阅读说明：本技术 一种在气相色谱柱固定相中掺杂石墨烯的方法 (Method for doping graphene in gas chromatography column stationary phase ) 是由 观文娜 王诗雨 毛鑫涛 刘婷婷 于 2020-06-18 设计创作，主要内容包括：本发明公开了一种在气相色谱柱固定相中掺杂石墨烯的方法,涉及分析化学技术领域。本发明具体包括以下步骤：将氯化钠加入甲醇溶液配置成氯化钠饱和甲醇溶液、将石墨烯在三氯甲烷中超声粉碎2h,制得石墨烯的三氯甲烷悬浊液、将氯化钠饱和甲醇溶液与石墨烯的三氯甲烷悬浊液进行混合,配制成混合悬浊液、对毛细管进行物理饱和吸附处理。本发明具有操作简单、方式通用、附着均匀、柱流失低等特点。本发明的沉积方法适用于多种色谱柱固定相,能够显著提高色谱柱内表面粗糙度,增大了内比表面积,适用于各种色谱柱固定相且能够显著提高柱效,具有良好的应用前景。(The invention discloses a method for doping graphene in a gas chromatographic column stationary phase, and relates to the technical field of analytical chemistry. The invention specifically comprises the following steps: adding sodium chloride into a methanol solution to prepare a sodium chloride saturated methanol solution, carrying out ultrasonic crushing on graphene in chloroform for 2 hours to prepare a chloroform turbid liquid of the graphene, mixing the sodium chloride saturated methanol solution and the chloroform turbid liquid of the graphene to prepare a mixed turbid liquid, and carrying out physical saturated adsorption treatment on a capillary tube. The method has the characteristics of simple operation, universal mode, uniform adhesion, low column loss and the like. The deposition method is suitable for various chromatographic column stationary phases, can obviously improve the roughness of the inner surface of the chromatographic column and increase the inner specific surface area, is suitable for various chromatographic column stationary phases, can obviously improve the column efficiency, and has good application prospect.)

1. A method for doping graphene in a fixed phase of a gas chromatographic column is characterized in that the method adopts an improved method based on a traditional sodium chloride deposition method, the graphene is fixed through recrystallization of sodium chloride, the graphene is physically occupied before the fixed phase is coated in a physical adsorption mode, and the graphene is introduced at a corresponding position of the fixed phase after the fixed phase is coated, and the method specifically comprises the following steps:

the method comprises the following steps: adding sodium chloride into a methanol solution to prepare a sodium chloride saturated methanol solution;

step two: ultrasonically crushing graphene in trichloromethane for 2 hours to prepare trichloromethane turbid liquid of the graphene;

step three: mixing a sodium chloride saturated methanol solution with a chloroform turbid liquid of graphene to prepare a mixed turbid liquid;

step four: carrying out physical saturation adsorption treatment on the capillary;

the graphene is one or more of single-layer graphene, multi-layer graphene, graphene quantum dots, graphene nanosheets, modified graphene and graphene oxide.

2. The method of claim 1, wherein the conventional sodium chloride deposition method is physical adsorption deposition method and the intermediate connecting substance is sodium chloride.

3. The method for doping graphene in a fixed phase of a gas chromatography column as recited in claim 1, wherein a solvent of a sodium chloride saturated methanol solution in the first step is methanol, a solute of the sodium chloride saturated methanol solution is sodium chloride, and the sodium chloride saturated methanol solution is prepared by:

s1: adding solid sodium chloride powder into 20ml of methanol solvent in batches and in batches, and then carrying out ultrasonic treatment on the solution;

s2: continuously adding solid sodium chloride powder to the methanol in batches and in times if no solid sodium chloride is precipitated after the single ultrasonic treatment;

s3: keeping the precipitate until the precipitate is formed after ultrasonic treatment, standing and layering to form a sodium chloride saturated methanol solution;

wherein the amount of solid sodium chloride powder added each time is 5g, and the time of ultrasonic treatment each time is 30 min.

