阅读说明：本技术 一种机械结构件微结构损伤失效检测分析方法 (Method for detecting and analyzing damage and failure of microstructure of mechanical structural part ) 是由 孟双德 王可君 于 2020-07-17 设计创作，主要内容包括：本发明公开一种机械结构件微结构损伤失效检测分析方法,该方法包括以下步骤：步骤一、缺陷检测：将待检测机械结构件放置在电子加速器的靶头前照射,用探测器对待检测机械结构件进行探测；步骤二、缺陷定位：两个探测器按预设角度接收待检测机械结构件湮灭放出511keV光子,并两个能谱通过三维合成云图,通过云图展示受检机械结构件的缺陷位置；步骤三、S参数计算：光谱的定性分析图,即得到可反映材料劣化信息的S参数；步骤四、缺陷情况分析：对于有缺陷的待检测机械结构件,由于电子的动量小,造成的多普勒展宽小,得到的S参数大。本发明具有根据所放出的γ射线强度,评估材料的劣化情形的特点。(The invention discloses a method for detecting and analyzing damage and failure of a microstructure of a mechanical structural part, which comprises the following steps: step one, defect detection: placing a mechanical structural part to be detected in front of a target head of an electron accelerator for irradiation, and detecting the mechanical structural part to be detected by using a detector; step two, defect positioning: the two detectors receive 511keV photons emitted by annihilation of the mechanical structural component to be detected according to a preset angle, the two energy spectrums are subjected to three-dimensional synthesis to form a cloud picture, and the defect position of the mechanical structural component to be detected is displayed through the cloud picture; step three, S parameter calculation: obtaining a qualitative analysis chart of the spectrum, namely obtaining an S parameter capable of reflecting material degradation information; step four, analyzing the defect condition: for a defective mechanical structural component to be detected, the Doppler broadening caused by small momentum of electrons is small, and the obtained S parameter is large. The present invention has a feature of evaluating the deterioration of a material based on the intensity of gamma rays emitted.)

1. A mechanical structural part microstructure damage failure detection and analysis method is characterized by comprising the following steps;

step one, defect detection: placing a mechanical structural part to be detected in front of a target head of an electron accelerator for irradiation, after the irradiation is finished, transmitting the mechanical structural part to be detected to a detector position, and detecting the mechanical structural part to be detected by using the detector;

the two high-energy germanium detectors detect the inner layer of the mechanical structural part from different directions according to a preset angle theta;

step two, defect positioning: the two detectors receive annihilation of a mechanical structural component to be detected at a preset angle to emit 511keV photons, output signals of the detectors are supplied to an amplifier and a multichannel analyzer of a subsequent circuit, pulse voltage is digitized to obtain two energy spectrums, the two energy spectrums are subjected to three-dimensional synthesis to form a cloud picture, and the defect position of the mechanical structural component to be detected is displayed through the cloud picture;

step three, S parameter calculation: a qualitative analysis graph of the spectrum, wherein the obtained specific spectrum integral is divided by a total background value to obtain an S parameter capable of reflecting material degradation information;

the doppler broadening of the spectrum is measured by S-parameter and full width at half maximum (FWHM), and the formula of S-parameter is:

the S parameter is the area of the smaller part of the energy spectrum with the middle deviation of 511keV compared with the area of the whole energy spectrum; the half-width analysis is the width corresponding to half of the maximum height of the 511keV energy spectrum, and the energy spectrum is analyzed by using an S parameter method; the method analyzes the proportion of different parts in the energy spectrum, and divides the 511keV energy spectrum into A, B, C parts;

step four, analyzing the defect condition: A. b, C the division in the energy spectrum region is not definite, and is generally adjusted according to the actual situation; for a defective mechanical structural part to be detected, the Doppler broadening caused by small momentum of electrons is small, so that the proportion of an area A in an energy spectrum is large, and parts B and C are relatively small, so that the obtained S parameter is large; on the contrary, if the mechanical structural member to be detected has fewer defects, the proportion of the area A is small, and if the proportion of the part B to the part C is large, the S parameter is small.

2. The method for detecting and analyzing damage and failure of the microstructure of the mechanical structural part as recited in claim 1, wherein the energy range of the electron accelerator is 40keV to 10 MeV.

3. The method for detecting and analyzing the damage and failure of the microstructure of the mechanical structural part as recited in claim 1, wherein the detector is a high-energy germanium detector.

