阅读说明：本技术 一种抑制氧化锌负极钝化的复配电解液 (Compound electrolyte for inhibiting passivation of zinc oxide cathode ) 是由 杨建文 熊伟雄 刘鑫鑫 倪文浩 黄斌 李伟 于 2021-06-02 设计创作，主要内容包括：本发明公开了一种抑制氧化锌负极钝化行为的复配电解液。还原态氧化锌电极在Li-2SO-4-Na-2SO-4-ZnSO-4复配水溶液中进行阳极极化时会发生显著的钝化行为,在Li-2SO-4-Na-2SO-4-ZnSO-4复配水溶液中加入(NH-4)-2SO-4并调节其pH至9.0,可以有效抑制氧化锌负极的钝化行为,获得大于540mAh g～(-1)的可逆充放电比容量。因此,该复配电解液用于水系锌电池具有良好的应用前景。(The invention discloses a compound electrolyte for inhibiting passivation behavior of a zinc oxide cathode. Reduced zinc oxide electrode in Li 2 SO 4 ‑Na 2 SO 4 ‑ZnSO 4 Significant passivation behavior occurs during anodic polarization in compounded aqueous solutions, in Li 2 SO 4 ‑Na 2 SO 4 ‑ZnSO 4 Adding (NH) into the compound aqueous solution 4 ) 2 SO 4 And the pH value is adjusted to 9.0, so that the passivation behavior of the zinc oxide cathode can be effectively inhibited, and more than 540mAh g is obtained ‑1 The reversible charge-discharge specific capacity of (2). Therefore, the temperature of the molten metal is controlled,the compound electrolyte has good application prospect when being used for a water-based zinc battery.)
技术领域
本发明涉及锌电极电解液领域，特别涉及一种氧化锌负极用电解液的制备方法。
背景技术
金属锌标准电势低，比容量高，资源丰富，环境友好，是一种综合性能较好的化学电源负极材料。采用强碱性电解液的锌电池(如碱性锌锰干电池、锌镍电池、锌银电池等)已经实现了商业化，但是由于强碱性电解液中存在大量OH-，锌负极会发生化学反应溶解，造成电极变形、电池容量衰减等问题。因此，降低强碱性电解液中的OH-浓度，采用非强碱性电解液有望改善锌负极材料的电化学稳定性。但是，在弱碱性电解液中，锌离子水解生成的氢氧化锌、氧化锌难溶化合物在金属锌表面的钝化行为将会严重影响电池的充放电动力学过程。
基于此，本发明制备了一种弱碱性复配电解液，有效抑制了氧化锌负极材料的表面钝化行为。