阅读说明：本技术 一种亚共晶Al-Si-Mg-Ti-Sn铸造合金及其制备方法 (Hypoeutectic Al-Si-Mg-Ti-Sn casting alloy and preparation method thereof ) 是由 杜晓东 柴蓉 刘润飞 吴玉程 孙建 于 2020-08-20 设计创作，主要内容包括：本发明公开了一种亚共晶Al-Si-Mg-Ti-Sn铸造合金及其制备方法,其中亚共晶Al-Si-Mg-Ti-Sn铸造合金的成分按质量百分比构成如下：Si 6.50～7.50％,Mg 0.45～0.7％,Ti 0.10～0.20％,Sn 0.4～0.6％,Fe≤0.12％,余量为铝。本发明的铝合金通过配料、熔炼铸造、热处理等工艺流程,改善Al-Si合金的微观组织和性能,在可以保证具有较高的强度和硬度的同时提高了合金的塑性,并降低了成本有利于其广泛应用于汽车零部件的制造行业。(The invention discloses a hypoeutectic Al-Si-Mg-Ti-Sn casting alloy and a preparation method thereof, wherein the hypoeutectic Al-Si-Mg-Ti-Sn casting alloy comprises the following components in percentage by mass: 6.50-7.50% of Si, 0.45-0.7% of Mg, 0.10-0.20% of Ti, 0.4-0.6% of Sn, less than or equal to 0.12% of Fe and the balance of aluminum. The aluminum alloy of the invention improves the microstructure and the performance of the Al-Si alloy through the process flows of material preparation, smelting casting, heat treatment and the like, improves the plasticity of the alloy while ensuring higher strength and hardness, reduces the cost and is beneficial to being widely applied to the manufacturing industry of automobile parts.)

1. A hypoeutectic Al-Si-Mg-Ti-Sn casting alloy is characterized by comprising the following components in percentage by mass:

6.50-7.50% of Si, 0.45-0.7% of Mg, 0.10-0.20% of Ti, 0.4-0.6% of Sn, less than or equal to 0.12% of Fe and the balance of aluminum.

2. A method of producing a hypoeutectic Al-Si-Mg-Ti-Sn casting alloy according to claim 1, characterized by comprising the steps of:

step 1: preparation of alloy ingot

1a, preparing materials: weighing Al-Si intermediate alloy, Al-Mg intermediate alloy, Al-Ti intermediate alloy, 500-mesh tin powder with the purity of 99.9 percent and industrial pure aluminum with the purity of 99.9 percent according to the proportion;

1b, coating and drying: mixing sodium silicate nonahydrate, zinc oxide and water to prepare a coating, uniformly coating the coating on a graphite clay crucible, a smelting tool and a mould, and drying the graphite clay crucible in a smelting furnace; in addition, the alloy raw materials weighed in the step 1a are dried and preheated at the temperature of 200-300 ℃ after surface oxide layers are ground;

1c, smelting and casting: sequentially adding Al-Si intermediate alloy and pure aluminum into a graphite clay crucible preheated to 300 ℃, placing the pure aluminum above the Al-Si intermediate alloy, heating to 730 ℃ along with a furnace, preserving heat and standing for 20min after the Al-Si intermediate alloy and the pure aluminum are completely molten; then adding Al-Ti intermediate alloy into the melted alloy melt; finally, quickly putting the Al-Mg intermediate alloy wrapped by the aluminum foil into the molten alloy, and pressing the Al-Mg intermediate alloy into the bottom of the molten alloy by using a slag removing spoon so as to reduce oxidation burning loss; fully stirring, adjusting the furnace temperature to 720 ℃, and keeping the temperature and standing for 20 min;

1d, refining: rapidly removing dross on the surface layer of the alloy melt by using a skimming ladle, and then adding C₂Cl₆Refining, degassing, standing at 720 deg.C for 10-20min, and removing residue;

1e, pouring: placing 500-mesh tin powder preheated to 150 ℃ at the bottom of an aluminum water bag, quickly flushing refined alloy melt into the aluminum water bag, standing again, degassing and preserving heat for 5 min; pouring the alloy melt into a metal mold preheated to 200-300 ℃ to obtain an alloy ingot;

step 2: solid solution treatment, pre-aging treatment and multistage aging treatment

And sequentially carrying out solid solution treatment, pre-aging treatment and multi-stage aging treatment on the obtained alloy ingot.

