02, 4.03, 4.05, 4.10, 4.15, 4.20, 4.25, 4.30, 4.35, 4.40, 4.45, 4.50, 4.55, 4.60 and any value therebetween, preferably 4.0 to 4.4, more preferably 4.03 to 4.35. The valence state of the V metal center has a significant effect on the overall catalyst. In the conversion of butane to maleic anhydride, V alone4+Photo ((VO)2P2O7) Cannot convert butane efficiently into maleic anhydride molecules, and requires a synergistic interaction between the two phases to produce maleic anhydride, and (VO)2P2O7Strongly interacting isolated V5+The active site is responsible for the activation of butane and the O-insertion reaction. Containing a certain number of V5+Is very important for obtaining better maleic anhydride selectivity. V4+Phase sum V5+The different proportions of the phases cause the V in the catalyst to assume different valences.

According to a preferred embodiment of the invention, the average valence of the first vanadium phosphorus oxide catalyst is 4.15 to 4.40, for example may be 4.15, 4.20, 4.25, 4.30, 4.35, 4.40 and any value therebetween, and the average valence of the second vanadium phosphorus oxide catalyst is 4.02 to 4.25, for example may be 4.02, 4.03, 4.05, 4.10, 4.15, 4.20, 4.25 and any value therebetween.

According to a preferred embodiment of the invention, the pore volume of the pores with a pore diameter of 2 to 50nm in the first vanadium phosphorus oxygen catalyst and/or the second vanadium phosphorus oxygen catalyst is 20 to 80% of the total pore volume, for example 20%, 30%, 40%, 50%, 60%, 70%, 80% and any value in between, preferably 30 to 60%; the pore volume of pores with a pore diameter of more than 50nm represents 30 to 70% of the total pore volume, and may for example be 30%, 40%, 50%, 60%, 70% and any value in between, preferably 40 to 70%; wherein the volume content of pores with a pore diameter of more than 50nm in the first vanadium phosphorus oxide catalyst is greater than the volume content of pores with a pore diameter of more than 50nm in the second vanadium phosphorus oxide catalyst.

According to a preferred embodiment of the invention, the first vanadium phosphorus oxide catalyst and/or the second vanadium phosphorus oxide catalyst has a bulk density of 0.60 to 0.90g/cm3For example, it may be 0.60g/cm3、0.65g/cm3、0.70g/cm3、0.75g/cm3、0.80g/cm3、0.85g/cm3、0.90g/cm3And any value therebetween, preferably 0.65 to 0.80g/cm3. The inventors of the present application have also found that the bulk density of the catalyst in a fixed bed reactor directly affects engineering properties such as the distribution of fluid flow in the bed and the pressure drop across the bed, while having a close relationship with the bulk density of the catalyst and the durability of the catalyst (lateral compressive strength of the catalyst and long term structural stability of the catalyst) given the economic considerations for synthesizing the catalyst. The proper bulk density of the catalyst is maintained, which is not only beneficial to the rapid diffusion of reaction fluid on the surface of the catalyst, but also can ensure the compressive strength of the catalyst in the using process.

According to a preferred embodiment of the invention, the vanadium content of the catalyst is between 20 and 30% by mass, and may be, for example, between 20%, 21%, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29%, 30% and any value between them, preferably between 21 and 26%; the phosphorus element may be contained in an amount of 15 to 25% by mass, for example, 15%, 16%, 17%, 18%, 19%, 20%, 21%, 22%, 23%, 24%, 25% by mass or any value therebetween, and preferably 15 to 19% by mass.

The molar ratio of vanadium and phosphorus in the catalyst has important influence on the aspects of improving the activity of the catalyst, generating the selectivity of the maleic anhydride and the like, but P/V with different ratios is not in a linear relation with the activity and the selectivity of the catalyst, and the molar ratio of the vanadium and the phosphorus is preferably 1 (0.8-2), for example, 1:0.8, 1:0.9, 1:1, 1:1.1, 1:1.2, 1:1.3, 1:1.4, 1:1.5, 1:1.6, 1:1.7, 1:1.8, 1:1.9, 1:2 and any value between the two; preferably 1 (0.9-1.2).