Technical Field

The invention relates to a method for detecting and analyzing damage and failure of a microstructure of a mechanical structural part, in particular to a method for detecting and analyzing damage and failure of a microstructure of a mechanical structural part, which can evaluate the degradation condition of a material according to the intensity of emitted gamma rays.

Background

Nondestructive testing is an important means for improving the reliability of the engine and is also an important link for determining the service life of the engine. Most of the current traditional non-destructive inspection methods at home and abroad, such as eddy current and X-ray methods, are useful only after a visible crack or a defect has propagated to the crack generation stage. The fatigue of the atomic layer, embrittlement and material lattice damage before cracks occur cannot be detected.

For example, in the current inspection method for airport mechanical structural components, not only visual inspection (VT, including endoscope), magnetic particle inspection (MT), liquid seepage inspection (PT), ultrasonic inspection (UT) and other non-destructive inspection methods, but also some small components, such as gas turbine generator blades, can be inspected for defects by using X-ray Radiation (RT) technology, but these methods must be found when component defects develop to a certain size or range, for example, inspection by the above methods may be difficult to find for cracks below 0.3mm, and thus there is a certain risk for high-risk flights; there is a need to establish methods and technical means for more sensitive and earlier detection of defects.

Microscopic compared to the above methods, optical or electron microscopy analysis is also possible, and in addition, changes in material hardness values or X-ray diffraction spectra sometimes reveal subtle changes in properties, such as hardening, softening, residual stress or other material degradation phenomena.

The positron is an anti-particle of an electron, the electron has the same mass as the electron and is opposite to the electron in electric property, annihilation is generated when the positron meets the electron in the detected material, 1-3 gamma photons can be generated, and the probability of generating 2 gamma photons is the maximum; the energy of the positron emitted from the incident source is high, on the order of hundreds of keV to several MeV; when the energy is lost through ionization, atom excitation and the like after entering the material, the kinetic energy is reduced to kT level within a few ps, the process is called thermalization, and the thermalized positron is freely diffused or annihilated with electrons in the material.

Disclosure of Invention

The invention aims to provide a method for detecting and analyzing the damage and the failure of a microstructure of a mechanical structure, which can evaluate the deterioration condition of a material according to the intensity of emitted gamma rays.

The purpose of the invention can be realized by the following technical scheme:

a method for detecting and analyzing damage and failure of a microstructure of a mechanical structural part comprises the following steps:

step one, defect detection: placing a mechanical structural part to be detected in front of a target head of an electron accelerator for irradiation, after the irradiation is finished, transmitting the mechanical structural part to be detected to a detector position, and detecting the mechanical structural part to be detected by using the detector;

the two high-energy germanium detectors detect the inner layer of the mechanical structural part from different directions according to a preset angle theta;

step two, defect positioning: the two detectors receive annihilation of a mechanical structural component to be detected at a preset angle to emit 511keV photons, output signals of the detectors are supplied to an amplifier and a multichannel analyzer of a subsequent circuit, pulse voltage is digitized to obtain two energy spectrums, the two energy spectrums are subjected to three-dimensional synthesis to form a cloud picture, and the defect position of the mechanical structural component to be detected is displayed through the cloud picture;

step three, S parameter calculation: a qualitative analysis graph of the spectrum, wherein the obtained specific spectrum integral is divided by a total background value to obtain an S parameter capable of reflecting material degradation information;

the doppler broadening of the spectrum is measured by S-parameter and full width at half maximum (FWHM), and the formula of S-parameter is:

the S parameter is the area of the smaller part of the energy spectrum with the middle deviation of 511keV compared with the area of the whole energy spectrum; the half-width analysis is the width corresponding to half of the maximum height of the 511keV energy spectrum, and the energy spectrum is analyzed by using an S parameter method; the method analyzes the proportion of different parts in the energy spectrum, and divides the 511keV energy spectrum into A, B, C parts;

step four, analyzing the defect condition: A. b, C the division in the energy spectrum region is not definite, and is generally adjusted according to the actual situation; for a defective mechanical structural part to be detected, the Doppler broadening caused by small momentum of electrons is small, so that the proportion of an area A in an energy spectrum is large, and parts B and C are relatively small, so that the obtained S parameter is large; on the contrary, if the defects in the mechanical structural part to be detected are less, the proportion of the area A is small, and if the proportion of the part B and the part C is large, the S parameter is small;

the energy range of the electron accelerator is 40 keV-10 MeV;

the detector is a high-energy germanium detector.

