阅读说明：本技术 一种山地自行车车架管用铝合金及其制备方法 (Aluminum alloy for mountain bicycle frame tube and preparation method thereof ) 是由 黄雪枫 朱阿根 朱甘良 于 2021-07-13 设计创作，主要内容包括：本发明涉及山地自行车车架技术领域,公开了一种山地自行车车架管用铝合金及其制备方法,S1：取用5-5.5％的硅、3-3.5％的铜、4-4.5％的钨、1-1.5％的硅、5-5.5％的锌、1-1.5％的钛、0.5-0.7％的锰、0.1-0.2％的镁、2-2.5％的钛、1.8-2％的铁和70-74.6％的铝；S2：将S1内放置于搅拌磨球机内对原料进行冲击和研磨,对原料进行细化和均匀分布,并加入一定量的石蜡；S3：将混合料加入定型模腔内,并通过压力冲头进行压制,随着压力增大,减少粉末颗粒之间的距离,使得空隙度降低,进而使得混合料密实成为压坯。本发明将部分金属采用镀层的方式提高铝合金管的外壁硬度和耐磨性,从而提高山地自行车架管的强度,同时增加表面处理方法,提高山地自行车架管的防锈性和着色性。(The invention relates to the technical field of mountain bike frames, and discloses an aluminum alloy for mountain bike frame tubes and a preparation method thereof, wherein the aluminum alloy comprises the following components in parts by weight: taking 5-5.5% of silicon, 3-3.5% of copper, 4-4.5% of tungsten, 1-1.5% of silicon, 5-5.5% of zinc, 1-1.5% of titanium, 0.5-0.7% of manganese, 0.1-0.2% of magnesium, 2-2.5% of titanium, 1.8-2% of iron and 70-74.6% of aluminum; s2: placing the raw materials in S1 in a stirring ball mill to impact and grind the raw materials, refining and uniformly distributing the raw materials, and adding a certain amount of paraffin; s3: add the stock mould intracavity with the mixture to suppress through the pressure drift, along with pressure increase, reduce the distance between the powder granule, make the porosity reduce, and then make the mixture closely knit to become the pressed compact. The invention adopts a plating mode to improve the hardness and the wear resistance of the outer wall of the aluminum alloy pipe by partial metal, thereby improving the strength of the mountain bicycle frame pipe, and simultaneously increasing the surface treatment method and improving the rust resistance and the coloring property of the mountain bicycle frame pipe.)

1. An aluminum alloy for a mountain bicycle frame tube is characterized in that the formula of the aluminum alloy comprises 5-5.5% of silicon, 3-3.5% of copper, 4-4.5% of tungsten, 1-1.5% of silicon, 5-5.5% of zinc, 0.8-1% of chromium, 1-1.5% of nickel, 1-1.5% of titanium, 0.5-0.7% of manganese, 0.1-0.2% of magnesium, 2-2.5% of titanium, 1.8-2% of iron, 70-74.6% of aluminum and 0.1-0.2% of impurities.

2. The aluminum alloy for mountain bicycle frame tubes as claimed in claim 1, wherein the aluminum alloy has a formulation comprising 5% silicon, 3% copper, 4% tungsten, 1% silicon, 5% zinc, 0.8% chromium, 1% nickel, 1% titanium, 0.5% manganese, 0.1% magnesium, 2% titanium, 1.8% iron, 74.6% aluminum and 0.1-0.2% impurities.

3. The aluminum alloy for mountain bicycle frame tubes as claimed in claim 1, wherein the aluminum alloy has a formulation comprising 5.25% silicon, 3.25% copper, 4.25% tungsten, 1.25% silicon, 5.25% zinc, 0.9% chromium, 1.25% nickel, 1.25% titanium, 0.6% manganese, 0.1% magnesium, 2.25% titanium, 1.9% iron, 72.3% aluminum and 0.1-0.2% impurities.