According to a preferred embodiment of the present invention, the catalyst further comprises graphite, preferably, graphite accounts for 1-4% of the total mass of the catalyst.

According to another aspect of the present invention there is provided a process for the preparation of the first and/or second vanadium phosphorus oxygen catalyst comprising:

step S1, carrying out contact reaction on a vanadium source, a phosphorus source and a liquid medium, and then carrying out solid-liquid separation to obtain a solid;

step S2, drying and roasting the obtained solid, then molding and reaming the roasted solid, and then performing activation treatment to obtain the vanadium-phosphorus-oxygen catalyst;

the activation is carried out in a mixed gas of water vapor and a supplementary gas at the temperature of 380-440 ℃, wherein the supplementary gas comprises one or more of air, nitrogen and inert gas.

According to a preferred form of the invention, the volume ratio of water vapour to make-up gas is from 1:1 to 3: 1. In the activation process, the moisture content in the activation atmosphere refines the particle structure of the catalyst, further influences the adjustment of the valence state of vanadium in the catalyst, and is more favorable for forming low-valence vanadium within the range.

According to the preferred embodiment of the invention, the space velocity of the mixed gas of the water vapor and the supplementary gas is 400--1Preferably 800--1More preferably 1000--1

According to a preferred embodiment of the present invention, the vanadium source comprises one or more of vanadium pentoxide, ammonium metavanadate and vanadyl oxalate;

the phosphorus source comprises one or more of 85% phosphoric acid, 95% phosphoric acid, 105% phosphoric acid, phosphorus pentoxide, and phosphorus pentachloride;

the liquid medium is organic alcohol, preferably isobutyl alcohol and/or benzyl alcohol;

the forming and pore-enlarging treatment comprises the steps of mixing the vanadium-phosphorus-oxygen catalyst precursor with a pore-enlarging agent, then carrying out compression forming on the vanadium-phosphorus-oxygen catalyst precursor, and removing the pore-enlarging agent, wherein the pore-enlarging agent is preferably an organic matter containing hydroxyl and/or carboxyl.

According to a preferred embodiment of the invention, the activation treatment is carried out in two stages:

the first stage is as follows: heating the catalyst before activation treatment to 270 ℃ and introducing a first active atmosphere, and continuously heating to 440 ℃ at 380 ℃ for first activation;

and a second stage: replacing the first active atmosphere with a second active atmosphere, and carrying out second activation on the catalyst at the temperature of 380-440 ℃;

wherein the first reactive atmosphere is different from the second reactive atmosphere.

According to the preferred embodiment of the invention, the reaction of n-butane oxidation to maleic anhydride is carried out in a reactor, the first vanadium phosphorus oxygen catalyst is filled in the inlet section of the reactor, the second vanadium phosphorus oxygen catalyst is filled in the outlet section of the reactor, the filling volume of the first vanadium phosphorus oxygen catalyst accounts for 20-80% of the total catalyst filling volume, and the filling volume of the second vanadium phosphorus oxygen catalyst accounts for 80-20% of the total catalyst filling volume.

By adopting the method provided by the invention, in a single-tube fixed bed reactor, under the condition that butane load is 1.5-2.0 v%, the conversion rate of butane is 82-90%, and the molar yield of maleic anhydride reaches 59-63%. Under the same operation conditions, the conversion rate of butane can be improved by 6.5 percent at most, and the molar yield of the maleic anhydride can be improved by 7.0 percent at most. The method provided by the invention can improve the raw material treatment capacity and the raw material conversion rate and the yield of the maleic anhydride.

Detailed Description

The present invention will be described in detail with reference to examples, but the present invention is not limited to the examples.

The vanadium valence state of the catalyst is determined by a potassium permanganate-ferrous ammonium sulfate titration method, the pore volume of the catalyst is determined by a specific surface area and mesopore-micropore analyzer, and the bulk density of the catalyst is determined by a tap density meter.