3. The method of claim 2, wherein:

in the step 1b, the coating comprises the following components in percentage by mass: 5% of sodium silicate nonahydrate, 15% of zinc oxide and the balance of water.

4. The method of claim 2, wherein:

in the step 2, the solution treatment process comprises the following steps: and (3) carrying out solid solution at 540 ℃ for 6h, and then quenching with water at 80 ℃ for 1 min.

5. The production method according to claim 2 or 4, characterized in that:

in the step 2, the pre-aging treatment process comprises the following steps: and heating the alloy ingot subjected to the solution treatment to 100 ℃ and preserving the heat for 3 hours.

6. The method of claim 5, wherein:

in the step 2, the multistage aging treatment process comprises the following steps: keeping the temperature at 130 ℃ for 2h and 155 ℃ for 2h in sequence, discharging and air cooling.

Technical Field

The invention belongs to the technical field of aluminum alloy materials, and particularly relates to a hypoeutectic Al-Si-Mg-Ti-Sn casting alloy and a preparation method thereof.

Background

Al-Si-Mg series aluminum alloy has excellent casting performance, corrosion resistance and higher specific strength, and is widely applied to the automobile and aerospace industries. With the further development of the fields of automobiles, aviation and the like, the flaky eutectic silicon in the casting structure of the Al-Si alloy restricts the further application of the eutectic silicon, so that the modification of the hypoeutectic Al-Si alloy is an important development trend in the aluminum alloy casting industry.

The hypoeutectic Al-Si series aluminum alloy has higher Si content, so that the casting performance and the flowing performance of the hypoeutectic Al-Si series aluminum alloy are improved; however, the heat treatment strengthening effect is not obvious, and a certain amount of Mg element is usually added to precipitate Mg2Si strengthening phase in the aging process, so that the purpose of heat treatment strengthening is achieved. Under normal solidification conditions, the microstructure of the Al-Si-Mg alloy consists of alpha-Al dendrites and randomly distributed acicular rod eutectic Si. The aluminum-silicon eutectic existing on the grain boundary in a needle-shaped rod shape seriously tears the alloy matrix, so that the continuity of the matrix is reduced, and stress concentration is easily generated at the tip and the edge of the aluminum-silicon eutectic, so that the mechanical property of the alloy is reduced; meanwhile, Fe is also a harmful element in the alloy, a needle-shaped or reticular iron-rich phase can be formed in the material, the cracking mechanism of the Al-Si-Mg alloy shows that tensile fracture is caused by the fracture of eutectic silicon and iron-rich intermetallic compound particles, the iron-rich phase is easy to generate stress concentration under the condition that the alloy is subjected to external force, and cracks are easy to generate at the junction of the iron-rich phase and the needle-shaped eutectic Si phase, so that the mechanical property and the elongation of the alloy are greatly influenced. The trace elements Sr, Ce, Er, Sc and Zr can adjust the coarse sheet eutectic silicon into a fibrous structure so as to improve the comprehensive performance of the alloy, but the elements Sr, Ce, Er, Sc and Zr are expensive, so that the application of the elements in practical production is limited. And the above elements do not improve the harmful effects of Fe well. In addition, most of the existing Al-Si-Mg series aluminum alloys are subjected to heat treatment in a solid solution and single-stage aging mode, the one-step solid solution aging process is simple to operate, supersaturated solid solution alloys subjected to solid solution quenching are directly aged at high temperature, the number of cores of strengthening phases is small, precipitated phases are not uniformly distributed, the obtained structure is poor in uniformity, the tensile strength, the yield strength, the conditional yield strength and the fracture toughness are difficult to obtain good matching, the alloys cannot obtain the optimal performance, the aging period is too long, and energy waste is caused.

Disclosure of Invention

The invention aims to improve the structure and performance of cast aluminum alloy on the premise of not using expensive elements such as Sc, Er, Ce, La and the like, overcomes the defects of the prior art, and provides hypoeutectic Al-Si-Mg-Ti-Sn cast alloy and a preparation method thereof.

The hypoeutectic Al-Si-Mg-Ti-Sn casting alloy comprises the following material components in percentage by mass:

6.50 to 7.50 percent of Si, 0.45 to 0.7 percent of Mg, 0.10 to 0.20 percent of Ti, 0.4 to 0.6 percent of Sn, less than or equal to 0.12 percent of Fe (impurity phase), and the balance of aluminum.