4. The aluminum alloy for mountain bicycle frame tubes as claimed in claim 1, wherein the aluminum alloy has a formulation comprising 5.5% silicon, 3.5% copper, 4.5% tungsten, 1.5% silicon, 5.5% zinc, 1% chromium, 1.5% nickel, 1.5% titanium, 0.7% manganese, 0.2% magnesium, 2.5% titanium, 2% iron, 70% aluminum and 0.1-0.2% impurities.

5. A preparation method of an aluminum alloy for a mountain bicycle frame tube is characterized in that the aluminum alloy for the mountain bicycle frame tube is used according to any one of claims 1 to 4, and the preparation method of the aluminum alloy for the mountain bicycle frame tube comprises the following steps:

s1: taking 5.5% of silicon, 3.5% of copper, 4.5% of tungsten, 1.5% of silicon, 5.5% of zinc, 1.5% of titanium, 0.7% of manganese, 0.2% of magnesium, 2.5% of titanium, 2% of iron and 70% of aluminum;

s2: placing the raw materials in S1 in a stirring ball mill to impact and grind the raw materials, refining and uniformly distributing the raw materials, and adding a certain amount of paraffin;

s3: adding the mixture into a shaping die cavity, pressing by a pressure punch, and reducing the distance between powder particles along with the increase of pressure to reduce the porosity and further compact the mixture into a pressed compact;

s4: heating the pressed compact under a vacuum condition, wherein impurities can be discharged by vacuum dewaxing in the sintering process, the purity of the sintering atmosphere is improved, and paraffin is discharged from the pressed compact along with the rise of temperature;

s5: placing the heat-treated pressed blank into a guide die for die-casting and cooling, and adding a forming agent to complete the die-casting and annealing of the pressed blank;

s6: straightening the pressed blank;

s7: mechanically polishing the outer wall of the pressed compact, and performing sand blasting treatment on the outer wall of the pressed compact;

s8: the green compact is subjected to anodic oxidation treatment, so that an oxide layer can be formed on the surface of the green compact, and the hardness and the wear resistance of the surface of a product can be improved;

s9: the green compact is descended and degreased, alkaline etching and activation are carried out, 1.5 percent of nickel is electroplated on the green compact to finish nickel plating, and finally, the green compact is dried;

s10: electroplating 1% of chromium on the green compact to complete chromium plating to form a chromium layer;

s11: and the green compact is coated with antirust paint to form an antirust coating, so that the antirust property of the outer wall of the green compact can be improved, and the outer wall of the green compact is painted and colored.

Technical Field

The invention relates to the technical field of mountain bike frames, in particular to an aluminum alloy for a mountain bike frame tube and a preparation method thereof.

Background

The frame is the soul of a mountain bike, the frame materials selected for different purposes are different, like long-distance people and cross-country people, the selected frames are different, the aluminum alloy mountain bike frame has the first visual feeling that most of pipes of the aluminum frame are rough compared with the steel frame, the cross-sectional shapes are richer (the cross-sectional shapes of a plurality of aluminum frames are triangular, quadrilateral and the like), and the controllability, the acceleration and the climbing performance of the aluminum alloy mountain bike frame are good.

The prior patent (publication number: CN202010037588.3) and a high-strength corrosion-resistant aluminum alloy and a preparation method thereof, which effectively remove impurities generated by each material, then carry out slag removal, deoxidation, desulfurization and dephosphorization again when adding a refining aid, thus better operation can be carried out through twice deslagging, deoxidation, desulphurization and dephosphorization, the residue of impurities is avoided, thereby solving the problem that the prior preparation method of the high-strength corrosion-resistant aluminum alloy has incomplete work of deslagging, deoxidation, desulfurization and dephosphorization, but the aluminum alloy has higher cost when being cut and processed, meanwhile, part of metal is directly heated and mixed, so that the strength of the metal cannot be effectively increased, the treatment on the outer wall of the aluminum alloy pipe is lacked, and the hardness, the wear resistance and the rust resistance of the outer wall of the aluminum alloy pipe cannot be ensured.

