阅读说明：本技术 热喷涂涂层封孔剂及其制备方法和封孔方法 (Thermal spraying coating hole sealing agent, preparation method thereof and hole sealing method ) 是由 邓春银 覃恩伟 刘成威 陆海峰 史一岭 黄骞 王博 吴树辉 魏少翀 陈国星 于 2020-12-02 设计创作，主要内容包括：本发明公开了一种热喷涂涂层封孔剂,所述封孔剂包括合金粉末、分散剂以及载体,所述合金粉末在所述封孔剂中的质量占比为5～10％,所述封孔剂的粘度为25℃下0.05～0.1Pa·S。采用合金粉末制备得到的封孔剂,后续能够对合金粉末进行重熔后实现封孔的功能,且持续效果好,不易失效。分散剂用于对合金粉末进行分散,避免合金粉末的团聚,并采用载体溶剂对合金粉末进行分散支撑,达到合金粉末均匀分散的目的。并通过控制合金粉末的占比、封孔剂的粘度以及本发明中的封孔流程和方法,使得封孔剂能够流入涂层孔隙并具有更大的渗透深度,达到更好的封孔效果。(The invention discloses a hole sealing agent for a thermal spraying coating, which comprises alloy powder, a dispersing agent and a carrier, wherein the mass ratio of the alloy powder in the hole sealing agent is 5-10%, and the viscosity of the hole sealing agent is 0.05-0.1 Pa.S at 25 ℃. The hole sealing agent prepared from the alloy powder can realize the hole sealing function after remelting the alloy powder, and has good continuous effect and difficult failure. The dispersing agent is used for dispersing the alloy powder to avoid the agglomeration of the alloy powder, and the carrier solvent is used for dispersing and supporting the alloy powder to achieve the aim of uniformly dispersing the alloy powder. By controlling the proportion of the alloy powder, the viscosity of the sealant and the hole sealing process and method, the sealant can flow into the coating pores and has larger penetration depth, so that a better hole sealing effect is achieved.)

1. A thermal spraying coating hole sealing agent is characterized in that: the hole sealing agent comprises alloy powder, a dispersing agent and a carrier, wherein the mass ratio of the alloy powder in the hole sealing agent is 5-10%, and the viscosity of the hole sealing agent is 0.05-0.1 Pa.S at 25 ℃.

2. The sealant according to claim 1, characterized in that: the alloy powder comprises, by mass, 11-19% of Cr, 3.5-5.5% of Si, 1.5-3.5% of B, and the balance of Ni.

3. The sealant according to claim 1, characterized in that: the grain size range of the alloy powder is 0.5-5 μm.

4. The sealant according to claim 1, characterized in that: the dispersant is acetone, and the carrier is a sodium silicate solvent.

5. The sealant according to claim 1, characterized in that: the mass ratio of the dispersing agent in the hole sealing agent is 30-40%.

6. A method for preparing the hole sealing agent according to any one of claims 1 to 5, characterized in that: the method comprises the following steps: preparing an alloy block, preparing the alloy block to obtain alloy powder, dispersing the alloy powder in a dispersing agent to obtain an alloy solution, and mixing the alloy solution with a carrier solvent to obtain the hole sealing agent.

7. The method of claim 6, wherein: the method specifically comprises the following steps: preparing an alloy block by a physical metallurgy method, impacting the alloy block by adopting an aerosol method to obtain alloy powder, dispersing the alloy powder in acetone by ultrasonic waves to obtain an alloy solution, and adding the alloy solution into a carrier solvent to obtain the hole sealing agent.

8. A method of sealing pores with the sealant according to any one of claims 1 to 5, wherein the sealing method comprises the steps of: placing a coating component to be sealed in a closed container, adding a sealing agent into the closed container, filling the sealing agent into the closed container, and controlling the closed container to be in a negative pressure state so that the sealing agent flows into pores in the coating; discharging the hole sealing agent in the closed container, cleaning the coating part, taking out the coating part and drying the coating part; and then remelting the sealant in the coating part to ensure that alloy powder in the sealant is solidified after remelting and the pores of the coating part are filled.