Example 1

212g V is added into a 5L reaction kettle2O52000mL of a mixed solution of isobutanol and 300mL of benzyl alcohol, stirring uniformly, dripping 105 wt% of phosphoric acid 217g under a reflux condition for 3h, heating and stirring until the reflux is maintained for 12h, centrifuging the obtained precipitate, drying in vacuum at 150 ℃ for 24h, mixing the raw powder with 4% of graphite powder and 10% of stearic acid, granulating, and pressing into a molded catalyst. The obtained catalyst precursor structure is subjected to pore-expanding agent removing operation in an activator, the temperature is increased to 185 ℃ at the heating rate of 2 ℃/min, the temperature is kept for 5h, the temperature is continuously increased to 198 ℃ at the heating rate of 2 ℃/min, the temperature is kept for 5h, the temperature is increased to 250 ℃ at the heating rate of 5 ℃/min, the temperature is kept for 2h, the atmosphere is replaced by a mixed atmosphere of 70% of water vapor and 30% of air, and the volume space velocity is 2300h-1Continuously heating to 410 ℃ at the heating rate of 5 ℃/min, keeping the temperature for 1h, replacing the atmosphere with 75% of water vapor and 25% of nitrogen, continuously roasting for 5h, then cooling to room temperature under the protection of 100% of nitrogen atmosphere to obtain the activated vanadium-phosphorus-oxygen catalyst VPO-A-1, wherein the V valence state is 4.02 determined by an oxidation-reduction titration method, the pore volume of pores with the diameter of 2-50nm in the catalyst accounts for 51% of the total pore volume, the pore volume of pores with the diameter of more than 50nm accounts for 47% of the total pore volume, and the bulk density of the formed catalyst is 0.65g/cm3

Example 2

212g V was charged into a 5L round bottom flask2O52250mL of a mixed solution of isobutanol and 250mL of benzyl alcohol is heated and stirred to reflux for 3h, 306g of 85 wt% phosphoric acid is dropwise added, the mixture is heated and stirred to reflux for 20h, the obtained precipitate is centrifuged, washed by absolute ethyl alcohol, dried at 150 ℃ for 24h, calcined at 250 ℃ for 5h, and the calcined raw powder, 4% of graphite powder and 10% of citric acid are mixed, granulated and pressed into a molded catalyst. Heating the obtained catalyst precursor structure in an activator at a heating rate of 2 ℃/min to 185 ℃, keeping the temperature for 5h, continuously heating at a heating rate of 5 ℃/min to 250 ℃, keeping the temperature for 1h, then replacing the atmosphere with a mixed atmosphere of 75% of water vapor and 25% of air, wherein the space velocity is 2000h-1At 5 ℃/min, raising the temperature to 400 ℃, keeping the temperature for 1h, replacing the atmosphere with 75% of water vapor and 25% of nitrogen, continuing to roast for 5h, then reducing the temperature to room temperature under the protection of 100% of nitrogen atmosphere to obtain the activated vanadium-phosphorus-oxygen catalyst VPO-A-2, wherein the V valence state is 4.06 determined by an oxidation-reduction titration method, the pore volume of pores with the diameter of 2-50nm in the catalyst accounts for 59% of the total pore volume, the pore volume of pores with the diameter of more than 50nm accounts for 40% of the total pore volume, and the bulk density of the formed catalyst is 0.68g/cm3