4. The method according to claim 1, wherein the solvent of the chloroform suspension of the graphene in the second step is chloroform, and the solute of the chloroform suspension of the graphene in the second step is graphene or graphene oxide, and the method for preparing the chloroform suspension of the graphene comprises:

adding graphene powder into trichloromethane, and then carrying out ultrasonic crushing treatment on the trichloromethane to form a uniform turbid liquid;

wherein the ultrasonic pulverization time is 180 min.

5. The method as claimed in claim 4, wherein the mass ratio of the chloroform suspension of the graphene is 0.1-3% m/v.

6. The method according to claim 1, wherein the step three is mixing a saturated methanol solution of sodium chloride with a chloroform suspension of graphene, and the specific mixing manner is as follows:

s01: adding 10ml of chloroform suspension of graphene into 2ml of sodium chloride saturated methanol solution, and stirring for 5min at 600 revolutions per minute;

s02: continuously adding 10ml of chloroform turbid liquid of graphene, and stirring at high speed for 2min to obtain mixed turbid liquid.

7. The method of claim 1, wherein a volume ratio of the sodium chloride saturated methanol solution to the chloroform suspension of the graphene is 1:1 to 1:5 when the sodium chloride saturated methanol solution and the chloroform suspension of the graphene are mixed.

8. The method for doping graphene in the fixed phase of the gas chromatography column as claimed in claim 7, wherein the mixing method of the sodium chloride saturated methanol solution and the chloroform suspension of the graphene is that the volume ratio of the sodium chloride saturated methanol solution to the chloroform suspension of the graphene is 1: and 5, after uniformly mixing and stirring, adding 5 volumes of chloroform turbid liquid of graphene, and then continuing stirring.

9. The method of claim 8, wherein the time for stirring the two times of adding the chloroform suspension of graphene is 5min and 2min respectively.

Technical Field

The invention belongs to the technical field of analytical chemistry, and particularly relates to a method for doping graphene in a gas chromatographic column stationary phase.

Background

In capillary gas chromatography analysis, the separation and detection effect is achieved through the difference of acting force between a fixed phase and an analyzed component. The graphene is used for a capillary gas chromatography solid phase, has special selectivity on aromatic substances due to the unique molecular structure and pi-pi stacking effect with a benzene ring-containing compound, and has better selective separation capacity on amines and alcohols which are easy to tailing, so that the graphene becomes a very ideal gas chromatography stationary phase. Fan and the like directly coat graphene on the inner wall of the quartz capillary tube, and compared with a commercial HP-5MS column, the column using graphene as a stationary phase has more advantages in the aspects of separation effect, running time, thermal stability (up to 280 ℃), repeatability, retention time repeatability and the like. Li and the like modify graphene with Polydimethylsiloxane (PDMS) and are used for a capillary chromatography stationary phase, and due to the fact that the effect of the graphene is increased, compared with a PDMS chromatographic column, the separation effect of the PDMS on polar and nonpolar compounds is improved. In order to increase the acting force between graphene and the inner wall of a quartz capillary, Han et al utilize the adhesiveness of Polydopamine (PDA), firstly modify the inner wall of the capillary with the Polydopamine, and then prepare a G-PDA capillary gas chromatographic column by a static method. Compared with single G and PDA chromatographic columns, the G-PDA chromatographic column has better separation effect on normal alkane, alcohol and aldehyde compounds. However, due to the characteristics of strong hydrophobicity and single structure of the surface of graphene, the graphene is difficult to be directly connected to the surface of a material or modified by a chemical bonding mode; in addition, due to strong van der waals force and pi-pi acting force between graphene sheets, graphene is very difficult to disperse in all solvents, and graphene sheets are easy to agglomerate and stack together, so that a uniform stationary phase is difficult to obtain.