Therefore, the aluminum alloy for the mountain bicycle frame tube and the preparation method thereof are provided, the hardness and the wear resistance of the outer wall of the aluminum alloy tube are improved by partially plating metal, so that the strength of the mountain bicycle frame tube is improved, and meanwhile, the surface treatment method is added, and the rust resistance and the coloring property of the mountain bicycle frame tube are improved.

Disclosure of Invention

The invention aims to provide an aluminum alloy for a mountain bicycle frame tube and a preparation method thereof, and solves the problems in the background art.

In order to achieve the purpose, the invention provides the following technical scheme: an aluminum alloy for a mountain bike frame tube is prepared from 5-5.5% of silicon, 3-3.5% of copper, 4-4.5% of tungsten, 1-1.5% of silicon, 5-5.5% of zinc, 0.8-1% of chromium, 1-1.5% of nickel, 1-1.5% of titanium, 0.5-0.7% of manganese, 0.1-0.2% of magnesium, 2-2.5% of titanium, 1.8-2% of iron, 70-74.6% of aluminum and 0.1-0.2% of impurities.

In a preferred embodiment of the present invention, 5% silicon, 3% copper, 4% tungsten, 1% silicon, 5% zinc, 0.8% chromium, 1% nickel, 1% titanium, 0.5% manganese, 0.1% magnesium, 2% titanium, 1.8% iron, 74.6% aluminum, and 0.1-0.2% impurities.

In a preferred embodiment of the present invention, 5.25% silicon, 3.25% copper, 4.25% tungsten, 1.25% silicon, 5.25% zinc, 0.9% chromium, 1.25% nickel, 1.25% titanium, 0.6% manganese, 0.1% magnesium, 2.25% titanium, 1.9% iron, 72.3% aluminum, and 0.1-0.2% impurities.

As a preferred embodiment of the present invention, 5.5% silicon, 3.5% copper, 4.5% tungsten, 1.5% silicon, 5.5% zinc, 1% chromium, 1.5% nickel, 1.5% titanium, 0.7% manganese, 0.2% magnesium, 2.5% titanium, 2% iron, 70% aluminum, and 0.1-0.2% impurities.

In a preferred embodiment of the invention, the method for preparing the aluminum alloy for the mountain bicycle frame tube utilizes the aluminum alloy for the mountain bicycle frame tube, and comprises the following steps:

s1: taking 5.5% of silicon, 3.5% of copper, 4.5% of tungsten, 1.5% of silicon, 5.5% of zinc, 1.5% of titanium, 0.7% of manganese, 0.2% of magnesium, 2.5% of titanium, 2% of iron and 70% of aluminum;

s2: placing the raw materials in S1 in a stirring ball mill to impact and grind the raw materials, refining and uniformly distributing the raw materials, and adding a certain amount of paraffin;

s3: adding the mixture into a shaping die cavity, pressing by a pressure punch, and reducing the distance between powder particles along with the increase of pressure so as to reduce the porosity and further compact the mixture into a pressed compact;

s4: heating the pressed compact under a vacuum condition, wherein impurities can be discharged by vacuum dewaxing in the sintering process, the purity of the sintering atmosphere is improved, and paraffin is discharged from the pressed compact along with the rise of temperature;

s5: placing the heat-treated pressed blank into a guide die for die-casting and cooling, and adding a forming agent to finish the die-casting and annealing the pressed blank;

s6: straightening the pressed blank;

s7: mechanically polishing the outer wall of the pressed compact, and performing sand blasting treatment on the outer wall of the pressed compact;

s8: the green compact is subjected to anodic oxidation treatment, so that an oxide layer can be formed on the surface of the green compact, and the hardness and the wear resistance of the surface of a product can be improved;

s9: the green compact is descended and degreased, alkaline etching and activation are carried out, 1.5 percent of nickel is electroplated on the green compact to finish nickel plating, and finally, the green compact is dried;

s10: electroplating 1% of chromium on the green compact to complete chromium plating to form a chromium layer;

s11: and the green compact is coated with antirust paint to form an antirust coating, so that the antirust property of the outer wall of the green compact can be improved, and the outer wall of the green compact is painted and colored.