The invention provides a method for detecting and analyzing the damage and failure of a microstructure of a mechanical structural part, which has the characteristic of evaluating the deterioration condition of a material according to the intensity of emitted gamma rays. The invention has the beneficial effects that: the positron will collide with a low-energy negative electron at the defect region and be anodized, annihilated, and release energy in the form of gamma rays; the conditions of mechanical structural parts are different, energy spectrums released by gamma rays are also different, and the size, the number and the type of defects in the material are easy to identify; by response data of gamma ray spectrum and the method, characteristic parameters of the defect can be obtained, namely, fatigue or brittle fracture damage value is quantitatively evaluated; by adopting a coherent lifetime method, not only can relevant defect data be obtained, but also data such as the form, position, size, density and the like of the defect can be obtained; the range of positron in a substance is very short and is only millimeter-scale, so that the surface of the material can only be analyzed by adopting a radioactive source method, and the internal defects of the material cannot be detected, so that the detection of a large-volume object by a positron annihilation analysis technology is limited;

the two high-energy germanium detectors detect the inner layer of the mechanical structural part from different directions according to a preset angle theta; the electron accelerator can generate more X rays with higher energy by targeting, and the sensitivity of the experiment can be improved; meanwhile, the experimental results of the detector under different observation angles theta are considered, and the number of photons detected in each pulse time is obtained through conversion by taking the working state of the accelerator as the tube current, the frequency and the pulse width; the higher the accelerator energy, the higher the corresponding sensitivity. For the iron structural member to be detected, the sensitivity of the 4MeV electron accelerator experiment is low, and the sensitivity is further reduced after hardening; the sensitivity of the 7MeV accelerator is more than 10 times higher than that of 4MeV, and the 7MeV accelerator is ideal and can provide enough space for shielding hardening;

by calculating the S parameter, the analysis of the electron momentum in the energy spectrum can be realized, and the defect condition of the material can be further judged;

the influence of the parameters such as the stretching rate, the maximum tensile strength and the maximum elongation at the test temperature on the S parameter is as follows:

(1) as the test temperature increased, the S parameter increased, showing that as the number of low momentum electrons increased, the number of defects in the sample increased;

(2) with the increase of the stretching rate, the S parameter is in a descending trend, that is, the degree of the defects of the material caused by stretching is reduced with the increase of the stretching rate, and under the condition of higher stretching rate, the micro defects (micro-holes and micro-cracks) in the test piece are not fully generated and developed, and the material is broken because the local stress is greater than the strength of the micro defects, so that the defects of the material are less, and the S parameter is smaller;

(3) the sample with high maximum tensile strength has smaller S parameter than that with low maximum tensile strength, and shows that the sample has less defects in the stretching process; the sample with large maximum elongation has larger S parameter, the higher the maximum tensile strength is, the larger the acting force among molecules of the propellant and the bonding force of the molecules are, and the propellant is more difficult to damage;

the energy range of the electron accelerator is 40 keV-10 MeV; an electron accelerator with lower energy is used for generating bremsstrahlung X rays, the bremsstrahlung X rays are collimated and then irradiate the mechanical structural part to be detected, positive electrons are generated in the mechanical structural part to be detected through an electron pair effect, and meanwhile, various problems of photonuclear reaction are avoided; enabling a high-energy light beam to penetrate through the target drone, enabling a mechanical structural part to be detected to emit a specific spectrum and electrons to form positrons when impacting a material, enabling the positrons generated by the impact to diffuse in the material, and combining with the material and emitting 511keV gamma rays with specific wavelengths when encountering free electrons; since the number of free electrons in a metal material is related to phenomena such as voids, dislocations, hardening and deterioration in the material, the deterioration of the material can be evaluated based on the intensity of gamma rays emitted.

The method comprises the following steps of irradiating a specific material with rays to form an isotope, attaching the radioactive source material to the surface of a mechanical structural part to be detected, diffusing positrons of the radioactive source material in the material, combining the materials when encountering free electrons and emitting specific gamma rays, and thus only needing to make a ray detector approach the mechanical structural part to be detected; the currently more commonly used radioactive source materials include 3 kinds of sodium 22, copper 63/62, gallium 68, etc., and the excitation energy ranges of the three kinds of radioactive source materials are between 0.5MeV and 2.9 MeV.

