阅读说明：本技术 一种能清理3d打印机打印头喷口的溶液 (Solution capable of cleaning nozzle of printing head of 3D printer ) 是由 王寅杰 于 2018-06-15 设计创作，主要内容包括：一种能清理3D打印机打印头喷口清理堵塞的溶液。从德国购进的ExOne3D打印机打印头所用的粘接剂为甲阶酚醛树脂,打印时被压缩空气压迫通过喷口喷到型砂层面上,喷口孔径为0.2mm,使用间歇停留时间一长,树脂就会在喷口孔中固化堵塞,必须由供应商取回维护,既影响了使用,又增加了费用,现自行配制一种氢氧化钾溶液,将打印头喷口浸入,加热到沸腾状态不超过10分钟,喷口中的树脂就被完全溶解,喷口恢复畅通。(A solution capable of cleaning blockage of a nozzle of a printing head of a 3D printer. The binder used by the ExOne3D printer head purchased from Germany is resol, the resol is pressed by compressed air to be sprayed onto the surface of the moulding sand layer through the nozzle during printing, the aperture of the nozzle is 0.2mm, the resin can be solidified and blocked in the nozzle hole after using the printer head for a long time, the resin has to be taken back by a supplier for maintenance, the use is influenced, the cost is increased, a potassium hydroxide solution is prepared by the prior art, the nozzle of the printer head is immersed and heated to a boiling state for no more than 10 minutes, the resin in the nozzle is completely dissolved, and the nozzle is recovered to be unblocked.)

一种能清理3D打印机打印头喷口的溶液

技术领域

3D打印机打印头喷口的清理堵塞的自配溶液

背景技术

3D打印机是一种从德国ExOne进口从图纸到实物，利用3D技术一步成型的设备，用于铸造砂模的成型，可减少制作模具的周期，直接成型加快了交货的进度，但在成型方面，砂模是石英砂和粘接剂分层成型，粘接剂是加入3D打印机的打印头容器后，通入压缩空气将粘接剂从喷口分层喷出，喷口是条形气孔(孔径0.2mm)结构，使用以后，残留的粘接剂会随着时间的延长逐渐硬化，而将喷口堵塞。如果3D打印机连续使用，粘接剂不会停留，就不会有喷口堵塞现象发生，只有当使用间隔时间稍长，粘接剂固化，就会出现喷口堵塞现象了。

每逢出现喷口堵塞现象，按照说明书用乙醇清理，发现清理失效，都是联系供应商***处，由***处专人到现场更换打印头，而将堵塞的打印头带回处理，每逢这种情况发生，首先得联系到***处，再由***处安排时间确定到现场服务，此时3D打印机就无法使用，必须等待来人更换打印头之后，方能再次使用。

发明内容

本发明目的是解决3D打印机打印头喷口堵塞时，能自己维护清理，采用比较简便方法将已堵塞的喷口恢复畅通。

技术方案是预先调制好饱和状态的氢氧化钾溶液，然后将已堵塞的喷口浸没在盛有氢氧化钾饱和溶液的开口容器中，将溶液加热到沸腾状态，喷口的树脂就会在10分钟左右完全溶化在溶液中恢复畅通。

本发明的显著效果是不必将堵塞的喷口再拆下交由供应商更换喷口，而是自行准备溶液，只花费10分钟就可解决喷口堵塞问题，既减少了等待时间，又节省了费用。

附图说明

图1、打印头浸入K(OH)清理示意图。

其中，1、打印头 2、喷口 3、容器 4、氢氧化钾溶液

具体实施方式

将打印头1的喷口2浸入盛有氢氧化钾饱和溶液4的容器3中，将氢氧化钾溶液4加热，使喷口2孔隙中树脂溶解。