Compared with the prior art, the invention has the following beneficial effects:

1. the invention can form two groups of metal layers and one group of oxide film on the surface of the aluminum alloy pipe through chromium plating, nickel plating and anodic oxidation treatment, the oxide layer at the bottom layer can improve the hardness of the product surface, the nickel groove layer can improve the surface wear resistance and the service life of corrosion and fatigue resistance, and the chromium layer at the outer wall is convenient for coloring the metal.

2. According to the invention, after the chromium flower is formed, the bottom layer of the coating can be carried out on the outer wall of the mountain bike pipe, so that the antirust coating and the paint surface are increased, the antirust property of the outer wall of the mountain bike pipe can be improved, the customized coloring treatment can be formed, the attractiveness of the product is improved, and the product competitiveness is improved.

Detailed Description

In order to make the technical means, the creation characteristics, the achievement purposes and the effects of the invention easily understood, the invention is further explained by combining the specific embodiments.

In the description of the present invention, it is possible for those skilled in the art to understand the specific meanings of the above-mentioned terms in the present invention in a specific case.

The invention provides a technical scheme that: the formula of the aluminum alloy for the mountain bicycle frame tube comprises 5-5.5% of silicon, 3-3.5% of copper, 4-4.5% of tungsten, 1-1.5% of silicon, 5-5.5% of zinc, 0.8-1% of chromium, 1-1.5% of nickel, 1-1.5% of titanium, 0.5-0.7% of manganese, 0.1-0.2% of magnesium, 2-2.5% of titanium, 1.8-2% of iron, 70-74.6% of aluminum and 0.1-0.2% of impurities.

The invention also discloses a preparation method of the aluminum alloy for the mountain bicycle frame tube, which comprises the following steps of:

detailed description of the preferred embodiment 1

S1: taking 5.5% of silicon, 3.5% of copper, 4.5% of tungsten, 1.5% of silicon, 5.5% of zinc, 1.5% of titanium, 0.7% of manganese, 0.2% of magnesium, 2.5% of titanium, 2% of iron and 70% of aluminum;

s2: placing the raw materials in S1 in a stirring ball mill to impact and grind the raw materials, refining and uniformly distributing the raw materials, and adding a certain amount of paraffin; the effect of mixing the raw materials is achieved.

S3: adding the mixture into a shaping die cavity, pressing by a pressure punch, and reducing the distance between powder particles along with the increase of pressure so as to reduce the porosity and further compact the mixture into a pressed compact; and carrying out die-casting molding on the mixture through a pressure device.

S4: heating the pressed compact under a vacuum condition, wherein impurities can be discharged by vacuum dewaxing in the sintering process, the purity of the sintering atmosphere is improved, and paraffin is discharged from the pressed compact along with the rise of temperature; the compact is degassed when the temperature reaches the threshold value, solid-phase sintering is carried out after purification, and the compact is compact in the compact without gaps during sintering, so that the hardness of the compact is improved.

S5: placing the heat-treated pressed blank into a guide die for die-casting and cooling, and adding a forming agent to finish the die-casting and annealing the pressed blank; after the pressed blank is kept at a high temperature for a certain time, the pressed blank is cooled to room temperature at a certain cooling speed, and the purposes of more uniform and stable structure, internal stress elimination and material shaping improvement are achieved through atomic diffusion.

S6: straightening the pressed blank; the product needs to be straightened by a straightening machine, and the levelness of the product is ensured.

S7: mechanically polishing the outer wall of the pressed compact, and performing sand blasting treatment on the outer wall of the pressed compact; the sand blasting is used for cleaning and coarsening the surface of the metal, so that the fatigue resistance of the product is improved, and the adhesion effect of the external coating is facilitated.