Example 3

212g V was charged into a 5L round bottom flask2O52250mL of a mixed solution of isobutanol and 250mL of benzyl alcohol is heated and stirred to reflux for 3h, 275g of 100 wt% phosphoric acid is dropwise added, the mixture is heated and stirred to reflux for 20h, the obtained precipitate is centrifuged, washed by absolute ethyl alcohol, dried at 150 ℃ for 24h, calcined at 250 ℃ for 5h, and the calcined raw powder, 4% of graphite powder and 10% of oxalic acid are mixed, granulated and pressed into a molded catalyst. Heating the obtained catalyst precursor structure in an activator at a heating rate of 2 ℃/min to 185 ℃, keeping the temperature for 5h, continuously heating at a heating rate of 5 ℃/min to 250 ℃, keeping the temperature for 1h, then replacing the atmosphere with a mixed atmosphere of 75% of water vapor and 25% of air, wherein the space velocity is 1700h-1The operation condition of (1) is that the temperature is raised to 390 ℃ at the heating rate of 5 ℃/min, the atmosphere is changed to 75 percent of water vapor and 25 percent of nitrogen after being kept for 1h, the roasting is continued for 5h, then the temperature is lowered to room temperature under the protection of 100 percent of nitrogen atmosphere, the activated vanadium phosphorus oxygen catalyst VPO-A-3 is obtained, the V valence state is 4.13 determined by an oxidation reduction titration method, the pore volume of pores with the diameter of 2-50nm in the catalyst accounts for 58 percent of the total pore volume, the pore volume of pores with the diameter of more than 50nm accounts for 40 percent of the total pore volume, and the bulk density of the formed catalyst is 0.76g/cm3

Example 4

127.2g V was added to a 3L round bottom flask2O51350mL of a mixed solution of isobutanol and 150mL of benzyl alcohol, heating and stirring to reflux for 3 hours, dropwise adding 137g of 105 wt% phosphoric acid, heating and stirring to reflux for 16 hours, centrifuging the obtained precipitate, washing with absolute ethanol, drying at 150 ℃ for 24 hours, calcining at 250 ℃ for 5 hours, and calciningMixing the calcined raw powder with 4% of graphite powder and 12% of oxalic acid, granulating, and pressing to form the catalyst. Heating the obtained catalyst precursor structure in an activator at a heating rate of 2 ℃/min to 185 ℃, keeping the temperature for 5h, continuously heating at a heating rate of 5 ℃/min to 250 ℃, keeping the temperature for 1h, replacing the atmosphere with a mixed atmosphere of 50% of water vapor and 50% of air, wherein the space velocity is 1800h-1The operation condition of (1) is that the temperature is raised to 410 ℃ at the heating rate of 5 ℃/min, the atmosphere is replaced by 75 percent of water vapor and 25 percent of nitrogen after being kept for 1h, the roasting is continued for 6h, then the temperature is lowered to room temperature under the protection of 100 percent of nitrogen atmosphere, the activated vanadium phosphorus oxygen catalyst VPO-A-4 is obtained, the V valence state is 4.09 determined by an oxidation-reduction titration method, the pore volume of pores with the diameter of 2-50nm in the catalyst accounts for 42 percent of the total pore volume, the pore volume of pores with the diameter of more than 50nm accounts for 57 percent of the total pore volume, and the bulk density of the formed catalyst is 0.70g/cm3

Example 5

127.2g V was added to a 3L round bottom flask2O51350mL of a mixed solution of isobutanol and 150mL of benzyl alcohol, heating and stirring the mixed solution until the reflux is carried out for 3 hours, dropwise adding 105 wt% of phosphoric acid 117g, heating and stirring the mixed solution until the reflux is kept for 16 hours, centrifuging the obtained precipitate, washing the precipitate by absolute ethyl alcohol, drying the precipitate at 150 ℃ for 24 hours, roasting the precipitate at 250 ℃ for 5 hours, mixing the roasted precipitate, 4% of graphite powder and 6% of ascorbic acid, granulating the mixture, and pressing the mixture to form the catalyst. Heating the obtained catalyst precursor structure in an activator at a heating rate of 2 ℃/min to 200 ℃, keeping the temperature for 6h, continuously heating at a heating rate of 5 ℃/min to 250 ℃, keeping the temperature for 2h, then replacing the atmosphere with a mixed atmosphere of 50% of water vapor and 50% of air, wherein the space velocity is 1500h-1The operation condition of (1) is that the temperature is raised to 420 ℃ at the heating rate of 5 ℃/min, the atmosphere is replaced by 50 percent of nitrogen and 50 percent of water vapor after being kept for 1h, the roasting is continued for 6h, then the temperature is reduced to room temperature under the protection of the nitrogen atmosphere, the activated vanadium phosphorus oxygen catalyst VPO-A-5 is obtained, the V valence state is 4.15 determined by an oxidation reduction titration method, the pore volume of pores with the diameter of 2-50nm in the catalyst accounts for 54 percent of the total pore volume, the pore volume of pores with the diameter of more than 50nm accounts for 45 percent of the total pore volume, and the bulk density of the formed catalyst is 0.75g/cm3

