阅读说明：本技术 基于钛线和生物可吸收聚合物的自固定网状植入物 (Self-fixating mesh implant based on titanium wire and bioabsorbable polymer ) 是由 A·A·卡赞采夫 A·A·尤苏波夫 A·I·阿列恒 V·A·扎瓦列夫 于 2018-01-31 设计创作，主要内容包括：本发明涉及医学和医疗技术的领域,目的在于改善用于疝修补术的技术网状植入物。一种自固定网状植入物由两层组成,上层和下层,基于钛线的网状层在上侧,生物可吸收聚合物层在下侧,其中钛线表面制成凹凸状。技术效果包括提高手术领域中固定植入物的效率,提高可塑性并降低植入物线破损风险,使固定简单化并提高固定的强度,保证植入物整个表面均匀固定在手术伤口的组织上,缩短手术持续时间,并且,作为结果,减少了麻醉剂量和创口体积,从而降低并发症的发生率。(The present invention relates to the field of medical and medical technology, with the aim of improving technical mesh implants for hernia repair. A self-fixating mesh implant is composed of two layers, an upper layer and a lower layer, a mesh layer based on titanium wires on the upper side, and a bioabsorbable polymer layer on the lower side, wherein the surface of the titanium wires is made concave-convex. Technical effects include improving the efficiency of fixing implants in the surgical field, improving plasticity and reducing the risk of implant thread breakage, simplifying fixation and improving strength of fixation, ensuring that the entire surface of the implant is uniformly fixed on the tissue of a surgical wound, shortening the duration of the surgery, and, as a result, reducing the anesthetic dose and wound volume, thereby reducing the incidence of complications.)

1. A self-fixing mesh implant is composed of two layers, an upper layer and a lower layer, a mesh layer based on titanium wires is arranged on the upper side, and a bioabsorbable polymer layer is arranged on the lower side, wherein the surface of the titanium wires is made into a concave-convex shape.

2. The self-fixating mesh implant of claim 1, wherein the titanium wire is made of a grade 5 alloy.

3. The self-fixating mesh implant of claim 1, wherein the surface relief of the titanium wire is made with a non-uniform titanium wire diameter that fluctuates from 0.00025 mm.

4. The self-fixating mesh implant of claim 1, wherein the surface of the concavo-convex titanium wire is coated with an oxide film.

5. The self-fixating mesh implant of claim 1, wherein the titanium wire thickness is 15-120 μ ι η.

6. The self-fixating mesh implant of claim 1, wherein the surface density of the titanium mesh is 20-80g/m ²。

7. The self-fixating mesh implant of claim 1, wherein the mesh size is 0.1-2 mm.

8. The self-fixating reticulated implant of claim 1, wherein the lower layer is made of a bioabsorbable polymer selected from polylactic acids.

9. The self-fixating mesh implant according to claim 1, wherein the bioabsorbable polymer is present in the form of droplets having a diameter of 0.2-1mm, located over the entire underlying surface.

10. The self-fixating reticulated implant of claim 1, wherein a lower layer of bioabsorbable polymer contains at least one drug.

Technical Field

The present invention relates to the field of medical and medical technology, with the aim of improving technical mesh implants for hernia repair.

Background

Disclosure of Invention

The technical problem solved by the proposed technical scheme is to develop a reticular titanium implant which can be fixed immediately without additional fixing frames (suture materials, nails, anchors and glue) in the surgical field.

Technical effects include improving the efficiency of fixing implants in the surgical field, simplifying fixation and improving the strength of fixation, ensuring that the entire surface of the implant is uniformly fixed on the tissue of the surgical wound, improving plasticity and reducing the risk of implant thread breakage, shortening the duration of the surgery, and, as a result, reducing the anesthetic dose and wound volume, thereby reducing the incidence of complications and enabling the patient to recover quickly.

The technical effect is achieved thanks to the fact that: the self-fixating mesh implant consists of two layers, an upper layer and a lower layer, a titanium wire based mesh layer on the upper side and a bioabsorbable polymer layer on the lower side, wherein the surface of the titanium wire is made concave-convex (relief).

The titanium wire is made of 5-grade alloy.

The surface irregularities of the titanium wire were made in a nonuniform titanium wire diameter fluctuating from 0.00025 mm.

The surface of the concave-convex titanium wire is coated with an oxide film.

The thickness of the titanium wire is 15-120 μm.

The surface density of the titanium mesh is 20-80g/m²。

The mesh size is 0.1-2 mm.

The lower layer is made of a bioabsorbable polymer selected from polylactic acid.

The bioabsorbable polymer is in the form of drops having a diameter of 0.2-1mm, located over the entire underlying surface.

The lower layer of bioabsorbable polymer contains at least one drug.

Drawings

FIG. 1. mesh implant;

FIG. 2 is a schematic view of a cross-section of an implant;

FIG. 3a shows a state of a series of crossing loops in a mesh fabric made of uneven threads;

FIG. 3b shows the state of the series of crossing loops in a mesh fabric made of threads without irregularities;

FIG. 4 is a graph of zero stiffness in tension for a woven mesh;

FIG. 5a examples of line surface relief after chemical etching;

FIG. 5b examples of line surface relief after ion treatment;

FIG. 6a. cross section of a line with a longitudinal sharp defect prior to treatment;

figure 6b. cross section of a line with a smooth longitudinal defect after treatment.

Detailed Description

The invention is based on the use of bioabsorbable polymers as a fixation frame for a mesh implant made of titanium wires.

The self-fixating mesh implant 1 consists of two layers 2 and 3, wherein the layer 2 made of a titanium wire-based mesh is on the upper side and the layer 3 made of a bioabsorbable polymer is on the lower side.