S8: the green compact is subjected to anodic oxidation treatment, so that an oxide layer can be formed on the surface of the green compact, and the hardness and the wear resistance of the surface of a product can be improved; by adopting the electrolysis principle, the product is an anode and is placed in an electrolyte solution to be electrified, so that the product can replace hydrogen in the electrolyte, and an oxidation layer can be formed on the surface of a pressed compact.

S9: the green compact is descended and degreased, alkaline etching and activation are carried out, 1.5 percent of nickel is electroplated on the green compact to finish nickel plating, and finally, the green compact is dried; the nickel layer can improve the corrosion-resistant fatigue life and service life of the product.

S10: electroplating 1% of chromium pair on the green compact to complete chromium plating to form a chromium layer; the chromium layer has good adsorbability and can be used as a bottom coating of coating.

S11: the green compact is coated with the antirust coating to form an antirust coating, so that the antirust property of the outer wall of the green compact can be improved, and the outer wall of the green compact is painted and colored; the antirust coating can improve the antirust property of the outer wall of the mountain bike pipe, the paint surface can be subjected to customized coloring treatment, the attractiveness of the product is improved, and the product competitiveness is improved.

Specific example 2

S1: taking 5.25% of silicon, 3.25% of copper, 4.25% of tungsten, 1.25% of silicon, 5.25% of zinc, 1.25% of titanium, 0.6% of manganese, 0.1% of magnesium, 2.25% of titanium, 1.9% of iron and 72.3% of aluminum;

s2: placing the raw materials in S1 in a stirring ball mill to impact and grind the raw materials, refining and uniformly distributing the raw materials, and adding a certain amount of paraffin; the effect of mixing the raw materials is achieved.

S3: adding the mixture into a shaping die cavity, pressing by a pressure punch, and reducing the distance between powder particles along with the increase of pressure so as to reduce the porosity and further compact the mixture into a pressed compact; and carrying out die-casting molding on the mixture through a pressure device.

S4: heating the pressed compact under a vacuum condition, wherein impurities can be discharged by vacuum dewaxing in the sintering process, the purity of the sintering atmosphere is improved, and paraffin is discharged from the pressed compact along with the rise of temperature; the compact is degassed when the temperature reaches the threshold value, solid-phase sintering is carried out after purification, and the compact is compact in the compact without gaps during sintering, so that the hardness of the compact is improved.

S5: placing the heat-treated pressed blank into a guide die for die-casting and cooling, and adding a forming agent to finish the die-casting and annealing the pressed blank; after the pressed blank is kept at a high temperature for a certain time, the pressed blank is cooled to room temperature at a certain cooling speed, and the purposes of more uniform and stable structure, internal stress elimination and material shaping improvement are achieved through atomic diffusion.

S6: straightening the pressed blank; the product needs to be straightened by a straightening machine, and the levelness of the product is ensured.

S7: mechanically polishing the outer wall of the pressed compact, and performing sand blasting treatment on the outer wall of the pressed compact; the sand blasting is used for cleaning and coarsening the surface of the metal, so that the fatigue resistance of the product is improved, and the adhesion effect of the external coating is facilitated.

S8: the green compact is subjected to anodic oxidation treatment, so that an oxide layer can be formed on the surface of the green compact, and the hardness and the wear resistance of the surface of a product can be improved; by adopting the electrolysis principle, the product is an anode and is placed in an electrolyte solution to be electrified, so that the product can replace hydrogen in the electrolyte, and an oxidation layer can be formed on the surface of a pressed compact.

S9: lowering and degreasing the green compact, carrying out alkaline etching and activation, electroplating the green compact with 1.25% of nickel to finish nickel plating, and finally drying; the nickel layer can improve the corrosion-resistant fatigue life and service life of the product.