Example 6

212g V was charged into a 5L round bottom flask2O52250mL of a mixed solution of isobutanol and 250mL of benzyl alcohol is heated and stirred to reflux for 3h, 281g of 85 wt% phosphoric acid is added dropwise, the mixture is heated and stirred to reflux for 20h, the obtained precipitate is centrifuged, washed with absolute ethyl alcohol, dried at 150 ℃ for 24h, calcined at 250 ℃ for 5h, and the calcined raw powder, 4% of graphite powder and 10% of citric acid are mixed, granulated and pressed into a molded catalyst. Heating the obtained catalyst precursor structure to 198 ℃ at a heating rate of 3 ℃/min in an activator, keeping the temperature for 10h, heating to 250 ℃ at a heating rate of 5 ℃/min, keeping the temperature for 2h, replacing the atmosphere with a mixed atmosphere of 75% of water vapor and 25% of air, wherein the space velocity is 1400h-1The operation condition of (1) is that the temperature is raised to 420 ℃ at the heating rate of 5 ℃/min, the atmosphere is replaced by 50 percent of nitrogen and 50 percent of water vapor after being kept for 1h, the roasting is continued for 6h, then the temperature is reduced to room temperature under the protection of the nitrogen atmosphere, the activated vanadium phosphorus oxygen catalyst VPO-A-6 is obtained, the V valence state is 4.17 determined by an oxidation reduction titration method, the pore volume of pores with the diameter of 2-50nm in the catalyst accounts for 56 percent of the total pore volume, the pore volume of pores with the diameter of more than 50nm accounts for 43 percent of the total pore volume, and the bulk density of the formed catalyst is 0.82g/cm3

Example 7

A catalyst precursor structure was prepared according to example 3, except that the amount of oxalic acid added was changed to 7%. Heating the obtained catalyst precursor structure in an activator at a heating rate of 2 ℃/min to 180 ℃, keeping the temperature for 6h, continuously heating at a heating rate of 5 ℃/min to 250 ℃, keeping the temperature for 2h, then replacing the atmosphere with a mixed atmosphere of 50% of water vapor and 50% of air, wherein the space velocity is 1500h-1The operation condition of (1) is that the temperature is raised to 430 ℃ at the heating rate of 5 ℃/min, the atmosphere is replaced by 75 percent of nitrogen and 25 percent of water vapor after the temperature is maintained for 1h, the roasting is continued for 6h, then the temperature is reduced to room temperature under the protection of the nitrogen atmosphere, the activated vanadium phosphorus oxygen catalyst VPO-B-1 is obtained, the V valence state is 4.07 by the oxidation reduction titration method, and the pore volume of 2-50nm pores in the catalyst accounts for the total pore volume41% of the total pore volume, the pore volume of pores with a pore diameter of greater than 50nm being 57%, the bulk density of the shaped catalyst being 0.72g/cm3

Example 8

A catalyst precursor structure was prepared by following the procedure described in example 3, except that the amount of stearic acid added was changed to 12%. Heating the obtained catalyst precursor structure in an activator to 185 ℃ at the heating rate of 2 ℃/min, keeping the temperature for 5h, continuously heating to 198 ℃ at the heating rate of 2 ℃/min, heating to 250 ℃ at the heating rate of 5 ℃/min, keeping the temperature for 2h, then replacing the atmosphere with a mixed atmosphere of 25% of water vapor and 75% of air, wherein the space velocity is 1000h-1The operation condition of (1) is that the temperature is raised to 420 ℃ at the heating rate of 5 ℃/min, the atmosphere is replaced by 75 percent of nitrogen and 25 percent of water vapor after being kept for 1 hour, the roasting is continued for 6 hours, then the temperature is reduced to room temperature under the protection of the nitrogen atmosphere, the activated vanadium phosphorus oxygen catalyst VPO-B-2 is obtained, the V valence state is 4.32 determined by an oxidation reduction titration method, the pore volume of pores with the diameter of 2-50nm in the catalyst accounts for 36 percent of the total pore volume, the pore volume of pores with the diameter of more than 50nm accounts for 62 percent of the total pore volume, and the bulk density of the formed catalyst is 0.70g/cm3