The upper layer 2 is represented by a weft-knitted or warp-knitted mesh, which can be made of titanium wires of the alloys VT1-00, VT-1.00wa (grade 1) or VT6 (grade 5) in a wire thickness of 15-120 μm. The surface density of the net is 20-80g/m²The size of the grid is 0.1-2 mm. The titanium wire used provides high bioinert and plasticity of the wire, which can avoid tissue damage.

The titanium wire is made according to the concave-convex surface.

The technical process capable of realizing the unevenness on the surface of the titanium wire comprises the following steps: power sonication, chemical etching, electrochemical polishing, ion treatment, etc. These treatments reduce the titanium wire diameter by 10-35% of the original diameter while reducing the inter loop contact area. As a result, a "telescoping effect" is obtained: the loops and wires pass between the loops into the area adjacent the loops, shown in fig. 3 a. This effect was not observed on the untreated line (fig. 3 a). In fig. 3a and 3a, the arrows and lines indicate the interpenetration of rings and lines within a ring between rings passing through in a ring train; the interpenetration in fig. 3a is stronger.

The telescoping effect and the reduction in drag in the crossover ring contact area are the primary reasons for eliminating the "spring" characteristic. This fact is confirmed by measuring the mechanical properties of the material.

Thus, when the knitted mesh is stretched, there is a zero stiffness (Z period) period, where Z aten is the zero stiffness of the mesh fabric with embossed threads (tension knitted metal fabric) and Z nat is the zero stiffness of the mesh fabric with no embossed threads (natural knitted metal fabric), i.e. the area on the graph when the mesh fabric is stretched without resistance (fig. 4). When the conventional mesh fabric and the treated mesh fabric of the same knitting type and thread thickness are compared, it can be confirmed that the area of zero stiffness of the treated mesh fabric made of the embossed threads is larger by 20% or more than that of the untreated mesh fabric made of the thread having no unevenness.

As a result of the process flow, irregularities appear on the surface of the titanium wire: irregularly positioned depressions and collisions (fig. 5a and 5 b).

Furthermore, the longitudinal sharp defects (fig. 6a) produced by the drawn wire are smoothed during the treatment of the surface of the wire in the woven mesh fabric structure (for example, by electrochemical polishing). The defects after machining are shown smoothly in figure 6 b. The smooth longitudinal defect, which is the concentrated area of internal stress, compensates for the residual stress of the thread itself and reduces the risk of breakage of the mesh fabric.

The result of the process is also a titanium wire with a non-uniform diameter, with a length that fluctuates from 0.00025mm, which also provides an additional degree of freedom of the cross-ring gap.

In order to further improve the plasticity, an oxide film having a thickness of 1 to 3 μm, a low coefficient of sliding friction, and allowing the rings to easily slide relative to each other (which has a positive effect on the ductility of the material) may be applied to the surface of the concavo-convex titanium wire. The surface oxide film reduces friction between the braided rings and the accompanying negative attributes: breakage when straightening the material, etc. The oxide film is obtained by immersing the mesh fabric made of the uneven thread in an electroplating bath (current constant) filled with a necessary solution for a certain period of time. Depending on the time and the voltage selected, the surface of the titanium wire gets an oxide film with a thickness of 1-3 μm. In this case, the thickness of the wire itself is not increased.

The implant 1 has an oval shape 5-15cm wide and the same length (fig. 1).

The bioabsorbable polymer is selected from polylactic acid. They are used as the lower (anchoring) layer 3 (fig. 2) by anchoring them to the underside of the mesh ring structure. The polymer layer may consist of drops having a diameter of 0.2-1 mm. The drops are firmly fixed, covering the mesh ring from three sides. The total thickness of the drop-shaped layer is not more than 0.2-2 mm. The thickness of the entire implant is in the range of 0.5-4 mm.

Drugs may be included in the structure of the bioabsorbable polymer: antibiotics, anti-inflammatory agents, and the like. The medicine is gradually released, and has prolonged therapeutic effect, and can prevent inflammation and wound infection.

The claimed invention is capable of:

-fast secure fixation of the implant;

-ensuring a uniform fixation of the entire surface of the implant on the surgically traumatized tissue;

significantly reducing the duration of the surgery, with consequent reduction in the anesthetic dose and in the wound volume, thus reducing the incidence of complications;

-a gradual release of the temporarily stored drug from the bioabsorbable material is achieved;

in the long term, the removal of foreign bodies other than titanium wires from surgical wounds is ensured.

The high degree of plasticity of the mesh minimizes the spring characteristics, reduces the possibility of biomechanical repulsion between the tissue and the mucosa, and enables the material to be placed under the mucosa without risk of injury. The mesh implant is free to expand at the surface of the surgical wound, readily assuming and maintaining a given shape, and if necessary, can be stretched to simulate the shape of the surgical wound.

The high porosity increases the permeability of biological fluids to the implant, accelerates the process of fibroblast and osteoblast colonization, and improves the bio-integration of the material.

The mesh fabric with surface irregularities made of titanium thread, once in contact with the wound surface, is saturated with blood and wound exudate, which exhibits a remarkable adhesion capacity to the wound surface, providing temporary self-fixing, eliminating the need for the surgeon to use other fixing elements: suture material, needles, miniscrew, etc. The high adhesion to the wound surface allows the titanium mesh to be placed onto the tissue without tension, under or over the implant, preventing frequent complications such as surgical wound dehiscence.

At the same time, the highly porous structure does not retain wound exudate, precluding fluid leakage and subsequent infection.

The irregularities of the thread surface significantly improve the fixation of fibrin fibres thereon, thereby facilitating the attraction of fibroblasts as a source of newly formed connective tissue.