9. The pore sealing method according to claim 8, characterized in that: the hole sealing method also comprises a pressurizing step before the hole sealing agent in the closed container is discharged, and specifically comprises the following steps: and after the pressure in the closed container is recovered to be normal pressure, pressurizing the closed container and maintaining the pressure.

10. The pore sealing method according to claim 8, characterized in that: and the cleaning step is to add water into the closed container and perform circulating cleaning, wherein the temperature of the water is not lower than 85 ℃.

Technical Field

The invention belongs to the technical field of hole sealing, and particularly relates to a thermal spraying coating hole sealing agent, a preparation method of the hole sealing agent and a method for sealing holes by using the hole sealing agent.

Background

The thermal spraying technology is a method of heating a spraying material to a molten or semi-molten state by using a heat source, spraying and depositing the spraying material on the surface of a pretreated substrate at a certain speed to form a coating, and endowing the surface of the substrate with special properties.

The thermal spraying coating is formed by mutually superposed particles, and pores are inevitably formed among the superposed particles, and the defects of the pores enable a corrosive medium to rapidly diffuse into a channel, thereby obviously reducing the corrosion performance of the coating. In particular, the presence of the through pores allows corrosive media to reach the surface of the protected substrate through the pores, causing chemical or electrochemical erosion of the coating and the substrate, corrosion products to accumulate at the interface, cracking and peeling of the thermal spray coating, and ultimately leading to failure of the coating.

The main approach for solving the problem of pores in the thermal spraying coating is to adopt a hole sealing technology, namely, a hole sealing agent (generally organic material oily matter) is coated and permeates into the thermal spraying coating to plug the pores of the thermal spraying coating, so that the hole sealing treatment of the thermal spraying coating is realized.

However, there are two problems to be solved in the current field of coating sealing:

firstly, the pore sealing agent is limited by the structural stability of the organic matter, and the service temperature of the pore sealing agent of the pure organic matter component is limited (generally less than 300 ℃).

Secondly, the traditional hole sealing method is a normal pressure brush coating type, namely, the organic hole sealing agent is manually and uniformly brushed on the surface of the coating under the normal pressure environment, and the hole sealing agent permeates into the pores of the coating by depending on the self-fluidity. The normal-pressure brushing type hole sealing process has the following defects:

(1) the technical defects of the normal-pressure brushing type hole sealing process are as follows:

the normal-pressure brushing type hole sealing process has the defects of shallow penetration depth of a hole sealing agent and nonuniform penetration depth of the hole sealing agent, and the service life of a coating is restricted. The surface of the coating is continuously worn by the medium during the service period of the coating, once the wear amount exceeds the penetration depth of the sealant, the pores among the particles in the coating are exposed to the medium environment, the corrosive medium can reach the protected matrix through the pores, the coating is easy to peel off, and the corrosion resistance or sealing effect is lost.

1. The penetration depth of the hole sealing agent is shallow: under the normal pressure brushing process, the sealant permeates into tiny pores on the surface of the coating by means of self-fluidity, and because air remains in the pores and the self-fluidity of the sealant is limited, the sealant can only permeate to the shallow surface of the coating, and the general penetration depth is about 20 mu m.

General industrial experience shows that the coating on the surface of a rotating part of rotating mechanical equipment operating in a conventional medium environment can fall off within 1-3 years of service time, and the coating which is controlled improperly by a hole sealing process falls off and fails within 1 year of service.