Drawings

In order to facilitate understanding for those skilled in the art, the present invention will be further described with reference to the accompanying drawings.

FIG. 1 is a block diagram of a method for detecting and analyzing damage and failure of a microstructure of a mechanical structural member according to the present invention;

FIG. 2 is a diagram illustrating a detection manner of a detector of the method for detecting and analyzing damage and failure of the microstructure of a mechanical structural member according to the present invention;

FIG. 3 is a diagram illustrating a Doppler spread spectrum defined by S parameters of the method for detecting and analyzing damage and failure of a microstructure of a mechanical structure according to the present invention.

Detailed Description

The purpose of the invention can be realized by the following technical scheme:

a method for detecting and analyzing damage and failure of a microstructure of a mechanical structural part, referring to FIG. 1, comprises the following steps:

step one, defect detection: placing a mechanical structural part to be detected in front of a target head of an electron accelerator for irradiation, after the irradiation is finished, transmitting the mechanical structural part to be detected to a detector position, and detecting the mechanical structural part to be detected by using the detector; the mechanical structural part to be detected irradiated by the electron accelerator forms radioactivity and emits positrons, and the positrons annihilate 511keV photons in the sample and are received by the detector; for the detection and flaw detection of shallow mechanical structural parts, a photon induction positron annihilation technology is applied, and in-depth photon and X-ray flaw detection is firstly carried out on the detected mechanical structural parts; when the X-ray enters the mechanical structural part, neutrons in partial atomic structures of the mechanical structural part can be collided out; after the atoms lose neutrons, the atoms become isotopes, begin to decay and generate positrons within a period of time, if no defects exist in mechanical structural parts, the positrons are distributed very uniformly, and in the free volume of the material, the volume Vf not occupied by molecules in the material is dispersed in the whole material in a mode of holes; just because of the existence of Vf, the molecular chain can generate random motion in motion; if the mechanical structural part is defective, the positron starts to decelerate and stops in the defective area; eventually, the positron will collide with a low-energy negative electron at the defect region and be anodized, annihilated, and release energy in the form of gamma rays; the conditions of mechanical structural parts are different, energy spectrums released by gamma rays are also different, and the size, the number and the type of defects in the material are easy to identify; by response data of gamma ray spectrum and the method, characteristic parameters of the defect can be obtained, namely, fatigue or brittle fracture damage value is quantitatively evaluated; by adopting a coincidenceleifetime method coincidence lifetime method, not only can relevant defect data be obtained, but also data such as the form, position, size, density and the like of the defect can be obtained; the range of positron in a substance is very short and is only millimeter-scale, so that the surface of the material can only be analyzed by adopting a radioactive source method, and the internal defects of the material cannot be detected, so that the detection of a large-volume object by a positron annihilation analysis technology is limited;

as shown in fig. 2, there are two detectors for detecting, and the two high-energy germanium detectors detect the inner layer of the mechanical structural member from different directions according to a preset angle θ; the electron accelerator can generate more X rays with higher energy by targeting, and the sensitivity of the experiment can be improved; meanwhile, the experimental results of the detector under different observation angles theta are considered, and the number of photons detected in each pulse time is obtained through conversion by taking the working state of the accelerator as the tube current, the frequency and the pulse width; the higher the accelerator energy, the higher the corresponding sensitivity. For the iron structural member to be detected, the sensitivity of the 4MeV electron accelerator experiment is low, and the sensitivity is further reduced after hardening; the sensitivity of the 7MeV accelerator is more than 10 times higher than that of 4MeV, and the 7MeV accelerator is ideal and can provide enough space for shielding hardening;

step two, defect positioning: the two detectors receive annihilation of a mechanical structural component to be detected at a preset angle to emit 511keV photons, output signals of the detectors are supplied to an amplifier and a multichannel analyzer of a subsequent circuit, pulse voltage is digitized to obtain two energy spectrums, the two energy spectrums are subjected to three-dimensional synthesis to form a cloud picture, and the defect position of the mechanical structural component to be detected is displayed through the cloud picture;

step three, S parameter calculation: as shown in fig. 3, in the qualitative analysis chart of the spectrum, the obtained specific spectrum integral is divided by the total background value to obtain an S parameter capable of reflecting material degradation information;