Example 9

127.2g V was added to a 3L round bottom flask2O51350mL of a mixed solution of isobutanol and 150mL of benzyl alcohol is heated and stirred to reflux for 3 hours, 169.5g of 105 wt% phosphoric acid is dropwise added, the mixture is heated and stirred to reflux for 16 hours, the obtained precipitate is centrifuged, washed by absolute ethyl alcohol, dried at 150 ℃ for 24 hours, calcined at 250 ℃ for 5 hours, and the calcined raw powder, graphite powder and 12% oxalic acid are mixed, granulated and pressed into a molded catalyst. Heating the obtained catalyst precursor structure in an activator at a heating rate of 2 ℃/min to 185 ℃, keeping the temperature for 5h, continuously heating at a heating rate of 2 ℃/min to 198 ℃, heating at a heating rate of 5 ℃/min to 250 ℃, keeping the temperature for 2h, then replacing the atmosphere with a mixed atmosphere of 25% of water vapor and 75% of air, wherein the space velocity is 2000h-1The temperature is raised to 400 ℃ at the temperature raising rate of 5 ℃/min, the atmosphere is replaced by 25 percent of water vapor and 75 percent of nitrogen after the temperature is maintained for 1h, and the roasting is continued6h, then cooling to room temperature under the protection of 100 percent nitrogen atmosphere to obtain an activated vanadium phosphorus oxygen catalyst VPO-B-3, wherein the V valence state is 4.25 determined by an oxidation reduction titration method, the pore volume of pores with the diameter of 2-50nm in the catalyst accounts for 30 percent of the total pore volume, the pore volume of pores with the diameter of more than 50nm accounts for 69 percent of the total pore volume, and the bulk density of the formed catalyst is 0.76g/cm3

Example 10

A catalyst precursor structure was produced in the same manner as in example 3, except that the amount of phosphoric acid added was changed to 321g, based on 100 wt%. Heating and stirring until reflux is maintained for 20h, centrifuging the obtained precipitate, washing with absolute ethanol, drying at 150 ℃ for 24h, roasting at 250 ℃ for 5h, mixing the roasted raw powder with 4% of graphite powder and 10% of oxalic acid, granulating, and pressing to form the catalyst. Heating the obtained catalyst precursor structure in an activator at a heating rate of 2 ℃/min to 185 ℃, keeping the temperature for 5h, continuously heating at a heating rate of 5 ℃/min to 250 ℃, keeping the temperature for 1h, then replacing the atmosphere with a mixed atmosphere of 50% of water vapor and 50% of air, wherein the space velocity is 800h-1The operation condition of (1) is that the temperature is raised to 400 ℃ at the heating rate of 5 ℃/min, the atmosphere is changed into 50 percent of water vapor and 50 percent of nitrogen after being kept for 1h, the roasting is continued for 5h, then the temperature is lowered to room temperature under the protection of 100 percent of nitrogen atmosphere, the activated vanadium phosphorus oxygen catalyst VPO-A-4 is obtained, the V valence state is 4.37 determined by an oxidation reduction titration method, the pore volume of pores with the diameter of 2-50nm in the catalyst accounts for 59 percent of the total pore volume, the pore volume of pores with the diameter of more than 50nm accounts for 40 percent of the total pore volume, and the bulk density of the formed catalyst is 0.78g/cm3