S10: electroplating the green compact with 0.9% chromium pair to complete chromium plating to form a chromium layer; the chromium layer has good adsorbability and can be used as a bottom layer for coating.

S11: the green compact is coated with the antirust coating to form an antirust coating, so that the antirust property of the outer wall of the green compact can be improved, and the outer wall of the green compact is painted and colored; the antirust coating can improve the antirust property of the outer wall of the mountain bike pipe, the paint surface can be subjected to customized coloring treatment, the attractiveness of the product is improved, and the product competitiveness is improved.

Specific example 3

S1: taking 5% of silicon, 3% of copper, 4% of tungsten, 1% of silicon, 5% of zinc, 1% of titanium, 0.5% of manganese, 0.1% of magnesium, 2% of titanium, 1.8% of iron and 74.6% of aluminum;

s2: placing the raw materials in S1 in a stirring ball mill to impact and grind the raw materials, refining and uniformly distributing the raw materials, and adding a certain amount of paraffin; the effect of mixing the raw materials is achieved.

S3: adding the mixture into a shaping die cavity, pressing by a pressure punch, and reducing the distance between powder particles along with the increase of pressure so as to reduce the porosity and further compact the mixture into a pressed compact; and carrying out die-casting molding on the mixture through a pressure device.

S4: heating the pressed compact under a vacuum condition, wherein impurities can be discharged by vacuum dewaxing in the sintering process, the purity of the sintering atmosphere is improved, and paraffin is discharged from the pressed compact along with the rise of temperature; the compact is degassed when the temperature reaches the threshold value, solid-phase sintering is carried out after purification, and the compact is compact in the compact without gaps during sintering, so that the hardness of the compact is improved.

S5: placing the heat-treated pressed blank into a guide die for die-casting and cooling, and adding a forming agent to finish the die-casting and annealing the pressed blank; after the pressed blank is kept at a high temperature for a certain time, the pressed blank is cooled to room temperature at a certain cooling speed, and the purposes of more uniform and stable structure, internal stress elimination and material shaping improvement are achieved through atomic diffusion.

S6: straightening the pressed blank; the product needs to be straightened by a straightening machine, and the levelness of the product is ensured.

S7: mechanically polishing the outer wall of the pressed compact, and performing sand blasting treatment on the outer wall of the pressed compact; the sand blasting is used for cleaning and coarsening the surface of the metal, so that the fatigue resistance of the product is improved, and the adhesion effect of the external coating is facilitated.

S8: the green compact is subjected to anodic oxidation treatment, so that an oxide layer can be formed on the surface of the green compact, and the hardness and the wear resistance of the surface of a product can be improved; by adopting the electrolysis principle, the product is an anode and is placed in an electrolyte solution to be electrified, so that the product can replace hydrogen in the electrolyte, and an oxidation layer can be formed on the surface of a pressed compact.

S9: lowering and degreasing the green compact, carrying out alkaline etching and activation, electroplating 1% of nickel on the green compact to finish nickel plating, and finally drying; the nickel layer can improve the corrosion-resistant fatigue life and service life of the product.

S10: electroplating 0.8% of chromium pair on the green compact to complete chromium plating to form a chromium layer; the chromium layer has good adsorbability and can be used as a bottom layer for coating.

S11: the green compact is coated with the antirust coating to form an antirust coating, so that the antirust property of the outer wall of the green compact can be improved, and the outer wall of the green compact is painted and colored; the antirust coating can improve the antirust property of the outer wall of the mountain bike pipe, the paint surface can be subjected to customized coloring treatment, the attractiveness of the product is improved, and the product competitiveness is improved.

When the aluminum alloy for the mountain bicycle frame tube and the preparation method thereof are used, it is to be noted that the invention relates to the aluminum alloy for the mountain bicycle frame tube and the preparation method thereof, each part is a universal standard part or a part known by a person skilled in the art, and the structure and the principle of the aluminum alloy can be known by the person skilled in the art through a technical manual or a conventional experimental method.