the doppler broadening of the spectrum is measured by S-parameter and full width at half maximum (FWHM), and the formula of S-parameter is:

the S parameter is the area of the smaller part of the energy spectrum with the middle deviation of 511keV compared with the area of the whole energy spectrum; the half-width analysis is the width corresponding to half of the maximum height of the 511keV energy spectrum, and the energy spectrum is analyzed by using an S parameter method; the method analyzes the proportion of different parts in the energy spectrum, and divides the 511keV energy spectrum into A, B, C parts;

step four, analyzing the defect condition: A. b, C the division in the energy spectrum region is not definite, and is generally adjusted according to the actual situation; for a defective mechanical structural part to be detected, the Doppler broadening caused by small momentum of electrons is small, so that the proportion of an area A in an energy spectrum is large, and parts B and C are relatively small, so that the obtained S parameter is large; on the contrary, if the defects in the mechanical structural part to be detected are less, the proportion of the area A is small, and if the proportion of the part B and the part C is large, the S parameter is small; by calculating the S parameter, the analysis of the electron momentum in the energy spectrum can be realized, and the defect condition of the material can be further judged;

the influence of the parameters such as the stretching rate, the maximum tensile strength and the maximum elongation at the test temperature on the S parameter is as follows:

(1) as the test temperature increased, the S parameter increased, showing that as the number of low momentum electrons increased, the number of defects in the sample increased;

(2) with the increase of the stretching rate, the S parameter is in a descending trend, that is, the degree of the defects of the material caused by stretching is reduced with the increase of the stretching rate, and under the condition of higher stretching rate, the micro defects (micro-holes and micro-cracks) in the test piece are not fully generated and developed, and the material is broken because the local stress is greater than the strength of the micro defects, so that the defects of the material are less, and the S parameter is smaller;

(3) the sample with high maximum tensile strength has smaller S parameter than that with low maximum tensile strength, and shows that the sample has less defects in the stretching process; the sample with large maximum elongation has larger S parameter, the higher the maximum tensile strength is, the larger the acting force among molecules of the propellant and the bonding force of the molecules are, and the propellant is more difficult to damage;

the energy range of the electron accelerator is 40 keV-10 MeV; an electron accelerator with lower energy is used for generating bremsstrahlung X rays, the bremsstrahlung X rays are collimated and then irradiate the mechanical structural part to be detected, positive electrons are generated in the mechanical structural part to be detected through an electron pair effect, and meanwhile, various problems of photonuclear reaction are avoided; enabling a high-energy light beam to penetrate through the target drone, enabling a mechanical structural part to be detected to emit a specific spectrum and electrons to form positrons when impacting a material, enabling the positrons generated by the impact to diffuse in the material, and combining with the material and emitting 511keV gamma rays with specific wavelengths when encountering free electrons; since the number of free electrons in a metal material is related to phenomena such as voids, dislocations, hardening and deterioration in the material, the deterioration of the material can be evaluated based on the intensity of gamma rays emitted.

The method comprises the following steps of irradiating a specific material with rays to form an isotope, attaching the radioactive source material to the surface of a mechanical structural part to be detected, diffusing positrons of the radioactive source material in the material, combining the materials when encountering free electrons and emitting specific gamma rays, and thus only needing to make a ray detector approach the mechanical structural part to be detected; the prior commonly used radioactive source materials comprise 3 kinds of sodium 22, copper 63/62, gallium 68 and the like, and the excitation energy range adopted by the three kinds of different radioactive source materials is between 0.5MeV and 2.9 MeV;

the detector is a high-energy germanium detector.

The working principle of the invention is as follows:

in the invention, a mechanical structural part to be detected irradiated by an electron accelerator can form radioactivity and emit positrons, and the positrons annihilate in a sample to emit 511keV photons and are received by a detector; for the detection and flaw detection of shallow mechanical structural parts, a photon induction positron annihilation technology is applied, and in-depth photon and X-ray flaw detection is firstly carried out on the detected mechanical structural parts; when the X-ray enters the mechanical structural part, neutrons in partial atomic structures of the mechanical structural part can be collided out; after the atoms lose neutrons, the atoms become isotopes, begin to decay and generate positrons within a period of time, if no defects exist in mechanical structural parts, the positrons are distributed very uniformly, and in the free volume of the material, the volume Vf not occupied by molecules in the material is dispersed in the whole material in a mode of holes; just because of the existence of Vf, the molecular chain can generate random motion in motion; if the mechanical structural part is defective, the positron starts to decelerate and stops in the defective area; eventually, the positron will collide with a low-energy negative electron at the defect region and be anodized, annihilated, and release energy in the form of gamma rays; the conditions of mechanical structural parts are different, energy spectrums released by gamma rays are also different, and the size, the number and the type of defects in the material are easy to identify; by response data of gamma ray spectrum and the method, characteristic parameters of the defect can be obtained, namely, fatigue or brittle fracture damage value is quantitatively evaluated; by adopting a coherent lifetime method, not only can relevant defect data be obtained, but also data such as the form, position, size, density and the like of the defect can be obtained; the range of positron in a substance is very short and is only millimeter-scale, so that the surface of the material can only be analyzed by adopting a radioactive source method, and the internal defects of the material cannot be detected, so that the detection of a large-volume object by a positron annihilation analysis technology is limited;

the two high-energy germanium detectors detect the inner layer of the mechanical structural part from different directions according to a preset angle theta; the electron accelerator can generate more X rays with higher energy by targeting, and the sensitivity of the experiment can be improved; meanwhile, the experimental results of the detector under different observation angles theta are considered, and the number of photons detected in each pulse time is obtained through conversion by taking the working state of the accelerator as the tube current, the frequency and the pulse width; the higher the accelerator energy, the higher the corresponding sensitivity. For the iron structural member to be detected, the sensitivity of the 4MeV electron accelerator experiment is low, and the sensitivity is further reduced after hardening; the sensitivity of the 7MeV accelerator is more than 10 times higher than that of 4MeV, and the 7MeV accelerator is ideal and can provide enough space for shielding hardening;

by calculating the S parameter, the analysis of the electron momentum in the energy spectrum can be realized, and the defect condition of the material can be further judged;

the influence of the parameters such as the stretching rate, the maximum tensile strength and the maximum elongation at the test temperature on the S parameter is as follows:

(1) as the test temperature increased, the S parameter increased, showing that as the number of low momentum electrons increased, the number of defects in the sample increased;

(2) with the increase of the stretching rate, the S parameter is in a descending trend, that is, the degree of the defects of the material caused by stretching is reduced with the increase of the stretching rate, and under the condition of higher stretching rate, the micro defects (micro-holes and micro-cracks) in the test piece are not fully generated and developed, and the material is broken because the local stress is greater than the strength of the micro defects, so that the defects of the material are less, and the S parameter is smaller;

(3) the sample with high maximum tensile strength has smaller S parameter than that with low maximum tensile strength, and shows that the sample has less defects in the stretching process; the sample with large maximum elongation has larger S parameter, the higher the maximum tensile strength is, the larger the acting force among molecules of the propellant and the bonding force of the molecules are, and the propellant is more difficult to damage;

the energy range of the electron accelerator is 40 keV-10 MeV; an electron accelerator with lower energy is used for generating bremsstrahlung X rays, the bremsstrahlung X rays are collimated and then irradiate the mechanical structural part to be detected, positive electrons are generated in the mechanical structural part to be detected through an electron pair effect, and meanwhile, various problems of photonuclear reaction are avoided; enabling a high-energy light beam to penetrate through the target drone, enabling a mechanical structural part to be detected to emit a specific spectrum and electrons to form positrons when impacting a material, enabling the positrons generated by the impact to diffuse in the material, and combining with the material and emitting 511keV gamma rays with specific wavelengths when encountering free electrons; since the number of free electrons in a metal material is related to phenomena such as voids, dislocations, hardening and deterioration in the material, the deterioration of the material can be evaluated based on the intensity of gamma rays emitted.

The method comprises the following steps of irradiating a specific material with rays to form an isotope, attaching the radioactive source material to the surface of a mechanical structural part to be detected, diffusing positrons of the radioactive source material in the material, combining the materials when encountering free electrons and emitting specific gamma rays, and thus only needing to make a ray detector approach the mechanical structural part to be detected; the currently more commonly used radioactive source materials include 3 kinds of sodium 22, copper 63/62, gallium 68, etc., and the excitation energy ranges of the three kinds of radioactive source materials are between 0.5MeV and 2.9 MeV.