Example 11

127.2g V was added to a 3L round bottom flask2O51350mL of isobutanol and 150mL of benzyl alcohol are heated and stirred to reflux for 3h, 104.3g of 105 wt% phosphoric acid is dropwise added, the mixture is heated and stirred to reflux for 16h, the obtained precipitate is centrifuged, washed by absolute ethyl alcohol, dried at 150 ℃ for 24h, calcined at 250 ℃ for 5h, and the calcined raw powder, graphite powder and 12% stearic acid are mixed, granulated and pressed into a molded catalyst. The obtained catalyst precursor structure is heated in an activator at a heating rate of 2 ℃/minHeating to 185 deg.C, maintaining at the temperature for 5h, continuing heating to 198 deg.C at a rate of 2 deg.C/min, heating to 250 deg.C at a rate of 5 deg.C/min, maintaining at the temperature for 2h, and replacing with 25% water vapor and 75% air at a space velocity of 2000h-1The operation condition of (1) is that the temperature is raised to 430 ℃ at the heating rate of 5 ℃/min, the atmosphere is changed to 25 percent of water vapor and 75 percent of nitrogen after being kept for 1 hour, the roasting is continued for 6 hours, then the temperature is reduced to room temperature under the protection of 100 percent of nitrogen atmosphere, the activated vanadium phosphorus oxygen catalyst VPO-B-5 is obtained, the V valence state is 4.39 determined by an oxidation reduction titration method, the pore volume of pores with the diameter of 2-50nm in the catalyst accounts for 38 percent of the total pore volume, the pore volume of pores with the diameter of more than 50nm accounts for 60 percent of the total pore volume, and the bulk density of the formed catalyst is 0.70g/cm3

Example 12

212g V was charged into a 5L round bottom flask2O52250mL of a mixed solution of isobutanol and 250mL of benzyl alcohol is heated and stirred to reflux for 3h, 230g of 100 wt% phosphoric acid is dropwise added, the mixture is heated and stirred to reflux for 20h, the obtained precipitate is centrifuged, washed by absolute ethyl alcohol, dried at 150 ℃ for 24h, calcined at 250 ℃ for 5h, and the calcined raw powder, 4% of graphite powder and 10% of tartaric acid are mixed, granulated and pressed into a molded catalyst. Heating the obtained catalyst precursor structure in an activator at a heating rate of 2 ℃/min to 185 ℃, keeping the temperature for 5h, continuously heating at a heating rate of 2 ℃/min to 198 ℃, heating at a heating rate of 5 ℃/min to 250 ℃, keeping the temperature for 2h, then replacing the atmosphere with a mixed atmosphere of 50% of water vapor and 50% of air, wherein the space velocity is 1600h-1The operation condition of (1) is that the temperature is raised to 410 ℃ at the heating rate of 5 ℃/min, the atmosphere is replaced by 25 percent of nitrogen and 75 percent of water vapor after being kept for 1 hour, the roasting is continued for 6 hours, then the temperature is reduced to room temperature under the protection of the nitrogen atmosphere, the activated vanadium phosphorus oxygen catalyst VPO-B-6 is obtained, the V valence state is 4.20 determined by an oxidation reduction titration method, the pore volume of pores with the diameter of 2-50nm in the catalyst accounts for 49 percent of the total pore volume, the pore volume of pores with the diameter of more than 50nm accounts for 50 percent of the total pore volume, and the bulk density of the formed catalyst is 0.79g/cm3

The performance of the catalyst is measured under the conditions that: the catalyst is filled in a fixed bed reactor with the specification of phi 25 multiplied by 2 multiplied by 4000mm (the outer diameter is 25mm, the wall thickness is 2mm and the height is 4000mm) of a single tube, the operation pressure is 0.02-0.15MPa, the concentration of n-butane is 1.5-1.8% (volume ratio) of mixed gas (n-butane and air), and the volume space velocity is 1500-2000h-1The catalyst performance was measured as follows. The performance of the catalysts of examples 1-12 is shown in Table 1.