2. The penetration depth of the sealant is not uniform: the normal-pressure brushing process is manually operated, and the experience and proficiency of operators and the geometric shape of the surface of a coating all influence the brushing uniformity of the sealant. If the thickness of the coating layer is not uniform, it may cause the penetration depth of the sealant to be shallower at the portion of the thin coating layer than at other portions. Industry experience has shown that the depth of penetration under the brush-coating process is 50% less at the shallowest depth than at the deepest depth. The penetration shallow part becomes the weak point of the service life of the coating and influences the service life of the coating.

(2) The normal-pressure brushing type hole sealing process has low production efficiency and is embodied in two aspects:

1. the curing time of the sealant is long: the sealant curing time refers to the time required for the sealant to brush on the surface of the coating until the sealant solidifies in the pores of the coating.

The normal-pressure brush-coating type hole sealing process depends on the fact that the self-fluidity of the hole sealing agent permeates into the pores of the coating, the fluidity of the hole sealing agent is generally poor, and the time consumption of the dynamic process that the hole sealing agent flows into and fills the pores is long. Industry experience has shown that cure times require at least 24 hours.

2. Difficult to automate: as mentioned above, the brush-coating hole sealing process is a manual operation activity, and the manual construction according to parts must be carried out by experienced personnel, and at present, the industrial automation process is not realized, so that the activity of carrying out high-efficiency thermal spraying construction on a large scale and in batches is restricted.

Disclosure of Invention

In view of the above, in order to overcome the defects of the prior art and achieve the above object, the present invention provides a thermal spray coating hole sealing agent, which can realize in-situ remelting, and has a deep penetration depth and a good hole sealing effect.

In order to achieve the purpose, the invention adopts the following technical scheme:

the hole sealing agent for the thermal spraying coating comprises alloy powder, a dispersing agent and a carrier, wherein the mass ratio of the alloy powder in the hole sealing agent is 5-10%, and the viscosity of the hole sealing agent is 0.05-0.1 Pa.S at 25 ℃. The viscosity of the sodium silicate solvent is preferably 0.01 to 0.05 Pa.S at 25 ℃.

The hole sealing agent prepared from the alloy powder can realize the hole sealing function after remelting the alloy powder, and has good continuous effect and difficult failure. The dispersing agent is used for dispersing the alloy powder to avoid the agglomeration of the alloy powder, and the carrier solvent is used for dispersing and supporting the alloy powder to achieve the aim of uniformly dispersing the alloy powder. And by controlling the proportion of the alloy powder and the viscosity of the sealant, the sealant can flow into the pores of the coating and has larger penetration depth, so that a better hole sealing effect is achieved.

According to some preferred embodiments of the present invention, the alloy powder contains, by mass%, 11 to 19% of Cr, 3.5 to 5.5% of Si, 1.5 to 3.5% of B, and the balance Ni. By reasonably setting the proportion of each element in the alloy powder, the hole sealing effect and the lasting effect after the hole sealing agent is remelted are better.

According to some preferred embodiments of the present invention, the alloy powder has a particle size in the range of 0.5 to 5 μm. The particle size is too small, the remelting and hole sealing effects are not good, and the particle size is too large to enter the coating pores, so that the remelting and hole sealing effects are influenced.

According to some preferred embodiments of the invention, the dispersant is acetone and the carrier is a sodium silicate solvent. The acetone and the sodium silicate are adopted to achieve better dispersion and support effects of the alloy powder compared with other reagents.

According to some preferred embodiments of the present invention, the mass ratio of the dispersant in the hole sealing agent is 30-40%. The content of the dispersing agent is reasonably controlled, so that the dispersing effect of the alloy powder is controlled on one hand, and the viscosity of the product can be controlled on the other hand.

The invention also provides a preparation method of the hole sealing agent, which comprises the following steps: preparing an alloy block, preparing the alloy block to obtain alloy powder, dispersing the alloy powder in a dispersing agent to obtain an alloy solution, and mixing the alloy solution with a carrier solvent to obtain the hole sealing agent. The hole sealing agent is formed by mixing the prepared alloy solution with a carrier solvent, so that the problem that the alloy powder cannot be dispersed due to agglomeration is avoided.