In the preparation of a capillary column, in order to obtain a chromatographic column with higher column efficiency, a stationary liquid needs to be uniformly coated on the inner wall of the capillary, so that the selected stationary phase material is required to have good coating property and can be uniformly distributed on the inner wall of the column. Graphene Oxide (GO) is one of important Graphene derivatives, and a large number of polar oxygen-containing functional groups such as hydroxyl, carboxyl, epoxy and the like are distributed among, on the surface and on the edge of a GO lamellar structure. The introduction of oxygen-containing groups weakens Van der Waals force between molecules, and the carboxyl hydrolysis enables GO to have negative charges in water, and the negative charges between molecules repel each other, so that GO can be stably dispersed in water and organic solvents, and a uniform stationary phase film can be conveniently formed on the inner wall of a tubular column in the capillary coating process. In 2012, Qu et al first applied GO to a capillary gas chromatography stationary phase, and bonded GO lamella to the inner wall of the capillary by using 3-aminopropyldiethoxymethylsilane as a cross-linking agent, and can separate a mixture with a boiling point of 78-218 ℃. Feng et al have improved on this basis, adopt one-step mixing method to coat the graphene oxide on the capillary inner wall, make the chromatographic column with higher theoretical plate number and high selectivity, overcome the phenomenon that graphene oxide is easy to agglomerate in the organic solvent of weak polarity simultaneously. Gonz lez-a-lverez et al prepared capillary gas chromatography columns by incorporating graphene oxide onto the silica surface of a capillary column and packing with an ionic liquid solution.

Aiming at the problems that the stationary phase of the existing capillary chromatographic column is relatively weak in polarity, the coating material structure of the stationary phase is single, the specific surface area is insufficient, the acting force is not rich enough and the like, the method for doping graphene in the stationary phase of the gas chromatographic column is provided so as to achieve the purposes of increasing the roughness of the inner wall of the capillary, increasing the internal specific surface area, increasing the mixed acting force of the stationary phase and doping graphene into the stationary phase by a physical occupying method.

Disclosure of Invention

The invention aims to provide a method for doping graphene in a fixed phase of a gas chromatography column, which is characterized in that the graphene is fixed at the joint of the graphene and the inner surface of a column tube through sodium chloride crystallization in the process of heating, evaporating and recrystallizing inner surface sodium chloride, so that the column loss caused by the graphene is reduced, the deposition is uniform and firm, and meanwhile, the capillary is statically coated after the graphene with high specific surface area is introduced into an inner surface coating, so that the aims of increasing the roughness of the inner wall of the capillary, increasing the inner specific surface area, increasing the mixing acting force of a stationary phase and doping the graphene into the fixed phase by a physical space occupying method are fulfilled.

In order to solve the technical problems, the invention is realized by the following technical scheme:

the invention relates to a method for doping graphene in a gas chromatographic column stationary phase, which adopts an improved method based on a traditional sodium chloride deposition method, wherein the graphene is fixed by recrystallization of sodium chloride, and is physically occupied by the graphene before a stationary phase is coated in a physical adsorption mode, so that the graphene is introduced at a corresponding position of the stationary phase after coating, and the method specifically comprises the following steps:

the method comprises the following steps: adding sodium chloride into a methanol solution to prepare a sodium chloride saturated methanol solution;

step two: ultrasonically crushing graphene in trichloromethane for 2 hours to prepare trichloromethane turbid liquid of the graphene;

step three: mixing a sodium chloride saturated methanol solution with a chloroform turbid liquid of graphene to prepare a mixed turbid liquid;

step four: carrying out physical saturation adsorption treatment on the capillary;

the graphene is one or more of single-layer graphene, multi-layer graphene, graphene quantum dots, graphene nanosheets, modified graphene and graphene oxide.

Further, the conventional sodium chloride deposition method is a physical adsorption deposition method and the intermediate connecting substance is sodium chloride.

Further, the solvent of the sodium chloride saturated methanol solution in the first step is methanol, the solute is sodium chloride, and the preparation method of the sodium chloride saturated methanol solution comprises the following steps:

s1: adding solid sodium chloride powder into 20ml of methanol solvent in batches and in batches, and then carrying out ultrasonic treatment on the solution;

s2: continuously adding solid sodium chloride powder to the methanol in batches and in times if no solid sodium chloride is precipitated after the single ultrasonic treatment;

s3: keeping the precipitate until the precipitate is formed after ultrasonic treatment, standing and layering to form a sodium chloride saturated methanol solution;

wherein the amount of solid sodium chloride powder added each time is 5g, and the time of ultrasonic treatment each time is 30 min.

