一种Ag/AgBr石墨烯复合凝胶的制备方法
阅读说明：本技术 一种Ag/AgBr石墨烯复合凝胶的制备方法 (Preparation method of Ag/AgBr graphene composite gel ) 是由 蔡小丹 于 2020-12-07 设计创作，主要内容包括：本发明公开了一种Ag/AgBr石墨烯复合凝胶的制备方法,包括下述步骤：首先将氧化石墨烯和硫酸与磷酸混合得到磷硫共掺杂氧化石墨烯,之后将其与NaHSO-3反应制备得到石墨烯凝胶,最后将复合凝胶与硝酸银、十六烷基三甲基溴化铵(CTAB)反应得到Ag/AgBr石墨烯复合凝胶。所述方法成本低、操作简单、高效节能,得到的复合凝胶应用于降解染料污水中的罗丹明B。(The invention discloses a preparation method of Ag/AgBr graphene composite gel, which comprises the following steps: firstly, mixing graphene oxide, sulfuric acid and phosphoric acid to obtain phosphorus-sulfur co-doped graphene oxide, and then mixing the phosphorus-sulfur co-doped graphene oxide with NaHSO 3 The graphene gel is prepared by reactionAnd finally, reacting the composite gel with silver nitrate and Cetyl Trimethyl Ammonium Bromide (CTAB) to obtain the Ag/AgBr graphene composite gel. The method is low in cost, simple to operate, efficient and energy-saving, and the obtained composite gel is applied to degrading rhodamine B in dye sewage.)
技术领域
本发明应用于光催化降解染料污水中的罗丹明B，具体涉及一种Ag/AgBr石墨烯复合凝胶的制备方法。
背景技术
在我们的日常生活中，染料在纺织服装业、造纸业、食品加工业等领域都有着及其广泛的应用。因此，染料废水也成为了影响人们生活和健康的一大污染源。在众多染料中，罗丹明B(RhB)是一种通过人工合成的荧光染料，呈碱性。它应用于造纸业、化妆品工业、矿业及医药等各大领域中，正因为它稳定性强、颜色鲜亮、价格低廉，也成为一种典型的工业染料废水污染物。其分子链中的醌式结构是罗丹明B显色的主要官能团，要降解它就要破坏该结构。目前，银/卤化银(Ag/AgX,X＝Cl,Br)作为一种光催化剂已经被广泛应用于污染物的光降解过程中，这是基于银/卤化银具有比较小的能带宽度。事实上，相对于Cl而言，Br具有较低的电子亲和能，因此Ag/AgBr显示了更高的催化活性。但目前为止，银/溴化银颗粒容易团聚的问题仍然存在。在近些年，由于石墨烯引人注目的物理性质和广泛的应用从而引起大家广泛的关注。石墨烯是通过sp2杂化碳原子形成的二维六角网格状的晶体,其厚度仅为单原子层。石墨烯其独特的电子结构特征和较大的比表面积，使其在在光催化降解有机染料方面显示出独特的优势。然而，由于还原石墨烯容易堆积和较差的水溶性，研究人员很少对石墨烯基光催化材料进行研究。氧化石墨烯表面富含有大量含氧官能团，比如羟基，羧基，环氧基等等，这些含氧官能团有效提高了氧化石墨烯在极性溶剂中的溶解度。鉴于以上的想法，很有必要去发展和制备rGO/Ag/AgX这类复合材料，但纯石墨烯的结构是十分稳定的，能够提供负载金属纳米颗粒的“负载位点”极少，且在催化过程中金属纳米颗粒还会团聚和脱落，从而导致催化剂本身性能降低。因此，大量的研究开始使用化学掺杂的方法来改良石墨烯的表面结构，以此来提升催化剂的催化性能。