According to some preferred implementation aspects of the invention, the method specifically comprises the following steps: preparing an alloy block by a physical metallurgy method, impacting the alloy block by adopting an aerosol method (high-speed airflow) to obtain alloy powder, dispersing the alloy powder in acetone by ultrasonic waves to obtain an alloy solution, and adding the alloy solution into a carrier solvent to obtain the hole sealing agent. The physical metallurgy method and the aerosol method for preparing the alloy block are conventional methods in the related field. The alloy powder can be further dispersed by adopting ultrasonic waves, so that the agglomeration of the alloy powder is avoided.

The invention also provides a method for sealing holes by adopting the hole sealing agent, which comprises the following steps: placing a coating component to be sealed in a closed container, adding a sealing agent into the closed container, filling the sealing agent into the closed container, and controlling the closed container to be in a negative pressure state so that the sealing agent flows into pores in the coating; discharging the hole sealing agent in the closed container, cleaning the coating part, taking out the coating part and drying the coating part; and then remelting the sealant in the coating part to ensure that alloy powder in the sealant is solidified after remelting and the pores of the coating part are filled. By adopting the process method and matching with the hole sealing agent, the hole sealing agent can penetrate into the pores of the coating and carry out in-situ remelting in the pores, so that the effect of fully sealing the pores is achieved, and the continuous effect is good.

According to some preferred embodiments of the invention, the sealing method further comprises a pressurizing step before discharging the sealing agent in the closed container, and specifically comprises the following steps: and after the pressure in the closed container is recovered to be normal pressure, pressurizing the closed container, and maintaining for a certain time. Namely, a positive pressure process is carried out after the negative pressure, so that the sealant can better enter the pores of the coating.

According to some preferred embodiments of the invention, the cleaning is to add water into the closed container and perform circulating cleaning, the temperature of the water is not lower than 85 ℃, so as to better clean the sealant remained on the surface of the coating part, and meanwhile, the organic components in the sealant are solidified and cured in the temperature environment of more than 85 ℃ to fill the pores in the coating.

In some embodiments of the present invention, the sealing method comprises the following steps:

A. and placing the coating component to be sealed in a closed container.

B. And feeding the liquid hole sealing agent into the closed container.

C. And pumping air in the container from the top of the closed container, finally filling the whole closed container with the hole sealing agent, and maintaining the container in a negative pressure state, wherein the negative pressure is maintained at 0-10 pa (absolute pressure) for 20-30 min. The negative pressure state can pump out air in the pores, which is helpful for the sealant to flow into the pores in the coating and reach deeper penetration depth.

D. The container is communicated with the atmosphere, and the pressure in the closed container is recovered to be normal pressure.

E. And pressurizing the inside of the closed container from the top of the closed container, wherein the pressure is maintained to be not less than 6-50 bar (absolute pressure), and the maintaining time is 20-30 min. The pressurization further forces the sealant to enter the pores inside the coating and reach a deeper penetration depth.

F. And discharging the hole sealing agent in the closed container.

G. And (3) communicating the closed container with a hot water tank, circulating the hot water for 10-15 min, and cleaning the residual hole sealing agent adhered to the surface of the coating part, wherein the temperature of the hot water is not lower than 85 ℃. And under the heating of high-temperature water, the sealant remained in the pores of the coating is solidified and fills the pores.

H. And taking out the coating part and airing.

I. The hole sealing agent in the coating hole is heated and melted by adopting modes such as laser heating, so that metal powder in the hole sealing agent is melted in situ, and is deformed and solidified after being melted to seal the hole, thereby achieving the hole sealing effect.