Further, in the second step, a solvent of the chloroform turbid liquid of the graphene is chloroform, a solute of the chloroform turbid liquid of the graphene is graphene or graphene oxide, and the preparation method of the chloroform turbid liquid of the graphene comprises the following steps:

adding graphene powder into trichloromethane, and then carrying out ultrasonic crushing treatment on the trichloromethane to form a uniform turbid liquid;

wherein the ultrasonic pulverization time is 180 min.

Further, the mass ratio of the chloroform suspension of the graphene is 0.1-3% m/v, and preferably 0.1% m/v.

Further, in the third step, a sodium chloride saturated methanol solution is mixed with a chloroform suspension of graphene, and the specific mixing manner is as follows:

s01: adding 10ml of chloroform suspension of graphene into 2ml of sodium chloride saturated methanol solution, and stirring for 5min at 600 revolutions per minute;

s02: continuously adding 10ml of chloroform turbid liquid of graphene, and stirring at high speed for 2min to obtain mixed turbid liquid.

Further, when the sodium chloride saturated methanol solution is mixed with the chloroform turbid liquid of the graphene, the volume ratio of the sodium chloride saturated methanol solution to the chloroform turbid liquid of the graphene is 1: 1-1: 5.

Further, the mixing method of the sodium chloride saturated methanol solution and the chloroform turbid liquid of the graphene is that the volume ratio of the sodium chloride saturated methanol solution to the chloroform turbid liquid of the graphene is 1: and 5, after uniformly mixing and stirring, adding 5 volumes of chloroform turbid liquid of graphene, and then continuing stirring.

Further, the stirring time after adding the chloroform turbid liquid of the graphene twice is 5min and 2min respectively.

The invention has the following beneficial effects:

1. the method is the same as the prior inner surface roughening treatment mode in whole, but can introduce graphene into the stationary phase coating in a simple and feasible mode, thereby improving the separation capability of the stationary phase of the capillary gas chromatographic column, providing stronger pi-pi conjugate acting force, providing higher inner specific surface area and ensuring more uniform coating.

2. The coating method adopted by the invention is a physical method, so that various universal stationary phases can be coated continuously, and meanwhile, the problems of infirm fixation of the graphene stationary phase, serious loss at high temperature and higher baseline are solved in a simple and feasible manner, so that the method has high practical application value.

Of course, it is not necessary for any product in which the invention is practiced to achieve all of the above-described advantages at the same time.

Drawings

In order to more clearly illustrate the technical solutions of the embodiments of the present invention, the drawings used in the description of the embodiments will be briefly introduced below, and it is obvious that the drawings in the following description are only some embodiments of the present invention, and it is obvious for those skilled in the art that other drawings can be obtained according to the drawings without creative efforts.

FIG. 1 is an electron microscope image of graphene hybrid processing on the inner surface of a capillary;

FIG. 2 is a grob diagram of an undoped single-layer graphene oxide ionic liquid capillary gas chromatography column;

fig. 3 is a grob diagram of a doped monolayer graphene oxide ionic liquid capillary gas chromatography column.

Detailed Description

The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.

The invention relates to a method for doping graphene in a gas chromatographic column stationary phase, which is characterized in that the inner surface of a quartz capillary of a gas chromatographic column is roughened and simultaneously mixed with graphene in a physical occupying way by artificially doping graphene in a roughening reagent on the inner surface of the capillary, and the graphene is fixed at the joint of the graphene and the inner surface of a column tube through sodium chloride crystallization through the heating, evaporating and recrystallizing process of the inner surface sodium chloride, so that the column loss caused by the graphene is reduced, the deposition is uniform and firm, and the capillary is statically coated after the graphene with high specific surface area is introduced into an inner surface coating, so that the aims of increasing the roughness of the inner wall of the capillary, increasing the inner specific surface area, increasing the mixing acting force of a stationary phase and doping the graphene into the stationary phase in the physical occupying way are fulfilled.

The invention is illustrated in detail by the following examples in connection with fig. 1-3: