一种聚酰亚胺P84/MIL-101（Cr）混合基质膜的制备方法
阅读说明：本技术 一种聚酰亚胺P84/MIL-101（Cr）混合基质膜的制备方法 (Preparation method of polyimide P84/MIL-101(Cr) mixed matrix film ) 是由 盖方圆 梁超安 赵晓刚 刘振国 王严 张铁欣 于 2021-09-13 设计创作，主要内容包括：本发明涉及一种基于MIL-101(Cr)混合基质膜的制备方法。本发明属于水处理膜分离领域,具体涉及聚酰亚胺P84和MIL-101(Cr)的混合基质膜,其制备方法包括制备MIL-101(Cr)：将九水硝酸铬与对苯二甲酸溶于去离子水中,水热条件下得到MIL-101(Cr)材料。将聚酰亚胺P84和不同比例的MIL-101(Cr)溶于N,N-二甲基甲酰胺中,超声,搅拌,相转化固化成膜。本方法制备出的P84/MIL-101(Cr)膜,在室温下具有优异的甲基橙和亚甲基蓝混合染料去除能力,具有制备方法简单、成本低廉,易于实现工业化生产的特点。(The invention relates to a preparation method of a mixed matrix film based on MIL-101 (Cr). The invention belongs to the field of water treatment membrane separation, and particularly relates to a mixed matrix membrane of polyimide P84 and MIL-101(Cr), wherein the preparation method comprises the following steps: dissolving chromium nitrate nonahydrate and terephthalic acid in deionized water, and obtaining the MIL-101(Cr) material under the hydrothermal condition. Dissolving polyimide P84 and MIL-101(Cr) with different proportions in N, N-dimethylformamide, performing ultrasonic treatment, stirring, and performing phase inversion curing to form a film. The P84/MIL-101(Cr) film prepared by the method has excellent removal capability of methyl orange and methylene blue mixed dye at room temperature, and has the characteristics of simple preparation method, low cost and easy realization of industrial production.)
技术领域
本发明涉及水处理膜分离领域，涉及聚酰亚胺P84/MIL-101(Cr)混合基质膜的制备方法。
技术背景
染料、重金属离子等有毒化合物对水源的污染是当今世界面临的严重环境问题之一，染料广泛应用于世界各地的造纸、橡胶、纺织和织物工业，这些染料对热、氧化剂和光都很稳定，它们在废水中的存在会扰乱水生生物的生物降解稳定性，因此，在工业废水中染料释放到环境中之前将其去除是至关重要的。其中，膜分离技术有着能耗低、污染小、节能环保等特点广泛应用于污水处理。
高分子聚合物膜由于渗透性和选择性的权衡而限制其应用，为此混合基质膜具有分散填料和聚合物的双重优点有望克服上述限制。MOFs(金属有机框架)是金属离子和有机配体进行自组装的过程，其具有发达的孔隙率、孔径可调、高比表面积、易于官能团化等优点。
以MIL-101(Cr)作为分散填料，比起无机纳米填料由于其本生具有有机官能团与聚合物的相容性更大。MIL-101(Cr)是金属铬和对苯二甲酸自组装而成的一种具有高比表面积、介孔的、亲水性MOFs材料，基于此，本发明提出了以聚酰亚胺P84为聚合物连续相，以MIL-101为分散相的混合基质膜用于甲基橙和亚甲基蓝的混合染料去除。
- 上一篇：一种医用注射器针头装配设备
- 下一篇：一种聚偏氟乙烯超滤膜及其制备方法