Compared with the prior art, the invention has the advantages that: the self-sealing hole sealing agent for the thermal spraying coating is prepared from alloy powder, can realize the hole sealing function after remelting the alloy powder, is good in continuous effect and not easy to lose efficacy. The dispersing agent is used for dispersing the alloy powder to avoid the agglomeration of the alloy powder, and the carrier solvent is used for dispersing and supporting the alloy powder to achieve the aim of uniformly dispersing the alloy powder. And by controlling the proportion of the alloy powder and the viscosity of the hole sealing agent and matching with a hole sealing process and a hole sealing method, the hole sealing agent can flow into the pores of the coating and has larger penetration depth, so that a better hole sealing effect is achieved.

Drawings

In order to more clearly illustrate the technical solutions in the embodiments of the present invention, the drawings needed to be used in the description of the embodiments will be briefly introduced below, and it is obvious that the drawings in the following description are only some embodiments of the present invention, and it is obvious for those skilled in the art to obtain other drawings based on these drawings without creative efforts.

FIG. 1 is a schematic diagram of a hole sealing method according to a preferred embodiment of the present invention;

FIG. 2 is a schematic diagram of the sealing method in step B according to the preferred embodiment of the present invention;

FIG. 3 is a schematic diagram of the sealing method in step C according to the preferred embodiment of the present invention;

FIG. 4 is a schematic diagram of a hole sealing method in step D according to a preferred embodiment of the present invention;

FIG. 5 is a schematic diagram of a step E of the hole sealing method in the preferred embodiment of the present invention;

FIG. 6 is a schematic diagram of a sealing method in step F according to a preferred embodiment of the present invention;

FIG. 7 is a schematic diagram of a step G of the hole sealing method in the preferred embodiment of the present invention;

FIG. 8 is a schematic diagram of a hole sealing method in step H according to a preferred embodiment of the present invention;

wherein: 1 a closure for closing the container, 2 a coating member, 3 a sealant, 41 a first opening, 42 a second opening, 43 a third opening, 44 a fourth opening.

Detailed Description

In order to make those skilled in the art better understand the technical solution of the present invention, the technical solution in the embodiment of the present invention will be clearly and completely described below with reference to the drawings in the embodiment of the present invention, and it is obvious that the described embodiment is only a part of the embodiment of the present invention, and not a whole embodiment. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.

Example one hole sealing agent

The thermal spray coating hole sealing agent in the embodiment comprises three components: alloy powder, a dispersant and a carrier solvent. Wherein the mass ratio of the alloy powder in the hole sealing agent is 5-10%, the mass ratio of the dispersing agent is 30-40%, and the balance is the carrier solvent. The viscosity of the hole sealing agent is 0.05-0.1 Pa.S at 25 ℃. The viscosity of the sodium silicate solvent is preferably 0.01 to 0.05 Pa.S at 25 ℃.

The dispersant in this example is acetone and the carrier is a sodium silicate solvent. The acetone and the sodium silicate are adopted to achieve better dispersion and support effects of the alloy powder compared with other reagents. In addition, in the sealant of the embodiment, the mass ratio of the alloy powder is 8%, and the mass ratio of the dispersing agent acetone is 35%. The dispersant is reasonably controlled, so that the dispersion effect of the alloy powder is controlled on one hand, and the product viscosity can be controlled on the other hand. The viscosity of the sodium silicate solvent is about 0.05 Pa.S at 25 ℃, and the viscosity of the finally prepared hole sealing agent is about 0.1 Pa.S at 25 ℃.

In this example, the alloy powder contains, by mass%, 16% of Cr, 4.5% of Si, 2.5% of B, and the balance Ni. By reasonably setting the proportion of each element in the alloy powder, the hole sealing effect and the lasting effect after the hole sealing agent is remelted are better; and the element arrangement can be close to and suitable for most coating components in the nuclear power field, so that the combination with the coating is firmer when the sealant is used for remelting and sealing holes. In other embodiments, the alloy powder comprises, by mass, 11-19% of Cr, 3.5-5.5% of Si, 1.5-3.5% of B, and the balance Ni.