The preparation method of the hypoeutectic Al-Si-Mg-Ti-Sn casting alloy comprises the following steps:

step 1: preparation of alloy ingot

1a, preparing materials: weighing Al-Si intermediate alloy, Al-Mg intermediate alloy, Al-Ti intermediate alloy, 500-mesh tin powder with the purity of 99.9 percent and industrial pure aluminum with the purity of 99.9 percent according to the proportion;

1b, coating and drying: preparing a coating according to the mixture ratio of sodium silicate nonahydrate (5%), zinc oxide (15%) and water (the balance), uniformly coating the coating on a graphite clay crucible, a smelting tool and a mould, and drying the graphite clay crucible in a smelting furnace; in addition, the alloy weighed in the step 1a is dried and preheated in a drying oven at the temperature of 200-300 ℃ after a surface oxide layer is ground;

1c, smelting and casting: sequentially adding Al-Si intermediate alloy and pure aluminum into a graphite clay crucible preheated to 300 ℃, placing the pure aluminum above the Al-Si intermediate alloy, heating to 730 ℃ along with a furnace, preserving heat and standing for 20min after the Al-Si intermediate alloy and the pure aluminum are completely molten; then adding Al-Ti intermediate alloy into the melted alloy melt; finally, quickly putting the Al-Mg intermediate alloy wrapped by the aluminum foil into the molten alloy, and pressing the Al-Mg intermediate alloy into the bottom of the molten alloy by using a slag removing spoon so as to reduce oxidation burning loss; fully stirring, adjusting the furnace temperature to 720 ℃, and keeping the temperature and standing for 20 min;

1d, refining: rapidly removing dross on the surface layer of the alloy melt by using a skimming ladleFollowed by addition of C₂Cl₆(accounting for 1-1.5 percent of the total mass) refining, degassing, standing at 720 ℃ and keeping the temperature for 10-20min, and removing slag;

1e, pouring: placing 500-mesh tin powder preheated to 150 ℃ at the bottom of an aluminum water bag, quickly flushing refined alloy melt into the aluminum water bag, standing again, degassing and preserving heat for 5 min; pouring the alloy melt into a metal mold preheated to 200-300 ℃ to obtain an alloy ingot;

step 2: solid solution treatment, pre-aging treatment and multistage aging treatment

And sequentially carrying out solid solution treatment, pre-aging treatment and multi-stage aging treatment on the obtained alloy ingot. The solution treatment process comprises the following steps: carrying out solid solution at 540 ℃ and heat preservation for 6h, and then quenching with water at 80 ℃ for 1 min; the pre-aging treatment process comprises the following steps: heating the quenched alloy ingot to 100 ℃ and preserving the heat for 3 hours; the multistage aging treatment process comprises the following steps: keeping the temperature at 130 ℃ for 2h and 155 ℃ for 2h in sequence, discharging and air cooling.

The design basis of the method of the invention is as follows:

