阅读说明：本技术 一种适用于磷酸铁锂材料的氧化物固态电解质制备方法及其应用 (Preparation method and application of oxide solid electrolyte suitable for lithium iron phosphate material ) 是由 胡培 徐杉 史德友 刘世琦 于 2019-10-25 设计创作，主要内容包括：本发明公开了一种适用于磷酸铁锂材料的氧化物固态电解质制备方法及其应用,通过溶胶凝胶法制备的NASICON型固态电解质Li<Sub>1+</Sub><Sub>x</Sub>Al<Sub>x</Sub>Ge<Sub>2–x</Sub>(PO<Sub>4</Sub>)<Sub>3</Sub>(LAGP),Ge与金属Li的稳定性高,会提高其化学稳定性、离子电导率和电化学窗口,解决固态锂电池存在电极体积膨胀、电解质/电极的界面阻抗大、循环稳定性低等问题,溶胶凝胶法得到的LAGP结晶度高,形貌均一,具有超细粒径,增大电极与电解质的反应接触面积,缓解了电解质/电极的界面这一固态电池发展的关键难题。该方法仪器设备要求简单,易扩大生产。(The invention discloses a preparation method and application of an oxide solid electrolyte suitable for a lithium iron phosphate material, and discloses a NASICON type solid electrolyte Li prepared by a sol-gel method 1+ x Al x Ge 2–x (PO 4 ) 3 (LAGP), the Ge and the metal Li have high stability, the chemical stability, the ionic conductivity and the electrochemical window of the Ge and the metal Li can be improved, the problems of electrode volume expansion, large interface resistance of electrolyte/electrode, low cycling stability and the like of the solid-state lithium battery are solved, the LAGP obtained by the sol-gel method has high crystallinity, uniform appearance and ultrafine particle size, the reaction contact area of the electrode and the electrolyte is increased, and the key problem of the development of the solid-state battery with the interface of the electrolyte/electrode is relieved. The method has simple requirements on instruments and equipment and is easy for expanded production.)

1. A preparation method and application of an oxide solid electrolyte suitable for a lithium iron phosphate material are characterized in that: the oxide solid electrolyte of the lithium iron phosphate material is a solid electrolyte Li with an NASICON structure_1+xAl_xGe_2–x(PO₄)₃Each TiO in the structure₆Octahedron and six POs₄Tetrahedrally connected, each PO₄Tetrahedron and four TiO₆Octahedrons are connected, and polyhedrons are connected through oxygen atoms at vertex angles which are mutually contacted to form a three-dimensional interconnected skeleton structure, so that an ion transmission channel parallel to the c axis is formed for lithium ion transmission.

2. The method for preparing the oxide solid electrolyte suitable for the lithium iron phosphate material according to claim 1, comprising the following steps:

dissolving lithium salt, aluminum salt, germanium salt, phosphate and citric acid in a certain amount of water, and stirring and dissolving to be transparent;

adding an organic solvent into the citric acid mixed solution according to a certain molar ratio, heating and stirring for a certain time to obtain a clear and transparent solution;

placing the solution in an oven, heating for a certain time at a certain temperature, and volatilizing the solvent to obtain brown gel;

grinding the brown gel uniformly, and sintering for a certain time at a certain temperature;

after the temperature is reduced to room temperature, the brown powder is continuously and uniformly ground and sintered for a certain time at a certain temperature to obtain white powder, namely a final product.

3. The method for preparing an oxide solid electrolyte suitable for a lithium iron phosphate material as claimed in claim 1, wherein: the lithium salt, the aluminum salt and the germanium salt are one or more of nitrate, sulfate and carbonate, and the phosphate is one or more of phosphate, monohydrogen phosphate and dihydrogen phosphate.

4. The method for preparing an oxide solid electrolyte suitable for a lithium iron phosphate material as claimed in claim 1, wherein: the molar amount of the citric acid is equal to the total molar amount of the metal ions.

5. The method for preparing an oxide solid electrolyte suitable for a lithium iron phosphate material as claimed in claim 1, wherein: the temperature of the oven is 150 ℃ and 180 ℃, and the heating time is 12-36 hours.

6. The method for preparing an oxide solid electrolyte suitable for a lithium iron phosphate material as claimed in claim 1, wherein: the first sintering temperature is 400-600 ℃, and the sintering time is 3-6 hours.

7. The method for preparing an oxide solid electrolyte suitable for a lithium iron phosphate material as claimed in claim 1, wherein: the second sintering temperature is 600-1000 ℃, and the sintering time is 3-6 hours.

8. The method for preparing an oxide solid electrolyte suitable for a lithium iron phosphate material as claimed in claim 1, wherein: the solid electrolyte Li with NASICON structure obtained by the method_1+xAl_xGe_2–x(PO₄)₃The crystal phase is separated out from the matrix of the glass phase, and the glass phase existing in the grain boundary can reduce the resistance of the grain boundary and simultaneously improve the compactness of the material and the ionic conductivity.