The grain size of the alloy powder is in the range of 0.5-5 μm. The particle size is too small, the remelting and hole sealing effect is poor, and the particle size is too large to enter the coating pores. The grain size of the alloy powder in this example was 2 μm.

The hole sealing agent prepared from the alloy powder can realize the hole sealing function after remelting the alloy powder, and has good continuous effect and difficult failure. The dispersing agent is used for dispersing the alloy powder to avoid the agglomeration of the alloy powder, and the carrier solvent is used for dispersing and supporting the alloy powder to achieve the aim of uniformly dispersing the alloy powder. And by controlling the proportion of the alloy powder, the viscosity of the sealant and the lower hole sealing process and method, the sealant can flow into the coating pores and has larger penetration depth, thereby achieving better hole sealing effect.

EXAMPLE two preparation of the hole sealing agent

The embodiment provides a preparation method of the hole sealing agent in embodiment 1, which specifically includes the following steps: the method specifically comprises the following steps: preparing an alloy block by a physical metallurgy method, impacting the alloy block by adopting an aerosol method (high-speed airflow) to obtain alloy powder, dispersing the alloy powder in acetone by ultrasonic waves to obtain an alloy solution, and adding the alloy solution into a carrier solvent to obtain a hole sealing agent which is oily. The hole sealing agent is formed by mixing the prepared alloy solution with a carrier solvent, so that the problem that the alloy powder cannot be dispersed due to agglomeration is avoided. The alloy powder can be further dispersed by adopting ultrasonic waves, so that the agglomeration of the alloy powder is avoided.

The physical metallurgy method and the aerosol method for preparing the alloy block are conventional methods in the related field.

EXAMPLE three hole sealing method

As shown in fig. 1 to 8, this embodiment provides a method for sealing holes by using the above-mentioned sealing agent, which specifically includes the following steps:

A. the coating component 2 to be sealed is placed in a closed container. The closed container comprises a box body at the lower part and a sealing cover 1 at the upper part, a first opening 41, a second opening 42 and a fourth opening 44 are arranged on the side wall of the box body, and a third opening 43 is arranged at the bottom of the box body. Wherein the first opening 41 and the second opening 42 are located on the same sidewall, the height of the second opening 42 is lower than that of the first opening 41, and the fourth opening 44 is located on the opposite sidewall, as shown in fig. 1.

In the embodiment, the base material of the coating part is carbon steel, the coating material is NiCr alloy, the thickness of the coating is 250 μm, and the preparation process of the coating is arc spraying.

B. The second opening 42 is opened, through which the liquid sealant 3 prepared in example 1 is fed into the closed vessel, as shown in fig. 2.

C. As shown in fig. 3, the second opening 42 is closed, the first opening 41 is opened, air in the sealed container is pumped out from the top of the sealed container through the first opening 41, and finally the sealant 3 fills the whole sealed container, the container is maintained in a negative pressure state, the absolute pressure of vacuum is 8Pa, the container is maintained for 30min, and then the first opening 41 is closed. The negative pressure state can pump out air in the pores, which is helpful for the sealant to flow into the pores in the coating and reach deeper penetration depth. In other embodiments, the negative pressure is no greater than 10pa (absolute pressure) for a 20min hold time.

D. The first opening 41 is opened again, and the container is communicated with the atmosphere through the first opening 41 to be depressurized, so that the pressure in the closed container is restored to the normal pressure state, as shown in fig. 4.

E. As shown in fig. 5, the first opening 41 is opened from the top of the closed casing to the inside of the closed casing, and then the first opening 41 is closed. The pressure is maintained at not less than 6bar (absolute) for not less than 20 min. Namely, a positive pressure process is carried out after the negative pressure, and the pressurizing operation can further force the hole sealing agent to enter the inner pores of the coating and achieve deeper penetration depth.