TABLE 1 reaction results of VPO catalyst catalyzed n-butane selective oxidation to maleic anhydride

Different catalysts are combined and filled, and then the test is carried out, reaction mixed gas enters from the upper part of the reactor and is discharged from the lower part of the reactor, and the embodiment is as follows:

filling the catalyst VPO-B-1 at the upper part of the single-tube reactor, wherein the filling height is 60% of the total bed height, filling the catalyst VPO-A-1 at the lower part of the single-tube reactor, wherein the filling height is 40% of the total bed height, and the catalyst is marked as T1;

filling the catalyst VPO-B-2 at the upper part of the single-tube reactor, wherein the filling height is 40% of the total bed height, filling the catalyst VPO-A-2 at the lower part of the single-tube reactor, the filling height is 60% of the total bed height, and the filling height is marked as T2;

filling the catalyst VPO-B-3 at the upper part of the single-tube reactor, wherein the filling height is 50% of the total bed height, filling the catalyst VPO-A-3 at the lower part of the single-tube reactor, wherein the filling height is 50% of the total bed height, and the catalyst is marked as T3;

filling the catalyst VPO-B-4 at the upper part of the single-tube reactor, wherein the filling height is 25% of the total bed height, filling the catalyst VPO-A-4 at the lower part of the single-tube reactor, the filling height is 75% of the total bed height, and the filling height is marked as T4;

filling the catalyst VPO-B-5 at the upper part of the single-tube reactor, wherein the filling height is 20% of the total bed height, filling the catalyst VPO-A-5 at the lower part of the single-tube reactor, wherein the filling height is 80% of the total bed height, and marking as T5;

filling the catalyst VPO-B-6 at the upper part of the single-tube reactor, wherein the filling height is 70% of the total bed height, filling the catalyst VPO-A-6 at the lower part of the single-tube reactor, wherein the filling height is 30% of the total bed height, and the catalyst is marked as T6;

filling the catalyst VPO-A-1 at the upper part of the single-tube reactor, wherein the filling height is 60% of the total bed height, filling the catalyst VPO-B-1 at the lower part of the single-tube reactor, wherein the filling height is 40% of the total bed height, and the catalyst is marked as T7;

filling the catalyst VPO-A-2 at the upper part of the single-tube reactor, wherein the filling height is 40% of the total bed height, filling the catalyst VPO-B-2 at the lower part of the single-tube reactor, the filling height is 60% of the total bed height, and the filling height is marked as T8;

filling the catalyst VPO-A-3 at the upper part of the single-tube reactor, wherein the filling height is 50% of the total bed height, filling the catalyst VPO-B-3 at the lower part of the single-tube reactor, wherein the filling height is 50% of the total bed height, and the catalyst is marked as T9;

filling the catalyst VPO-A-4 at the upper part of the single-tube reactor, wherein the filling height is 25% of the total bed height, filling the catalyst VPO-B-4 at the lower part of the single-tube reactor, the filling height is 75% of the total bed height, and the catalyst is marked as T10;

filling the catalyst VPO-A-5 at the upper part of the single-tube reactor, wherein the filling height is 20% of the total bed height, filling the catalyst VPO-B-5 at the lower part of the single-tube reactor, wherein the filling height is 80% of the total bed height, and marking as T11;

filling the catalyst VPO-A-6 at the upper part of the single-tube reactor, wherein the filling height is 70% of the total bed height, filling the catalyst VPO-B-6 at the lower part of the single-tube reactor, wherein the filling height is 30% of the total bed height, and the catalyst is marked as T12;

the properties of the combined packing catalyst in a single tube fixed bed reactor were measured as shown in table 2:

TABLE 2 reaction results of the selective oxidation of n-butane to maleic anhydride with VPO catalyst

It should be noted that the above-mentioned embodiments are only for explaining the present invention, and do not constitute any limitation to the present invention. The present invention has been described with reference to exemplary embodiments, but the words which have been used herein are words of description and illustration, rather than words of limitation. The invention can be modified, as prescribed, within the scope of the claims and without departing from the scope and spirit of the invention. Although the invention has been described herein with reference to particular means, materials and embodiments, the invention is not intended to be limited to the particulars disclosed herein, but rather extends to all other methods and applications having the same functionality.

11页详细技术资料下载
上一篇:一种医用注射器针头装配设备
下一篇:一种合成11-硫基萘并[2,3-b]苯并呋喃化合物的方法

网友询问留言

已有0条留言

还没有人留言评论。精彩留言会获得点赞!

精彩留言,会给你点赞!

技术分类