Technical Field

The invention belongs to the technical field of new energy material preparation, and particularly relates to a preparation method and application of an oxide solid electrolyte suitable for a lithium iron phosphate material.

Background

The all-solid-state lithium ion battery can provide higher energy density than the conventional battery, and is considered as one of the most important energy storage technologies of the next generation. The solid electrolyte not only maintains lithium ion conductivity but also acts as a battery separator. The positive electrode material of the all-solid-state lithium ion battery is similar to that of the traditional lithium ion battery (such as lithium transition metal oxide or sulfide); most negative electrode materials are lithium metal, lithium alloys and graphene. The all-solid-state lithium ion battery may be classified into an inorganic solid electrolyte battery and a polymer battery according to the use of a solid electrolyte. Several key challenges that still need to be addressed remain: for example, electrode material volume changes, solid electrolyte conductivity, large interfacial (electrode/electrolyte) resistance, low loading of electrode active materials and poor cycling stability, etc. One of the important problems to be solved is how to improve the ionic conductivity between the electrode and the solid electrolyte interface and increase the ion transport rate of the solid electrolyte.

The key point for solving the problem is to research and synthesize the solid electrolyte with high stability, high ionic conductivity, high lithium electrochemical window and high specific surface area. Among the three major types of solid electrolytes, sulfide electrolytes have high ionic conductivity but poor air-sensitive and air-sensitive properties and stability; the polymer electrolyte has high specific surface area, large contact area with an electrode, but low electrochemical window to lithium, and the inorganic oxide electrolyte has low ionic conductivity, is difficult to realize large specific surface area and is fragile. Because of the good overall performance of oxide electrolytes, researchers have made a lot of work on some of the problems of oxide electrolytes. The patent CN 108383517A adopts a solid phase sintering method to prepare Li-Mg-P-O solid electrolyte ceramic, and the method obtains the product by planet ball milling of mixed materials and solid phase mixing and sintering. The pure solid phase method is easy to cause uneven dispersion of ions, generate impure phases and influence the overall performance of the material. The patent CN109713347A adopts a method of ultrasonic cleaning and microwave chemical reaction to obtain a product, the uniformity and the specific surface area of the product are greatly improved, but the method has expensive test equipment and is not suitable for industrial production.

The invention does a great deal of work in the aspects of reducing the production cost and debugging the specific surface area of the product, the product obtained by adopting the sol-gel method has high yield and low energy consumption, and the product has the advantages of high ionic conductivity and high specific surface area, and is suitable for industrialized popularization and production.

Disclosure of Invention

The invention aims to provide a preparation method and application of an oxide solid electrolyte suitable for a lithium iron phosphate material, which can improve the ionic conductivity of the electrolyte and achieve the purposes of enlarging the contact area of the electrolyte and an electrode and improving the cycle performance of a solid battery by a sol-gel method.

In order to achieve the above purpose, the solution of the invention is:

1) dissolving lithium salt, aluminum salt, germanium salt, phosphate and citric acid in a certain amount of water, and stirring and dissolving to be transparent;

2) adding an organic solvent into the citric acid mixed solution according to a certain molar ratio, heating and stirring for a certain time to obtain a clear and transparent solution;

3) placing the solution in an oven, heating for a certain time at a certain temperature, and volatilizing the solvent to obtain brown gel;

4) grinding the brown gel uniformly, and sintering for a certain time at a certain temperature;

5) after the temperature is reduced to room temperature, the brown powder is continuously and uniformly ground and sintered for a certain time at a certain temperature to obtain white powder, namely a final product.

The lithium salt, the aluminum salt and the germanium salt are one or more of nitrate, sulfate and carbonate, and the phosphate is one or more of phosphate, monohydrogen phosphate and dihydrogen phosphate.

The molar amount of the citric acid is equal to the total molar amount of the metal ions.

The temperature of the oven is 150 ℃ and 180 ℃, and the heating time is 12-36 hours.

The first sintering temperature is 400-600 ℃, and the sintering time is 3-6 hours.

The second sintering temperature is 600-1000 ℃, and the sintering time is 3-6 hours.

The invention has the advantages that: the solid electrolyte Li with NASICON structure obtained by the method_1+xAl_xGe_2–x(PO₄)₃The crystal phase is separated out from the matrix of the glass phase, and the glass phase existing in the grain boundary can reduce the resistance of the grain boundary and simultaneously improve the compactness of the material and the ionic conductivity.

The solid electrolyte has simple process, can control the shape and the particle size of the material, and is beneficial to the industrialization process of power batteries.

Drawings

FIG. 1 is Li provided in example 1 of the present invention_1.5Al_0.5Ge_1.5(PO₄)₃X-ray diffraction pattern of (a).

FIG. 2 shows Li provided in example 1 of the present invention_1.5Al_0.5Ge_1.5(PO₄)₃Scanning electron microscopy of (a).

Fig. 3 is a graph comparing the cycle performance of lithium batteries using li1.5al0.5ge1.5(PO4)3 samples provided in examples 1 and 2 of the present invention.