The working principle and the using process of the invention are as follows: taking 5-5.5% of silicon, 3-3.5% of copper, 4-4.5% of tungsten, 1-1.5% of silicon, 5-5.5% of zinc, 1-1.5% of titanium, 0.5-0.7% of manganese, 0.1-0.2% of magnesium, 2-2.5% of titanium, 1.8-2% of iron and 70-74.6% of aluminum; then placing 5-5.5% of silicon, 3-3.5% of copper, 4-4.5% of tungsten, 1-1.5% of silicon, 5-5.5% of zinc, 1-1.5% of titanium, 0.5-0.7% of manganese, 0.1-0.2% of magnesium, 2-2.5% of titanium, 1.8-2% of iron and 70-74.6% of aluminum in a stirring ball mill to impact and grind the raw materials, refining and uniformly distributing the raw materials, and adding a certain amount of paraffin for mixing; then adding the mixed raw materials into a shaping die cavity, pressing the shaping die cavity through a punch of a pressure device, and reducing the distance between powder particles of the mixed materials along with the increase of pressure so as to reduce the void degree and further compact the mixed materials into a pressed compact; the pressed compact is placed in a vacuum heating furnace to be heated, the pressed compact is heated under the vacuum condition, impurities can be discharged by vacuum dewaxing in the sintering process, the purity of sintering atmosphere is improved, paraffin is discharged from the pressed compact along with the rise of temperature, the pressed compact is subjected to degassing reaction along with the temperature reaching a threshold value so as to be purified and subjected to solid phase sintering, and the pressed compact is tightly sintered to have no gap; placing the pressed blank subjected to the heat treatment of the purchased airline ticket into a die for die-casting cooling, and adding a forming agent to complete the die-casting cooling, so that the pressed blank is annealed, namely, the pressed blank is cooled to room temperature at a certain cooling speed after being kept at a high temperature for a certain time, and the atomic diffusion is used for achieving more uniform and stable organization, eliminating internal stress and improving material shaping; straightening the pressed blank by a straightening machine; the outer wall of the pressed compact is mechanically polished by a polisher to ensure that the outer wall is free of burrs, then the outer wall of the pressed compact is subjected to sand blasting by a sand blasting machine, the surface of the pressed compact is cleaned and the metal surface is roughened, the fatigue resistance of the product is improved, meanwhile, the adhesion effect of an external coating is facilitated, the pressed compact is subjected to anodic oxidation treatment, namely, the product is an anode and is placed in an electrolyte solution to be electrified by adopting an electrolysis principle, so that the product can replace hydrogen in the electrolyte, an oxide layer can be formed on the surface of the pressed compact, and the hardness and the wear resistance of the surface of the product can be improved; the pressed blank is subjected to descending degreasing, alkaline etching and activation are carried out, 1-1.5% of nickel is electroplated on the pressed blank to finish nickel plating, and finally, the pressed blank is dried to form a nickel layer, so that the corrosion-resistant fatigue life and the service life of the product are prolonged; then, 0.8-1% of chromium is plated on the green compact to complete chromium plating, so that a chromium layer is formed, has good adsorbability and can be used as a bottom layer for coating; the antirust coating is coated on the product to form an antirust coating, so that the antirust property of the outer wall of the pressed compact can be improved, and then the outer wall of the pressed compact is painted and colored, wherein 0.1-0.2% of impurities are generated in the processing process.

While there have been shown and described what are at present considered the fundamental principles of the invention and its essential features and advantages, it will be apparent to those skilled in the art that the invention is not limited to the details of the foregoing illustrative embodiments, but is capable of other specific forms without departing from the spirit or essential characteristics thereof. The present embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description, and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein.

Furthermore, it should be understood that although the present description refers to embodiments, not every embodiment may contain only a single embodiment, and such description of the embodiments is for clarity only, and those skilled in the art should make the description as a whole, and the embodiments may be combined as appropriate to form other embodiments understood by those skilled in the art.