The invention provides a method for detecting and analyzing the damage and failure of a microstructure of a mechanical structural part, which has the characteristic of evaluating the deterioration condition of a material according to the intensity of emitted gamma rays. The invention has the beneficial effects that: the positron will collide with a low-energy negative electron at the defect region and be anodized, annihilated, and release energy in the form of gamma rays; the conditions of mechanical structural parts are different, energy spectrums released by gamma rays are also different, and the size, the number and the type of defects in the material are easy to identify; by response data of gamma ray spectrum and the method, characteristic parameters of the defect can be obtained, namely, fatigue or brittle fracture damage value is quantitatively evaluated; by adopting a coherent lifetime method, not only can relevant defect data be obtained, but also data such as the form, position, size, density and the like of the defect can be obtained; the range of positron in a substance is very short and is only millimeter-scale, so that the surface of the material can only be analyzed by adopting a radioactive source method, and the internal defects of the material cannot be detected, so that the detection of a large-volume object by a positron annihilation analysis technology is limited;

the two high-energy germanium detectors detect the inner layer of the mechanical structural part from different directions according to a preset angle theta; the electron accelerator can generate more X rays with higher energy by targeting, and the sensitivity of the experiment can be improved; meanwhile, the experimental results of the detector under different observation angles theta are considered, and the number of photons detected in each pulse time is obtained through conversion by taking the working state of the accelerator as the tube current, the frequency and the pulse width; the higher the accelerator energy, the higher the corresponding sensitivity. For the iron structural member to be detected, the sensitivity of the 4MeV electron accelerator experiment is low, and the sensitivity is further reduced after hardening; the sensitivity of the 7MeV accelerator is more than 10 times higher than that of 4MeV, and the 7MeV accelerator is ideal and can provide enough space for shielding hardening;

by calculating the S parameter, the analysis of the electron momentum in the energy spectrum can be realized, and the defect condition of the material can be further judged;

the influence of the parameters such as the stretching rate, the maximum tensile strength and the maximum elongation at the test temperature on the S parameter is as follows:

(1) as the test temperature increased, the S parameter increased, showing that as the number of low momentum electrons increased, the number of defects in the sample increased;

(2) with the increase of the stretching rate, the S parameter is in a descending trend, that is, the degree of the defects of the material caused by stretching is reduced with the increase of the stretching rate, and under the condition of higher stretching rate, the micro defects (micro-holes and micro-cracks) in the test piece are not fully generated and developed, and the material is broken because the local stress is greater than the strength of the micro defects, so that the defects of the material are less, and the S parameter is smaller;

(3) the sample with high maximum tensile strength has smaller S parameter than that with low maximum tensile strength, and shows that the sample has less defects in the stretching process; the sample with large maximum elongation has larger S parameter, the higher the maximum tensile strength is, the larger the acting force among molecules of the propellant and the bonding force of the molecules are, and the propellant is more difficult to damage;

the energy range of the electron accelerator is 40 keV-10 MeV; an electron accelerator with lower energy is used for generating bremsstrahlung X rays, the bremsstrahlung X rays are collimated and then irradiate the mechanical structural part to be detected, positive electrons are generated in the mechanical structural part to be detected through an electron pair effect, and meanwhile, various problems of photonuclear reaction are avoided; enabling a high-energy light beam to penetrate through the target drone, enabling a mechanical structural part to be detected to emit a specific spectrum and electrons to form positrons when impacting a material, enabling the positrons generated by the impact to diffuse in the material, and combining with the material and emitting 511keV gamma rays with specific wavelengths when encountering free electrons; since the number of free electrons in a metal material is related to phenomena such as voids, dislocations, hardening and deterioration in the material, the deterioration of the material can be evaluated based on the intensity of gamma rays emitted.

The method comprises the following steps of irradiating a specific material with rays to form an isotope, attaching the radioactive source material to the surface of a mechanical structural part to be detected, diffusing positrons of the radioactive source material in the material, combining the materials when encountering free electrons and emitting specific gamma rays, and thus only needing to make a ray detector approach the mechanical structural part to be detected; the currently more commonly used radioactive source materials include 3 kinds of sodium 22, copper 63/62, gallium 68, etc., and the excitation energy ranges of the three kinds of radioactive source materials are between 0.5MeV and 2.9 MeV.

The foregoing is merely exemplary and illustrative of the present invention and various modifications, additions and substitutions may be made by those skilled in the art to the specific embodiments described without departing from the scope of the invention as defined in the following claims.