F. The third opening 43 is opened to discharge the sealing agent 3 in the closed vessel, as shown in fig. 6.

G. As shown in FIG. 7, the closed container is communicated with a hot water tank through a third opening 43 and a fourth opening 44 to form a water loop, hot water is circulated for 15min to clean residual sealant attached to the surface of the coating part, and the temperature of the hot water is not lower than 85 ℃. Meanwhile, under the heating of high-temperature water, the organic components of the sealant left in the pores of the coating solidify and fill the pores.

And C, after all the air in the pores is pumped away, the pores are in negative pressure, so that the sealant in the pores cannot flow out, and the hot water can only clean residual sealant adhered to the surface of the coating part.

H. The cover 1 is opened and the coated part is removed for drying, as shown in fig. 8.

I. The hole sealing agent in the coating hole is heated and melted by adopting modes such as laser heating, so that metal in the hole sealing agent is remelted in situ to form a compact surface structure, the hole sealing effect is achieved, and the hole sealing effect and the lasting effect are good. The maintenance effect of hole sealing is good even if the temperature of service is higher than 500 ℃ in the follow-up process.

By adopting the process method and matching with the hole sealing agent, the hole sealing agent can be deeper into the pores of the coating and is subjected to in-situ remelting in the pores, so that the hole sealing effect is fully achieved, and the continuous effect is good.

The hole sealing process can be designed into a production line through the steps A to I, and automatic operation is realized.

Example four hole sealing method

This example is substantially the same as example 3, except that the coating material in this example is WC (tungsten carbide) and the coating is prepared by a process of supersonic flame spraying.

Comparative example 1

The comparative example uses the sealant of example 1, but uses the traditional normal pressure brush coating process to seal the holes: brushing and standing for 30 min.

Comparative example No. two

Basically the same as example 3, except that the coating material in this example was WC (tungsten carbide) and the coating was prepared by a process of supersonic flame spraying.

The following are the results of the pore sealing penetration depths of examples 3 to 4 and comparative examples 1 to 2.

The results in the table above show that for coatings prepared by the arc spraying process, the hole sealing method of example 3 can achieve 100% penetration filling of the full thickness, whereas the conventional normal-pressure brush-coating type hole sealing method can only penetrate to 20% of the thickness of the coating; for the coating prepared by the supersonic flame spraying process, the penetration depth of the coating prepared by the supersonic flame spraying process in example 4 is improved by 40% compared with that of the normal-pressure brushing hole sealing method. Therefore, the penetration depth can be effectively increased by adopting the sealant and the sealing method.

The invention provides a thermal spraying coating hole sealing agent and a vacuum hole sealing method, designs a self-sealing metal alloy powder organic composite hole sealing agent, provides a continuous automatic hole sealing method for solving the technical defect of a brush coating type hole sealing process by utilizing vacuum, and is convenient for realizing automation of the hole sealing process.

Compared with the traditional hole sealing agent and hole sealing process, the method has the following advantages: (1) the metal alloy powder sodium silicate sealant is high temperature resistant and corrosion resistant, and can be self-healed into a compact oxide film structure at high temperature. (2) For the coating part prepared by the electric arc spraying process, the hole sealing agent can realize full-thickness penetration filling, and the service life of the coating is greatly prolonged. (3) The hole sealing curing time is shortened to 20% of the normal-pressure brush-coating type hole sealing process, namely the hole sealing curing of the single-interval coating part is not more than 5h, and the hole sealing efficiency of the coating is greatly improved. (4) By adopting the hole sealing agent and the hole sealing process, the batch automatic hole sealing assembly line of the workpieces can be realized, and the production efficiency of thermal spraying is greatly improved.

The above embodiments are merely illustrative of the technical concept and features of the present invention, and the purpose thereof is to enable those skilled in the art to understand the content of the present invention and implement the invention, and not to limit the scope of the invention, and all equivalent changes or modifications made according to the spirit of the present invention should be covered by the scope of the present invention.