the invention relates to a method for improving the performance of an aluminum alloy, which comprises the steps of designing components and improving a heat treatment process, wherein the component design comprises the steps of adding a small amount of alloy elements to improve the matrix form and form a strengthening phase so as to achieve the purposes of improving the strength and the plasticity and the like, while the traditional one-time solid solution aging cannot enable the alloy to obtain the optimal performance, a G.P region with higher density can be obtained in the alloy through graded aging, and then the core of a precipitation phase improves the uniformity of the structure so as to improve the comprehensive mechanical property of the alloy₅FeSi) phase and Al-Mg-Fe-Si phase mainly in a needle-shaped or net-shaped form, the existence of an iron-rich phase is one of the main reasons for easy breakage of the material, and the addition of Sn element can form Fe with Fe₂Sn, thereby reducing and breaking the iron-rich phase to improve the plasticity of the material; eutectic silicon is nucleated and grown by taking impurity phases (iron-rich phase, ACP phase and oxide film)) in the aluminum alloy as nucleation points, and the Sn element is addedOn the other hand, the solid solubility of Sn element in the aluminum alloy is small, most of the Sn element exists in β -Sn phase, after heat treatment, β -Sn phase is gathered around spheroidized primary Si and eutectic Si, and some Sn-Si-contained microstructure can form a net structure to obtain Sn-Si tissue structure, the plasticity and wear resistance of the material can be improved due to the soft-hard and soft-hard interphase structure, part of Sn element in the alloy can be combined with Mg element in the alloy to form Mg2Sn phase, the formed Mg2Sn phase can improve the plasticity of the material to a certain extent, Ti generates TiAl3 in the aluminum alloy, TiAl3 plays a role in heterogeneous nucleation during solidification, a nucleation point is provided for α -Al primary phase, grains are refined, the performance of the alloy is improved, the mass fraction of Ti is preferably 0.10-0.20%, finally, the aluminum-based alloy is subjected to the aging treatment of aluminum-based on the aluminum-based alloy of the invention, and the aluminum-based on the artificial aging treatment of aluminum-based on the low-iron-containing Fe-Al-phase, and Fe-based on the artificial aging treatment, the heat-containing Fe-containing Al-based alloy, and the aging treatment of the aluminum-based on the artificial aging treatment of aluminum-₂Sn, the supersaturated solid solution alloy forms enough second phase cores in the heat preservation process of pre-aging at 100 ℃, the crushed and fine form of the iron-containing impurity phase is stabilized, and the negative influence of Fe on the alloy is reduced; the first stage of multistage ageing treatment, the ageing temperature is 130 ℃, the heat preservation time is 2h, in the ageing process, vacancies are released along with the precipitation of elements such as Sn, Si and the like to enable a GP zone to continuously grow and become a metastable phase, on the basis of forming enough cores by pre-ageing, the dispersion degree of the precipitated phase is high, and at the moment, particles which are uniformly distributed, finer and tend to be circular are gradually formed in the shape of the eutectic silicon from a large irregular shape. In the second stage, more Mg is separated out when the temperature is kept at 155 ℃ for 2h for aging₂Si，Mg₂Sn, eutectic silicon and other fine round strengthening phases are distributed in a dispersed and uniform manner, so that the strength and the plasticity of the material are improved.

Compared with the prior art, the invention has the beneficial effects that:

1. the invention is on Al-Si0.4-0.6 Sn element is added into the-Mg alloy, the Si phase form distribution is changed, and Fe is formed with Fe₂Sn reduces and crushes the iron-rich phase, so that the alloy fracture mode has the trend of converting from brittle fracture to ductile fracture, the good mechanical property of the material is ensured, the plasticity of the material is improved, and the material can be more widely applied to the manufacturing of automobile parts.

2. According to the invention, the 500-mesh tin powder preheated to 150 ℃ is placed at the bottom of the aluminum water bag, the refined alloy solution is rapidly flushed into the aluminum water bag, and the aluminum water bag is kept stand to degas, so that the high-temperature retention time of Sn is reduced, the direct contact with the ambient air is reduced, the oxidation burning loss of Sn is less, and the beneficial effects of Sn can be fully exerted. Compared with an Al-Sn intermediate alloy block, the 500-mesh Sn powder greatly increases the contact surface with a solution, accelerates the melting and homogenizing speed, and can realize uniform distribution of Sn element in an aluminum water ladle.

3. The invention is subjected to the pre-aging treatment of heat preservation for 3h at 100 ℃, stabilizes the shape of the fine and broken iron-containing impurity phase, reduces the negative influence of Fe element on the elongation of the material, increases the core quantity of precipitated phase, and provides conditions for the subsequent aging process and the dispersion and uniform distribution of the aging phase. After pre-aging and sectional aging, the impurity phase Fe element at the grain boundary is changed into fine and broken Fe₂Sn，Mg₂The fine round strengthening phases of Si, eutectic silicon and the like are distributed and dispersed and uniform, and the alloy strength and the plasticity are improved. The common Al-Si-Mg-Ti cast aluminum alloy has tensile strength below 245MPa and elongation below 8% after being treated by conventional T6. After the multi-stage aging treatment, the tensile strength of the alloy is 256.2MPa at least, and the elongation is 8.6% at least.

4. The invention avoids the addition of expensive elements such as Sc, Er, Ce and the like, and effectively reduces the cost of the alloy.

Detailed Description

The material components of the aluminum alloy in the embodiments 1-6 of the invention are as follows by mass percent as shown in the following table 1:

table 1 the raw materials of the alloys in examples 1 to 6 are constituted by mass percent